Transient liquid phase bonding compositions and power electronics assemblies incorporating the same

Inventors: Shailesh N. Joshi (Ann Arbor, MI); Yanghe Liu (Ann Arbor, MI)
Assignee: Toyota Motor Engineering & Manufacturing North America, Inc.
B22F1/17B22F3/1035B22F7/064B23K35/22C08K3/08C23C18/1633C23C18/1635H01L23/3736H01L24/29H01L24/83B22F2301/30B22F2999/00C08K2003/085C22C1/0416C22C1/0425C22C1/0433C22C1/0466C22C1/0483H01L23/36H01L24/00H01L24/48H01L24/73H01L2224/29309H01L2224/29311H01L2224/29324H01L2224/29339H01L2224/29347H01L2224/29355H01L2224/29439H01L2224/29447H01L2224/29455H01L2224/29499H01L2224/32245H01L2224/48091H01L2224/48139H01L2224/48247H01L2224/48472H01L2224/73265H01L2224/83825H01L2924/00014H01L2924/10254H01L2924/10272H01L2924/10323H01L2924/10325H01L2924/1033H01L2924/1203H01L2924/13055H01L2924/13091H01L2924/19107
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,208,448
App. No.
17/411,615
Granted
Jan 28, 2025
Kind
B2
Abstract

A transient liquid phase (TLP) composition includes a plurality of first high melting temperature (HMT) particles, a plurality of second HMT particles, and a plurality of low melting temperature (LMT) particles. Each of the plurality of first HMT particles have a core-shell structure with a core formed from a first high HMT material and a shell formed from a second HMT material that is different than the first HMT material. The plurality of second HMT particles are formed from a third HMT material that is different than the second HMT material and the plurality of LMT particles are formed from a LMT material. The LMT particles have a melting temperature less than a TLP sintering temperature of the TLP composition and the first, second, and third HMT materials have a melting point greater than the TLP sintering temperature.

Claims (44)

1. A method, comprising:

positioning a TLP bonding layer between a metal substrate and a semiconductor device to form an assembly, the TLP bonding layer comprising first HMT particles, second HMT particles, and LMT particles, wherein:

each of the first HMT particles comprise a core-shell structure having a core formed from a first HMT material and a shell formed from a second HMT material, each of the second HMT particles is formed from a third HMT material, and

each of the plurality of LMT particles is formed from a LMT material; and

heating the assembly to a TLP sintering temperature greater than a melting point of the LMT material to cause the LMT particles to at least partially melt and form a TLP intermetallic layer between the first and second HMT particles, the metal substrate, and the semiconductor device, forming a TLP bond layer between the metal substrate and the semiconductor device having a variation in stiffness of the TLP bond layer,

wherein, after heating the assembly, the TLP bonding layer has a graded stiffness along the thickness of the TLP bonding layer between the metal substrate and the semiconductor device.

2. The method of claim 1 , wherein positioning the TLP bonding layer comprises arranging the first HMT particles within the TLP bonding layer to have a graded average diameter along a thickness of the TLP bonding layer.

3. The method of claim 1 , wherein positioning the TLP bonding layer comprises arranging the first HMT particles within the TLP bonding layer to have a graded density along a thickness of the TLP bonding layer.

4. The method of claim 3 , wherein positioning the TLP bonding layer further comprises positioning or laying down a plurality of layers of TLP compositions having different quantities of first HMT particles to achieve the graded density along the thickness of the TLP bonding layer.

5. The method of claim 3 , wherein positioning the TLP bonding layer to have a graded density further comprises:

depositing a first layer comprising a first density of the first HMT particles onto the metal substrate; and

depositing a second layer comprising a second density of the first HMT particles onto the first layer.

6. The method of claim 5 , wherein a thickness of the first layer is equal to a thickness of the second layer.

7. The method of claim 5 , wherein a thickness of the first layer is not equal to a thickness of the second layer.

8. The method of claim 3 , wherein positioning the TLP bonding layer to have a graded density further comprises:

positioning a first thin foil, formed from the LMT material, onto the metal substrate, wherein a first density of the first HMT particles and the second HMT particles are attached to the first thin foil; and

positioning a second thin foil, formed from the LMT material, onto the first thin foil, wherein a second density of first HMT particles and second HMT particles are attached to the second thin foil.

9. The method of claim 8 , wherein a thickness of the first thin foil is equal to a thickness of the second thin foil.

10. The method of claim 8 , wherein a thickness of the first thin foil is not equal to a thickness of the second thin foil.

