Non-oriented electrical steel sheet having superior magnetic properties and method of manufacturing same
A non-oriented electrical steel sheet with excellent magnetism may include Si at 2.5 to 3.8 wt %, Al at 0.5 to 2.5 wt %, Mn at 0.2 to 4.5 wt %, C at 0.005 wt % or less (excluding 0 wt %), S at 0.005 wt % or less (excluding 0 wt %), N at 0.005 wt % or less (excluding 0 wt %), Nb at 0.004% or less (excluding 0 wt %), Ta at 0.0005 to 0.0025 wt %, and the balance of Fe and inevitable impurities.
1 . A non-oriented electrical steel sheet, comprising Si at 2.5 to 3.8 wt %, Al at 0.7 to 2.0 wt %, Mn at 0.2 to 4.5 wt %, C at 0.005 wt % or less (excluding 0 wt %), S at 0.005 wt % or less (excluding 0 wt %), N at 0.005 wt % or less (excluding 0 wt %), Nb at 0.004% or less (excluding 0 wt %), Ti at 0.004% or less (excluding 0 wt %), V at 0.004% or less (excluding 0 wt %), Ta at 0.0005 to 0.0025 wt %, and the balance of Fe and inevitable impurities,
wherein the steel sheet contains one or more of a carbide-based precipitate, a nitride-based precipitate, and a sulfide-based precipitate with a diameter of 20 to 100 nm, and
a distribution density of each of the carbide-based precipitate, the nitride-based precipitate, and the sulfide-based precipitate is 0.9 pcs/μm 2 or less.
2 . The non-oriented electrical steel sheet of claim 1 , further comprising
one or more of Cu at 0.025 wt % or less (excluding 0 wt %), B at 0.002 wt % or less (excluding 0 wt %), Mg at 0.005 wt % or less (excluding 0 wt %), and Zr at 0.005 wt % or less (excluding 0 wt %).
3 . The non-oriented electrical steel sheet of claim 1 , wherein
a thickness of the steel sheet is 0.1 to 0.3 mm.
4 . The non-oriented electrical steel sheet of claim 1 , wherein
an average grain diameter is 40 to 100 μm.
5 . The non-oriented electrical steel sheet of claim 1 , wherein
a hysteresis loss in W 10/400 iron loss is 1.0 W/kg or less, and a hysteresis loss in W 10/400 iron loss is 3.8 W/kg or less.