IP Library Granted Patent US 12,206,105
Granted Patent B2
US 12,206,105 · App. 17/311,465 · Granted Jan 21, 2025

Positive electrode material for high-power lithium ion battery and preparation method thereof

Inventors: Xin Guo (Changsha, CN); Haishi Hu (Changsha, CN); Zhibing Hu (Changsha, CN); Chenghuan Huang (Changsha, CN); Haiyan Zhang (Changsha, CN); Youyuan Zhou (Changsha, CN)
Assignees: Minmetals New Energy Materials(Hunan) Co., Ltd.; JINCHI ENERGY MATERIALS CO., LTD.
H01M4/525C01G53/006C01G53/42C01G53/50H01M4/505H01M10/0525C01P2004/03C01P2004/61C01P2004/62C01P2006/12C01P2006/40H01M2004/021H01M2004/028
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,206,105
App. No.
17/311,465
Granted
Jan 21, 2025
Kind
B2
Abstract

Disclosed is a positive electrode material for a high-power lithium ion battery. The positive electrode material is in form of secondary particles with a hollow microsphere structure, and a shell of the secondary particles is formed by aggregating a plurality of primary particles. The secondary particles have a uniform particle size, a loose and porous surface, and a large specific surface area. The obtained particles are regular in shape, stable in material structure, so that the positive electrode material has high rate performance and excellent cycle performance. The disclosure also provides a preparation method for the positive electrode material comprising (1) synthesizing a Ni x Co y M z (OH) 2 precursor by a co-precipitation method, such that the precursor has a central portion consisted by fine particles and a shell portion consisted by large particles having a larger particle size than that of the fine particles; (2) mixing the precursor and a lithium salt uniformly, and adding an oxide of a doping element during the mixing, and then sintering the mixture to provide a Li a Ni x Co y M z O 2 positive electrode material. The preparation method is simple and low cost, and can be industrialized.

Claims (16)

1. A preparation method of a positive electrode material for a lithium ion battery, wherein the positive electrode material is represented by Li a Ni x Co y M z O 2 , wherein 0.96≤a≤1.35, 0.3≤x≤1, 0≤y≤0.4, 0≤z≤0.4, x+y+z=1, M is one or more selected from Mn, Al, Zr, Mg, W, Ti, Y, La, B and Sr; the positive electrode material is secondary particles with a hollow microsphere structure, and a shell of the secondary particles is formed by aggregating a plurality of primary particles, wherein the preparation method comprises the steps of:

(1) synthesizing a Ni x Co y M z (OH) 2 precursor by a co-precipitation method comprising a nucleation and inner core growth stage and a shell growth stage; and wherein the obtained precursor has a central portion consisting of fine particles with a particle size of <0.3 μm and a shell portion consisting of large particles having a particle size larger than that of the fine particles;

(2) mixing the precursor obtained in step (1) with a lithium salt uniformly, and then sintering the mixture to obtain the Li a Ni x Co y M z O 2 positive electrode material;

wherein in step (1), synthesizing the Ni x Co y M 2 (OH) 2 precursor by the co-precipitation method comprises the steps of: adding a metal salt solution of Ni, Co and M, an alkaline solution and an aqueous ammonia solution to a reaction kettle containing a base solution for reaction, during which a reaction temperature is 40° C.-60° C., a stirring speed is 100 r/min-1000 r/min, pH of a reaction system is controlled from 8-13, and nitrogen is continuously introduced into the reaction kettle; controlling an ammonium concentration of the reaction system in a range of 7 g/L-15 g/L at the nucleation and inner core growth stage, and in a range of 30 g/L-40 g/L at the shell growth stage for synthesizing the precursor, providing that the ammonium concentration of the reaction system at the shell growth stage is higher than that at the nucleation and inner core growth stage; and subjecting a precipitate obtained from the reaction to solid-liquid separating, aging, washing and drying to obtain the Ni x Co y M 2 (OH) 2 precursor.

2. The preparation method according to claim 1 , wherein the metal salt solution is one or more selected from sulfate solution, a nitrate solution, a chloride solution, an acetate solution and a meta-aluminate solution, a total concentration of metal ions in the metal salt solution is 0.05 mol/L-3 mol/L; the alkaline solution is a sodium hydroxide solution and has a concentration of 1 mol/L-10 mol/L; and the ammonium concentration of the aqueous ammonia solution is 3 mol/L-6 mol/L.

3. The preparation method according to claim 1 , wherein in step (2), adding the lithium salt in an amount such that a molar ratio of Li to Ni+Co+M is 0.96-1.35, and the lithium salt is one or more selected from lithium carbonate, lithium hydroxide, lithium oxalate and lithium acetate; when mixing the precursor with the lithium salt, an oxide of a doping element which is one or more selected from Al, Zr, Mg, W, Ti, Y, La, B and Sr is additionally added, and the doping element is presented in the positive electrode material in a mass percentage of 0.01 wt %-2 wt %.

