Porous silicon and method of manufacture
A method for manufacturing porous silicon can include reducing unpurified silica in the presence of a reducing agent to prepare a porous silicon material. A porous silicon material including silicon nanoparticles and clusters of silicon nanoparticles, where the pores are cooperatively defined by the nanoparticles within the clusters.
1. A silicon material comprising:
a primary structure comprising silicon nanoparticles; and
a secondary structure comprising aggregates of the silicon nanoparticles, wherein the aggregates comprise a nonspheroidal morphology;
wherein the silicon nanoparticles cooperatively define pores within the aggregates.
2. The silicon material of claim 1 , wherein the silicon nanoparticles are manufactured from fumed silica.
3. The silicon material of claim 2 , wherein the fumed silica is mixed with a reducing agent, and wherein the mixture of the fumed silica and the reducing agent is heated to a reducing temperature.
4. The silicon material of claim 1 , wherein the nonspheroidal morphology comprises a vermiform morphology.
5. The silicon material of claim 1 , wherein the aggregates comprise an aggregate size between about 1-5 μm.
6. The silicon material of claim 1 , further comprising a tertiary structure comprising agglomerates of the aggregates of the silicon nanoparticles.
7. The silicon material of claim 1 , wherein during expansion, a pore size decreases and a total volume of the aggregates changes by less than 40%.
8. The silicon material of claim 1 , wherein a pore size of the pores is between about 0.2 nm and 500 nm.
9. The silicon material of claim 1 , further comprising a conductive coating.
10. The silicon material of claim 9 , wherein the conductive coating coats the silicon nanoparticles.
11. The silicon material of claim 9 , wherein the conductive coating comprises at least one of: polytetrafluoroethylene, polyvinylidene fluoride, polyacrylic acid, carboxymethyl cellulose, styrene-butadiene rubber, polyacrylonitrile, alginate, polyimide, polyamide, polyaniline, polypyrrole, poly(thiophene), poly(3,4-ethylenedioxythiophene), amorphous carbon, or graphitic carbon.
12. The silicon material of claim 1 , wherein the silicon nanoparticles are interconnected.
13. A method for manufacturing battery anode material, comprising:
mixing fumed silica nanoparticles with a reducing agent to form a first mixture; and
reducing the fumed silica nanoparticles to silicon nanoparticles by heating the first mixture to a reducing temperature of the mixture, wherein the silicon nanoparticles comprise a porosity between 30 and 99%, and wherein the silicon nanoparticles form a secondary structure comprising aggregates.
14. The method of claim 13 , further comprising exposing the fumed silica nanoparticles to a salt by:
dissolving the salt in a solvent; and
evaporating the solvent to coat the fumed silica nanoparticles with the salt.
15. The method of claim 14 , wherein the salt comprises sodium chloride.
16. The method of claim 14 , further comprising milling the mixture of the fumed silica and the salt before exposing the mixture to a reducing agent.
17. The method of claim 13 , further comprising removing a byproduct of the reduction by washing the silicon using an acidic solution.
18. The method of claim 13 , further comprising coating the silicon with an electrically conductive coating.
19. The method of claim 18 , wherein the electrically conductive coating comprises amorphous carbon.
20. The method of claim 13 , wherein the reducing agent comprises at least one of magnesium or aluminium.
21. The method of claim 13 , further comprising purifying the fumed silica before mixing the fumed silica with the salt.
22. The method of claim 13 , further comprising coating the fumed silica particles with a carbonaceous coating.
23. The method of claim 22 , wherein the carbonaceous coating comprises a polymeric coating.