Method for manufacturing magnetic powder, method for manufacturing compact, magnetic powder, and compact
A method for manufacturing a magnetic powder includes a step of producing a magnetic powder by spray-drying a spray liquid containing first magnetic particles, second magnetic particles, a thermosetting resin, and an organic solvent. A magnetic powder includes first magnetic particles and a thermosetting resin coating film on surfaces of the first magnetic particles. The first magnetic particles are soft magnetic metal particles. The resin coating film contains second magnetic particles. The second magnetic particles have a smaller average particle size than the first magnetic particles.
1. A method for manufacturing a magnetic powder, the method comprising:
producing a magnetic powder by spray-drying a spray liquid containing first magnetic particles, second magnetic particles, a thermosetting resin, and an organic solvent,
wherein the magnetic powder includes the first magnetic particles and a thermosetting resin coating film on surfaces of the first magnetic particles,
the first magnetic particles are soft magnetic metal particles,
the resin coating film contains the second magnetic particles, and
the second magnetic particles have a smaller average particle size than the first magnetic particles.
2. The method for manufacturing a magnetic powder according to claim 1 , wherein
the second magnetic particles are buried in the resin coating film.
3. The method for manufacturing a magnetic powder according to claim 1 , wherein
the second magnetic particles have an average particle size of from 1 nm to 1 μm.
4. The method for manufacturing a magnetic powder according to claim 1 , wherein
the average particle size of the second magnetic particles is equal to or smaller than 1/10 an average particle size of the first magnetic particles.
5. The method for manufacturing a magnetic powder according to claim 1 , wherein
the second magnetic particles are metal oxide magnetic particles.
6. The method for manufacturing a magnetic powder according to claim 1 , wherein
the second magnetic particles are ferrite magnetic particles.
7. The method for manufacturing a magnetic powder according to claim 6 , wherein
the ferrite magnetic particles contain at least one ferrite selected from the group consisting of magnetite, manganese ferrite, magnesium ferrite, strontium ferrite, nickel-zinc ferrite, and nickel ferrite.
8. The method for manufacturing a magnetic powder according to claim 6 , wherein
the ferrite magnetic particles contain one or both of magnetite and manganese ferrite in total of 65 mass % or more.
9. The method for manufacturing a magnetic powder according to claim 1 , wherein
the second magnetic particles are spherical.
10. A method for manufacturing a compact, the method comprising:
producing a magnetic powder by the method for manufacturing a magnetic powder according to claim 1 , and
producing a compact by subjecting the magnetic powder to heat press molding to cure the thermosetting resin coating film.
11. The method for manufacturing a compact according to claim 10 , wherein
the producing of a compact involves subjecting a mixture containing the magnetic powder and an oxide powder to heat press molding.
12. The method for manufacturing a compact according to claim 10 , wherein
the compact is a powder magnetic core.
13. The method for manufacturing a compact according to claim 10 , further comprising:
disposing a coil conductor inside the compact or on a surface of the compact.
14. A magnetic powder comprising:
first magnetic particles, and
a thermosetting resin coating film on surfaces of the first magnetic particles,
wherein the first magnetic particles are soft magnetic metal particles,
the resin coating film contains second magnetic particles, and
the second magnetic particles have a smaller average particle size than the first magnetic particles.
15. The magnetic powder according to claim 14 , wherein
the second magnetic particles are buried in the resin coating film.
16. The magnetic powder according to claim 14 , wherein
the second magnetic particles have an average particle size of from 1 nm to 1 μm.
17. The magnetic powder according to claim 14 , wherein
the average particle size of the second magnetic particles is equal to or smaller than 1/10 an average particle size of the first magnetic particles.
18. The magnetic powder according to claim 14 , wherein
the second magnetic particles are metal oxide magnetic particles.
19. The magnetic powder according to claim 14 , wherein
the second magnetic particles are ferrite magnetic particles.
20. The magnetic powder according to claim 19 , wherein
the ferrite magnetic particles contain at least one ferrite selected from the group consisting of magnetite, manganese ferrite, magnesium ferrite, strontium ferrite, nickel-zinc ferrite, and nickel ferrite.