Chemically strengthened glass plate, and cover glass and electronic device comprising chemically strengthened glass
The present invention relates to a chemically strengthened glass sheet in which a value of SB/(SA×t) is 5.0 mm −1 or more, where SA (MPa·μm) is an integrated value of a compressive stress from a surface of the glass sheet to a depth of 10 μm, SB (MPa·μm) is an integrated value of a compressive stress from the depth of 10 μm to DOL which is a depth at which the compressive stress is zero, and t (mm) is a thickness of the glass sheet.
1. A chemically strengthened glass sheet, wherein the chemically strengthened glass sheet has a value of SB/(SA×t) of 5.0 mm −1 or more, where SA (MPa·μm) is an integrated value of a compressive stress from a surface of the glass sheet to a depth of 10 μm, SB (MPa·μm) is an integrated value of a compressive stress from the depth of 10 μm to DOL which is a depth at which the compressive stress is zero, t (mm) is a thickness of the glass sheet, and SA is 4,000 MPa·μm or less and SB is 12,000 MPa·μm or more.
2. The chemically strengthened glass sheet according to claim 1 , wherein the DOL is 110 μm or more.
3. The chemically strengthened glass sheet according to claim 1 , wherein the chemically strengthened glass sheet has a four-point bending strength of 600 MPa or more.
4. The chemically strengthened glass sheet according to claim 1 , wherein the chemically strengthened glass sheet has a compressive stress value of 150 MPa or more at a position of a depth of 50 μm from the surface.
5. The chemically strengthened glass sheet according to claim 1 , wherein the chemically strengthened glass sheet has a surface compressive stress value of 500 MPa or more.
6. The chemically strengthened glass sheet according to claim 1 , wherein the chemically strengthened glass sheet has a base composition comprising, in terms of mol % on an oxide basis, 40-60% of SiO 2 , 20-45% of Al 2 O 3 and 5-15% of Li 2 O.
7. The chemically strengthened glass sheet according to claim 1 , wherein the chemically strengthened glass sheet is a crystallized glass comprising one or more crystals selected from the group consisting of a β-spodumene crystal, a lithium metasilicate crystal, and a lithium phosphate crystal.
8. The chemically strengthened glass sheet according to claim 7 , wherein the crystallized glass comprises the β-spodumene crystal comprising, in terms of mass % on an oxide basis, 58-70 mass % of SiO 2 , 15-30 mass % of Al 2 O 3 , 2-10 mass % of Li 2 O, 0-5 mass % of Na 2 O, and 0-2 mass % of K 2 O, and having a total content of Na 2 O and K 2 O of 1-5 mass %.
9. A cover glass, comprising:
the chemically strengthened glass sheet of claim 1 .
10. An electronic device, comprising:
the chemically strengthened glass sheet of claim 1 .
11. The chemically strengthened glass sheet according to claim 1 , wherein a sum (SA+SB) of SA and SB is 15,000 MPa·μm or more.
12. The chemically strengthened glass sheet according to claim 11 , wherein the DOL is 110 μm or more.
13. The chemically strengthened glass sheet according to claim 11 , wherein the chemically strengthened glass sheet has a four-point bending strength of 600 MPa or more.
14. The chemically strengthened glass sheet according to claim 11 , wherein the chemically strengthened glass sheet has a compressive stress value of 150 MPa or more at a position of a depth of 50 μm from the surface.
15. The chemically strengthened glass sheet according to claim 11 , wherein the chemically strengthened glass sheet has a surface compressive stress value of 500 MPa or more.
16. The chemically strengthened glass sheet according to claim 1 , wherein the chemically strengthened glass sheet has a base composition comprising, in terms of mol % on an oxide basis, 40-60% of SiO 2 , 20-45% of Al 2 O 3 and 5-15% of Li 2 O.
17. The chemically strengthened glass sheet according to claim 11 , wherein the chemically strengthened glass sheet is a crystallized glass comprising one or more crystals selected from the group consisting of a β-spodumene crystal, a lithium metasilicate crystal, and a lithium phosphate crystal.
18. The chemically strengthened glass sheet according to claim 17 , wherein the crystallized glass comprises the β-spodumene crystal comprising, in terms of mass % on an oxide basis, 58-70 mass % of SiO 2 , 15-30 mass % of Al 2 O 3 , 2-10 mass % of Li 2 O, 0-5 mass % of Na 2 O, and 0-2 mass % of K 2 O, and having a total content of Na 2 O and K 2 O of 1-5 mass %.
19. A cover glass, comprising:
the chemically strengthened glass sheet of claim 11 .
20. An electronic device, comprising:
the chemically strengthened glass sheet of claim 11 .