Method for producing positive electrode active material for lithium ion secondary batteries
Making a positive electrode active material for lithium ion secondary batteries includes: weighting and mixing lithium carbonate and a compound containing respective metallic elements other than Li in a composition formula Li α Ni x Co y M2 1-x-y-z M2 z O 2+β so as to have a metallic constituent ratio of the formula to obtain a mixture, and firing the mixture to obtain a lithium composite compound. Performing, on the mixture, a first heat treatment at 200° C. to 400° C. for 0.5 to 5 hours to obtain a first precursor. A step of performing a heat treatment on the first precursor under an oxidizing atmosphere at 450° C. to 800° C. for 0.5 to 50 hours, and reacting 92 mass % or more of the lithium carbonate to obtain a second precursor, and a finishing step of performing a heat treatment on the second precursor under an oxidizing atmosphere at 755° C. to 900° C. for 0.5 to 50 hours to obtain the lithium composite compound.
1. A method for producing positive electrode active material for lithium ion secondary batteries, the method comprising:
a mixing step of weighing and mixing a lithium carbonate and a compound containing respective metallic elements other than Li in Formula (1), Li α Ni x Co y M1 1-x-y-z M2 z O 2+ß , so as to have a metallic constituent ratio of a composition formula in accordance with the Formula (1) to obtain a mixture,
where values in the Formula (1) meet: 0.97≤α≤1.08, −0.1≤ß≤0.1, 0.7<x≤0.9, 0.03≤y≤0.3, 0≤z≤0.1, and 0<1-x-y-z, M1 is at least one kind of an element selected from the group consisting of Mn and Al, and M2 is at least one kind of an element selected from the group consisting of Mg, Ti, Zr, Mo, and Nb; and
a firing step of firing the mixture to obtain a lithium composite compound expressed by the Formula (1),
wherein the firing step includes:
a first precursor forming step of performing a heat treatment on the mixture at a heat treatment temperature of 200° C. or more and 400° C. or less for 0.5 hours or more and 5 hours or less to obtain a first precursor;
a second precursor forming step of performing a heat treatment on the first precursor under an oxidizing atmosphere at a heat treatment temperature of 450° C. or more and 800° C. or less for 0.5 hours or more and 50 hours or less, the second precursor forming step reacting 92 mass % or more of the lithium carbonate to obtain a second precursor;
a measurement step that includes measuring an amount of reacted lithium carbonate in the second precursor after the second precursor forming step; and
a finishing heat treatment step of performing a heat treatment on the second precursor under an oxidizing atmosphere at a heat treatment temperature of 755° C. or more and 900° C. or less for 0.5 hours or more and 50 hours or less to obtain the lithium composite compound.
2. The method for producing positive electrode active material for lithium ion secondary batteries according to claim 1 ,
wherein the heat treatment temperature in the finishing heat treatment step is 840° C. or more and 890° C. or less.
3. The method for producing positive electrode active material for lithium ion secondary batteries according to claim 1 ,
wherein the second precursor forming step forms the second precursor such that 97 mass % or more of the lithium carbonate has reacted, the lithium carbonate being contained in the mixture weighed and mixed so as to have the metallic constituent ratio of the composition formula in the Formula (1).
4. The method for producing positive electrode active material for lithium ion secondary batteries according to claim 1 ,
wherein the heat treatment temperature in the second precursor forming step is 600° C. or more and 700° C. or less.
5. The method for producing positive electrode active material for lithium ion secondary batteries according to claim 1 ,
wherein the M1 in the Formula (1) is Mn, 0.04≤1-x-y-z≤0.18 being met.
6. The method for producing positive electrode active material for lithium ion secondary batteries according to claim 1 ,
wherein the lithium composite compound is not water-washed after the finishing heat treatment step.
7. The method for producing positive electrode active material for lithium ion secondary batteries according to claim 1 , the method comprising
a step of performing a water washing on the lithium composite compound after the finishing heat treatment step.
8. The method for producing positive electrode active material for lithium ion secondary batteries according to claim 7 , the method comprising
a step of performing a drying at least once or more after the step of performing the water washing.