Resin composition, adhesive member, and display device
A resin composition has a viscosity of equal to or less than about 20 mPa·s at a temperature in a range of about 30° C. to about 50° C. as measured according to JIS Z8803, a storage modulus in a range of about 1.7×10 5 Pa to about 3×10 5 Pa at about −20° C., and a storage modulus in a range of about 1.5×10 4 Pa to about 6×10 4 Pa at about 25° C. An adhesive member formed of the resin composition is also provided.
1. A resin composition comprising at least one bifunctional (meth)acrylate monomer selected from the group consisting of 1,4-butanediol di(meth)acrylate, 1,3-butylene glycol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, 1,8-octanediol di(meth)acrylate, 1,9-octanediol diacrylate, 1,9-nonanediol diacrylate, 1,12-dodecanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, dicyclopentanyl di(meth)acrylate, cyclohexane-1,4-dimethanol di(meth)acrylate, tricyclodecanedimethanol (meth)diacrylate, dimethylol dicyclopentane di(meth)acrylate, neopentyl glycol-modified trimethylpropane di(meth)acrylate, adamantane di(meth)acrylate, and trimethylolpropane tri(meth)acrylate,
wherein the resin composition has a viscosity equal to or less than about 20 mPa·s at a temperature in a range of about 30° C. to about 50° C.; and
wherein, after UV curing, the resin composition has;
a storage modulus in a range of about 1.7×10 5 Pa to about 3×10 5 Pa at about −20° C.; and
a storage modulus in a range of about 1.5×10 4 Pa to about 6×10 4 Pa at about 25° C.
2. The resin composition of claim 1 , wherein, after UV curing, a ratio of the storage modulus at about 25° C. to the storage modulus at about −20° C. is in a range of about 0.05 to about 1.
3. The resin composition of claim 1 , wherein, after UV curing, the resin composition has a storage modulus in a range of about 1.5×10 4 Pa to about 6×10 4 Pa at about 60° C.
4. The resin composition of claim 3 , wherein, after UV curing, a ratio of the storage modulus at about 60° C. to the storage modulus at about −20° C. is in a range of about 0.05 to about 1.
5. The resin composition of claim 1 , further comprising an organic solvent,
wherein a content of the organic solvent is less than about 0.5 wt % based on a total weight of the resin composition.
6. The resin composition of claim 1 ,
wherein a content of the at least one bifunctional (meth)acrylate monomer is less than about 1 wt % based on a total weight of the resin composition.
7. The resin composition of claim 1 , further comprising a (meth)acrylate monomer containing a hydroxy group.