Curable resin composition, dry film, resin-clad copper foil, cured product, and electronic component
To provide a curable resin composition, from which a cured product having high heat resistance, a low dielectric loss tangent, high adhesion to a conductor can be obtained. A dry film, a resin-clad copper foil, a cured product, and an electronic component containing the curable resin composition are to be provided. A curable resin composition containing (A) an epoxy resin and (B) a compound having an active ester group is obtained, which has ratio of the total amount of epoxy group(s) in (A) the epoxy resin/the total amount of active ester group(s) in (B) the compound having an active ester group in the composition in the range of 0.2 to 0.6. A dry film, a resin-clad copper foil, a cured product, and an electronic component containing the curable resin composition are also obtained.
1. A curable resin composition, comprising:
an epoxy resin;
an inorganic filler:
a curing accelerator; and
a compound having an active ester group,
wherein the curing accelerator includes at least one selected from the group consisting of an imidazole, an imidazole derivative, and an amine, a ratio of the total amount of epoxy groups in the epoxy resin/the total amount of active ester groups in the compound having an active ester group in the curable resin composition is in a range of 0.2 to 0.6, the epoxy resin includes a biphenyl aralkyl type epoxy resin and at least one compound selected from the group consisting of bisphenol A type epoxy resin and bisphenol F type epoxy resin, the compound having an active ester group is selected from the group consisting of a compound of formula (1),
where each X 1 , independently from each other, is a group having a benzene ring or a naphthalene ring, k is 0 or 1, and n as an average number of repeating units is in a range of 0.25 to 1.5, and a compound having a structural moiety of formula (2),
where the compound having the structural moiety of the formula (2) has a structure with monovalent aryloxy groups at both ends thereof, m is an integer in a range of 1 to 6, each n, independently from each other, is an integer in a range of 1 to 5, and each q, independently from each other, is an integer in a range of 1 to 6, and each X 2 , independently from each other, is a group of formula (3),
where each k, independently from each other, is an integer in a range of 1 to 5, or a group of formula (4),
where Y is a group of the formula (3), each k, independently from each other, is an integer in a range of 1 to 5, and each t, independently from each other, is an integer in a range of 0 to 5.
2. The curable resin composition according to claim 1 , wherein the compound having an active ester group is the compound of formula (1),
3. The curable resin composition according to claim 1 , wherein the compound having an active ester group is the compound having a structural moiety of formula (2),
4. The curable resin composition according to claim 1 , wherein the inorganic filler comprises silica such that an amount of the silica is at least 65% by mass with respect to 100% by mass of a solid content in the curable resin composition.
5. A dry film, comprising:
a resin layer comprising the curable resin composition of claim 1 .
6. A resin-clad copper foil, comprising:
a copper foil; and
a resin layer formed on the copper foil and comprising the curable resin composition of claim 1 .
7. A cured product obtained by a process comprising curing the curable resin composition of claim 1 .
8. An electronic component, comprising:
the cured product of claim 7 .
9. A resin-clad copper foil, comprising:
a copper foil having a carrier; and
a resin layer formed on the copper foil and comprising the curable resin composition of claim 1 .
10. The curable resin composition according to claim 2 , wherein the inorganic filler comprises silica such that an amount of the silica is at least 65% by mass with respect to 100% by mass of a solid content in the curable resin composition.
11. A dry film, comprising:
a resin layer comprising the curable resin composition of claim 2 .
12. A resin-clad copper foil, comprising:
a copper foil; and
a resin layer formed on the copper foil and comprising the curable resin composition of claim 2 .
13. A cured product obtained by a process comprising curing the curable resin composition of claim 2 .
14. The curable resin composition according to claim 3 , wherein the inorganic filler comprises silica such that an amount of the silica is at least 65% by mass with respect to 100% by mass of a solid content in the curable resin composition.
15. A dry film, comprising:
a resin layer comprising the curable resin composition of claim 3 .
16. A resin-clad copper foil, comprising:
a copper foil; and
a resin layer formed on the copper foil and comprising the curable resin composition of claim 3 .
17. The curable resin composition according to claim 1 , wherein the curable accelerator includes the amine.
18. The curable resin composition according to claim 1 , wherein the curable accelerator includes dimethylaminopyridine.
19. The curable resin composition according to claim 1 , wherein the ratio of the total amount of epoxy groups in the epoxy resin/the total amount of active ester groups in the compound having an active ester group in the curable resin composition is in a range of 0.2 to 0.4.
20. The curable resin composition according to claim 1 , wherein the ratio of the total amount of epoxy groups in the epoxy resin/the total amount of active ester groups in the compound having an active ester group in the curable resin composition is in a range of 0.2 to 0.3.