4. The preparation method according to claim 1 , wherein in step (2), the sintering is performed under a temperature of 500° C.-1000° C. for 6-24 hours with an atmosphere of air or oxygen or a mixture of oxygen and air.

5. The preparation method according to claim 4 , wherein a multi-stage temperature-controlled sintering method is used in the sintering, wherein firstly a temperature of 500° C.-700° C. is held for 5-6 hours, secondly the temperature is elevated to 810° C.-1000° C. and held for 8-10 hours, and lastly the temperature is lowered to 700° C.-750° C. and held for 5-8 hours.

6. A preparation method of a positive electrode material for a lithium ion battery, wherein the positive electrode material is represented by Li a Ni x Co y M z O 2 , wherein 0.96≤a≤1.35, 0.3≤x≤1, 0≤y≤0.4, 0≤z≤0.4, x+y+z=1, M is one or more selected from Mn, Al, Zr, Mg, W, Ti, Y, La, B and Sr; the positive electrode material is secondary particles with a hollow microsphere structure, and a shell of the secondary particles is formed by aggregating a plurality of primary particles; the secondary particles have an average particle size of 0.1 μm-40 μm and a specific surface area of 0.1 m2/g-15.0 m2/g; the primary particles have a particle size of 0.1 μm-3.5 μm; and a ratio of a thickness of the shell of the secondary particles to the particle size of the secondary particles is 1%-49%, wherein the preparation method comprises the steps of:

(1) synthesizing a Ni x Co y M z (OH) 2 precursor by a co-precipitation method comprising a nucleation and inner core growth stage and a shell growth stage; and wherein the obtained precursor has a central portion consisting of fine particles with a particle size of <0.3 μm and a shell portion consisting of large particles having a particle size larger than that of the fine particles;

(2) mixing the precursor obtained in step (1) with a lithium salt uniformly, and then sintering the mixture to obtain the Li a Ni x Co y M z O 2 positive electrode material;

wherein in step (1), synthesizing the Ni x Co y M 2 (OH) 2 precursor by the co-precipitation method comprises the steps of: adding a metal salt solution of Ni, Co and M, an alkaline solution and an aqueous ammonia solution to a reaction kettle containing a base solution for reaction, during which a reaction temperature is 40° C.-60° C., a stirring speed is 100 r/min-1000 r/min, pH of a reaction system is controlled from 8-13, and nitrogen is continuously introduced into the reaction kettle; controlling an ammonium concentration of the reaction system in a range of 7 g/L-15 g/L at the nucleation and inner core growth stage, and in a range of 30 g/L-40 g/L at the shell growth stage for synthesizing the precursor, providing that the ammonium concentration of the reaction system at the shell growth stage is higher than that at the nucleation and inner core growth stage; and subjecting a precipitate obtained from the reaction to solid-liquid separating, aging, washing and drying to obtain the Ni x Co y M 2 (OH) 2 precursor.

7. The preparation method according to claim 6 , wherein the metal salt solution is one or more selected from sulfate solution, a nitrate solution, a chloride solution, an acetate solution and a meta-aluminate solution, a total concentration of metal ions in the metal salt solution is 0.05 mol/L-3 mol/L; the alkaline solution is a sodium hydroxide solution and has a concentration of 1_mol/L-10 mol/L; and the ammonium concentration of the aqueous ammonia solution is 3 mol/L-6 mol/L.

8. The preparation method according to claim 6 , wherein in step (2), adding the lithium salt in an amount such that a molar ratio of Li to Ni+Co+M is 0.96-1.35, and the lithium salt is one or more selected from lithium carbonate, lithium hydroxide, lithium oxalate and lithium acetate; when mixing the precursor with the lithium salt, an oxide of a doping element which is one or more selected from Al, Zr, Mg, W, Ti, Y, La, B and Sr is additionally added, and the doping element is presented in the positive electrode material in a mass percentage of 0.01 wt %-2 wt %.

9. The preparation method according to claim 6 , wherein in step (2), the sintering is performed under a temperature of 500° C.-1000° C. for 6-24 hours with an atmosphere of air or oxygen or a mixture of oxygen and air.

10. The preparation method according to claim 9 , wherein a multi-stage temperature-controlled sintering method is used in the sintering, wherein firstly a temperature of 500° C.-700° C. is held for 5-6 hours, secondly the temperature is elevated to 810° C.-1000° C. and held for 8-10 hours, and lastly the temperature is lowered to 700° C.-750° C. and held for 5-8 hours.

