High temperature treated media
A thermally bonded filtration media that can be used in high temperature conditions in the absence of any loss of fiber through thermal effects or mechanical impact on the fiber components is disclosed. The filter media can be manufactured and used in a filter unit or structure, can be placed in a stream of removable fluid, and can remove a particulate load from the mobile stream at an increased temperature range. The combination of bi-component fiber, other filter media fiber, and other filtration additives provides an improved filtration media having unique properties in high temperature, high performance applications.
1. A nonwoven web comprising fibers in a thermally bonded sheet, the nonwoven web comprising:
(a) about 5 wt-% to about 25 wt-% of a first bi-component fiber comprising a first core polymer with a melting point of 240° C. or greater and a first shell polymer with a melting point of 115° C. or lower; wherein the first bi-component fiber has a diameter of about 5 μm to about 25 μm;
(b) about 25 wt-% to about 60 wt-% of a second bi-component fiber comprising a second core polymer with a melting point of 240° C. or greater and a second shell polymer with a melting point of 120° C. or greater and lower than the melting point of the second core polymer; wherein the second bi-component fiber has a diameter of about 5 μm to 25 μm; and
(c) a staple fiber,
wherein the nonwoven web has a solidity of 10% or less.
2. The nonwoven web of claim 1 , wherein the melting point of the second shell polymer is in a range of 140° C. to 180° C.
3. The nonwoven web of claim 1 , wherein the staple fiber comprises about 1 wt-% to 20 wt-% of a polyester fiber having a diameter of 7 to 15 μm and about 10 wt-% to 50 wt-% of cotton linter fiber having a diameter of 15 μm to 55 μm.
4. The nonwoven web of claim 1 , wherein the web exhibits a wet bursting strength of 5 lb/in 2 or greater.
5. The nonwoven web of claim 1 , wherein the web exhibits a wet bursting strength of 10 lb/in 2 to 20 lb/in 2 .
6. The nonwoven web of claim 1 , wherein the web has a tensile strength of 2 lb/in or greater at 100° C.
7. The nonwoven web of claim 1 , wherein the web comprises from 0.5 wt-% to 5 wt-% of a C 2 to C 9 fluorochemical treatment, based on a total weight of the web.
8. The nonwoven web of claim 7 , wherein the fluorochemical comprises a C 2-6 fluoroalkyl acrylic polymer.
9. The nonwoven web of claim 7 , wherein the fluorochemical comprises a C 6 fluoroalkyl acrylic polymer.
10. The nonwoven web of claim 1 , wherein the fibers comprise a treatment on the fibers of about 2 wt-% of a C 6 fluoroalkyl acrylic polymer.
11. The nonwoven web of claim 1 , wherein the staple fiber comprises cotton, polyester, cellulose, or a combination thereof.
12. The nonwoven web of claim 11 , wherein the staple fiber comprises cotton linter and polyester fibers.
13. A filter element comprising the nonwoven web of claim 1 .
14. The filter element of claim 13 , wherein the filter element comprises filter media comprising two or more layers of the nonwoven web.
15. The filter element of claim 13 , wherein the two or more layers comprise an efficiency layer and a loading layer.