Non-oriented electrical steel sheet and manufacturing method therefor

1. A non-oriented electrical steel sheet comprising,

based on 100 wt % of a total composition thereof, Ti at 0.0015 wt % or more to 0.0030 wt % or less, Nb at 0.0005 wt % or more to 0.0035 wt % or less, Vat 0.0015 wt % or more to 0.0040 wt % or less, B at 0.0003 wt % to 0.0020 wt %, and the remaining portion including Fe and impurities,

wherein a value of ([Ti]+0.8[Nb]+0.5[V])/(10*[B]) is 0.4 to 7.8,

wherein when a rolling direction of the electrical steel sheet corresponds to an x-axis, a width direction thereof corresponds to a y-axis, and a direction normal to an xy plane thereof corresponds to a z-axis, a value of (length of the grain in the y-axis direction)/(length of the grain in the z-axis direction) measured on a yz plane is 1.18 or more to 1.5 or less, and

wherein the electrical steel sheet, based on 100 wt % of a total composition thereof, further includes P at 0.005 wt % to 0.08 wt %, Sn at 0.01 wt % to 0.08 wt %, Sb at 0.005 wt % to 0.05 wt %, or a combination thereof, and [P]+[Sn]+[Sb] is 0.01 wt % to 0.1 wt %.

2. The non-oriented electrical steel sheet of claim 1 , wherein a grain size of the electrical steel sheet is 60 μm to 95 μm.

3. The non-oriented electrical steel sheet of claim 1 , wherein the electrical steel sheet, based on 100 wt % of a total composition thereof, further includes C at greater than 0 to 0.004 wt % or less, Si at 2.5 wt % to 3.5 wt %, Al at 0.5 wt % to 1.8 wt %, Mn at 0.05 wt % to 0.9 wt %, N at greater than 0 to 0.0030 wt % or less, and S at greater than 0 to 0.0030 wt % or less.

4. The non-oriented electrical steel sheet of claim 1 ,

wherein in the electrical steel sheet, the number of inclusions including Ti, Nb, V, and B is 500/mm 2 or less,

wherein the measurement of the number of inclusions is performed by a transmission electron microscope (TEM), and the number of measured inclusions is analyzed by EDS.