High resolution and high flexibility fiber optical cables and microfabrication methods for making same
The present disclosure relates to methods of forming a fiber optic core, and a fiber optic component with a highly uniform cladding covering the fiber optic core. In one microfabrication process a first sacrificial tubing is provided which has a predetermined inner diameter. A quantity of a curable polymer is also provided. The first sacrificial tubing is at least partially filled with the curable polymer. The curable polymer is then cured. The first sacrificial tubing is then removed to produce a finished fiber optic core. Additional operations may be performed by which the fiber optic core is placed inside a thermoplastic tubing, which is itself placed inside a sacrificial heat shrink. Heat is applied to reflow the thermoplastic tubing around the fiber optic core, thus forming a highly uniform thickness cladding. When the sacrificial heat shrink tubing is removed a finished fiber optic component is present. Additional microfabrication methods are disclosed which involve dip coating a pre-formed fiber optic core in a polymer, and then curing the polymer to form a finished fiber optic component with a uniform thickness cladding.
1. A method of forming a fiber optic component, comprising:
providing a first sacrificial tubing having a predetermined inner diameter;
providing a quantity of a curable polymer;
at least partially filling the first sacrificial tubing with the curable polymer;
curing the curable polymer;
removing the first sacrificial tubing to produce a fiber optic core;
forming a cladding on the fiber optic core by thermally reflowing a thermoplastic over the fiber optic core, to form the fiber optic component.
2. The method of claim 1 , wherein the curable polymer comprises a curable photopolymer curable by an application of ultraviolet light.
3. The method of claim 2 , wherein the curing of the photocurable polymer is performed over a time period of a few seconds to tens of minutes.
4. The method of claim 1 , wherein the thermally reflowing of the thermoplastic over the fiber optic core comprises heating a thermoplastic tubing having a predetermined inner diameter, within which the fiber optic core is placed, to uniformly reflow the thermoplastic tubing over the fiber optic core to form the cladding, and wherein the cladding cross sectional area is closely associated with a cross sectional area of the thermoplastic tubing.
5. The method of claim 4 , wherein the thermally reflowing of the thermoplastic over the fiber optic core comprises:
placing a thermoplastic tubing inside a sacrificial heat shrink tubing, with the thermoplastic tubing having a predetermined inner diameter;
inserting the fiber optic core at least partially into the thermoplastic tubing;
applying heat to thermally reflow material forming the thermoplastic tubing over the fiber optic core to form the cladding; and
allowing the material to cool to solidify the cladding.
6. The method of claim 5 , removing the sacrificial heat shrink tubing from the cladding to reveal the fiber optic component.
7. The method of claim 1 , wherein the cladding has a thickness of about tens of μm to about tens of mm.
8. A method of forming a fiber optic component, comprising:
providing a first sacrificial tubing having a predetermined inner diameter;
providing a quantity of a curable polymer;
at least partially filling the first sacrificial tubing with the curable polymer;
curing the curable polymer;
removing the first sacrificial tubing to reveal a fiber optic core;
providing a sacrificial heat shrink tubing;
providing a thermoplastic tubing inside the sacrificial heat shrink tubing;
placing the fiber optic core inside the thermoplastic tubing;
applying heat to the thermoplastic tubing to thermally reflow material of the thermoplastic tubing around the fiber optic to form a cladding around the fiber optic core; and
removing the heat shrink tubing to reveal a fully formed fiber optic component.
9. The method of claim 8 , wherein the curable polymer comprises an ultraviolet light curable photopolymer.
10. The method of claim 8 , wherein the thermoplastic tubing comprises a meltable polymeric material.
11. A method of forming a fiber optic component, comprising:
providing a sacrificial heat shrink tubing;
providing a thermoplastic tubing inside the sacrificial heat shrink tubing;
providing a mandrel having a predetermined outer diameter selected to be equal to a desired outer diameter of a fiber optic core component;
placing the mandrel inside the thermoplastic tubing;
applying heat to the thermoplastic tubing to thermally reflow material of the thermoplastic tubing around the mandrel to form a cladding layer;
removing the mandrel to leave the cladding layer;
forming the fiber optic optical core by at least partially filling the cladding layer with a quantity of a curable polymer;
curing the curable polymer; and
removing the sacrificial heat shrink tubing to produce a fiber optic component.