Assignments (2)
CHANGE OF NAME Recorded Nov 18, 2024
From: HUNAN CHANGYUAN LICO CO., LTD.
To: MINMETALS NEW ENERGY MATERIALS (HUNAN) CO., LTD.
Reel/Frame 069305/0559 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Oct 27, 2021
From: GUO, XIN; HU, HAISHI; HU, ZHIBING; HUANG, CHENGHUAN; ZHANG, HAIYAN; ZHOU, YOUYUAN
To: HUNAN CHANGYUAN LICO CO., LTD.; JINCHI ENERGY MATERIALS CO., LTD.
Reel/Frame 057939/0328 →
Priority Claims (1)
CN 202010087825.7 · Feb 12, 2020 · national
Continuity (1)
Related Publication 20220102717A1 · Mar 31, 2022
References Cited (48)
US 8486564B2 · Nagai · 2013 [cited by applicant]
US 9391318B2 · Nagai et al. · 2016 [cited by applicant]
US 9559351B2 · Mori · 2017 [cited by applicant]
US 9653725B2 · Nagai · 2017 [cited by applicant]
US 10424787B2 · Kamata et al. · 2019 [cited by applicant]
US 10601036B2 · Aida et al. · 2020 [cited by applicant]
US 20050058588A1 · Kang · 2005 [cited by applicant]
US 20110052989A1 · Venkatachalam · 2011 [cited by examiner]
US 20120282525A1 · Nagai · 2012 [cited by applicant]
US 20130011331A1 · Nagai · 2013 [cited by applicant]
US 20130302687A1 · Nagai · 2013 [cited by applicant]
US 20130337331A1 · Mori · 2013 [cited by examiner]
US 20140205901A1 · Nagai · 2014 [cited by examiner]
US 20160093885A1 · Kamata et al. · 2016 [cited by applicant]
US 20170110726A1 · Aida et al. · 2017 [cited by applicant]
US 20170207453A1 · Oda · 2017 [cited by examiner]
US 20180254481A2 · Kamata et al. · 2018 [cited by applicant]
US 20190341610A1 · Aida et al. · 2019 [cited by applicant]
US 20190379038A1 · Toma · 2019 [cited by examiner]
US 20200006770A1 · Kamata et al. · 2020 [cited by applicant]
CN 102612772A · 2012 [cited by applicant]
CN 103562136A · 2014 [cited by applicant]
CN 103765638A · 2014 [cited by applicant]
CN 105122517A · 2015 [cited by applicant]
CN 105185979 · 2015 [cited by examiner]
CN 105185979A · 2015 [cited by applicant]
CN 105958063A · 2016 [cited by applicant]
CN 106133960A · 2016 [cited by applicant]
CN 110518232A · 2019 [cited by applicant]
CN 110931772A · 2020 [cited by applicant]
EP 3176859A1 · 2017 [cited by applicant]
JP 2011119092A · 2011 [cited by applicant]
JP 2013051172A · 2013 [cited by applicant]
JP 2015191844A · 2015 [cited by applicant]
JP 2015227263A · 2015 [cited by applicant]
JP 2016154143A · 2016 [cited by applicant]
JP 2018095505A · 2018 [cited by applicant]
JP 2019149349A · 2019 [cited by applicant]
JP 2020001935A · 2020 [cited by applicant]
WO 2012131779A1 · 2012 [cited by applicant]
Han et al. “Hierarchically assembled LiNi0.8Co0.1Mn0.102 secondary particles with high exposure of {010} plane synthesized via co-precipitation method.” Electrochimica Acta 329 (2020) 135057, available online Oct. 17, 2… [cited by examiner]
Liang et al. “Co-precipitation synthesis of Ni0.6Co0.2Mn0.2(OH)2 precursor and characterization of LiNi0.6Co0.2Mn0.2O2 cathode material for secondary lithium batteries.” Electrochmica Acta 130 (2014) 82-89 (Year: 2014). [cited by examiner]
W. Hua et al. “Unravelling the growth mechanism of hierarchically structured Ni1/3Co1/3Mn1/3(OH)2 and their application as precursors for high-power cathode materials.” Electrochimica Acta 232 (2017) 123-131 (Year: 2017… [cited by examiner]
Su et al. “Exposing the {010} Planes by Oriented Self-Assembly with Nanosheets to Improve the Electrochemical Performances of Ni-Rich Li[Ni0.8Co0.1Mn0.1]O2 Microspheres.” ACS Appl. Mater. Interfaces 2018, 10, 6407-6414 … [cited by examiner]
International Search Report in the international application No. PCT/CN2020/089850, mailed on Nov. 13, 2020, 4 pgs. [cited by applicant]
First Office Action of the Chinese application No. 202010087825.7, issued on Apr. 3, 2020, 19 pgs. [cited by applicant]
Supplementary European Search Report in the European application No. 20904305.8, mailed on Oct. 7, 2022, 6 pgs. [cited by applicant]
English translation of the Written Opinion of the International Search Authority in the international application No. PCT/CN2020/089850, mailed on Nov. 13, 2020, 5 pgs. [cited by applicant]