11. The method of claim 1 , further comprising incorporating the assembly into an inverter circuit.

12. The method of claim 1 , wherein:

the first HMT material is nickel, silver, copper, aluminum, or an alloy thereof;

the second HMT material is nickel, silver, copper, or an alloy thereof;

the third HMT material is nickel, silver, copper, aluminum, or an alloy thereof; and

the LMT material is tin, indium, or an alloy thereof.

13. A method, comprising:

providing a metal substrate;

positioning a first thin foil, formed from a LMT material, onto the metal substrate, wherein a first density of first HMT particles and second HMT particles are attached to the first thin foil, wherein the first HMT particles comprise a core-shell structure having a core formed from a first HMT material and a shell formed from a second HMT material and the second HMT particles are formed from a third HMT material;

positioning a second thin foil, formed from the LMT material, onto the first thin foil, wherein a second density of first HMT particles and second HMT particles are attached to the second thin foil;

placing a semiconductor device over the second thin foil to form an assembly;

heating the assembly to a TLP sintering temperature greater than a melting point of the LMT material to cause LMT particles in the LMT material to at least partially melt and form a TLP intermetallic layer between the first and second HMT particles, the metal substrate, and the semiconductor device, thereby forming a TLP bond layer between the metal substrate and the semiconductor device having a variation in stiffness of the TLP bond layer; and

incorporating the assembly into an invertor circuit.

14. The method of claim 13 , wherein, after heating the assembly, the TLP bonding layer has a graded stiffness between the metal substrate and the semiconductor device.

15. The method of claim 13 , wherein positioning the first thin foil and positioning the second thin foil is completed such that the first HMT particles within the TLP bonding layer have a graded average diameter along a thickness of the TLP bond layer resulting therefrom.

16. The method of claim 13 , wherein a thickness of the first thin foil is equal to a thickness of the second thin foil.

17. The method of claim 13 , wherein a thickness of the first thin foil is not equal to a thickness of the second thin foil.

18. A method, comprising:

positioning a TLP bonding layer comprising a first layer having a first density of first HMT particles and a second layer having a second density of the first HMT particles between a metal substrate and a semiconductor device to form an assembly, the TLP bonding layer further comprising second HMT particles and LMT particles, wherein:

each of the first HMT particles comprise a core-shell structure having a core formed from a first HMT material and a shell formed from a second HMT material,

each of the second HMT particles is formed from a third HMT material, and

each of the plurality of LMT particles is formed from a LMT material;

heating the assembly to a TLP sintering temperature greater than a melting point of the LMT material to cause the LMT particles to at least partially melt and form a TLP intermetallic layer between the first and second HMT particles, the metal substrate, and the semiconductor device, forming a TLP bond layer between the metal substrate and the semiconductor device having a variation in stiffness of the TLP bond layer; and

incorporating the assembly into an invertor circuit,

wherein, after heating the assembly, the TLP bonding layer has a graded stiffness along the thickness of the TLP bonding layer between the metal substrate and the semiconductor device.

Assignments (2)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Apr 17, 2025
From: TOYOTA MOTOR ENGINEERING & MANUFACTURING NORTH AMERICA, INC.
To: TOYOTA JIDOSHA KABUSHIKI KAISHA
Reel/Frame 070873/0539 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Aug 25, 2021
From: JOSHI, SHAILESH N; LIU, YANGHE
To: TOYOTA MOTOR ENGINEERING & MANUFACTURING NORTH AMERICA, INC.
Reel/Frame 057287/0614 →
Continuity (2)
Continuation 15700712 · Sep 11, 2017
Related Publication 20210381110A1 · Dec 9, 2021
References Cited (23)
US 3342563A · Butts · 1967 [cited by applicant]
US 3545944A · Emanuelson et al. · 1970 [cited by applicant]
US 4602731A · Dockus · 1986 [cited by applicant]
US 7244467B2 · Grossman et al. · 2007 [cited by applicant]
US 7565996B2 · Das · 2009 [cited by examiner]
US 9343425B1 · Joshi · 2016 [cited by examiner]
US 9620434B1 · Joshi · 2017 [cited by examiner]
US 20070089811A1 · Ikeda · 2007 [cited by examiner]
US 20080083748A1 · Thyssen et al. · 2008 [cited by applicant]
US 20150008253A1 · Yoon · 2015 [cited by examiner]
US 20160108204A1 · Joshi et al. · 2016 [cited by applicant]
US 20170062304A1 · Joshi · 2017 [cited by examiner]
US 20170080682A1 · Joshi et al. · 2017 [cited by applicant]
US 20170095891A1 · Anderson et al. · 2017 [cited by applicant]
US 20170263586A1 · Joshi · 2017 [cited by examiner]
US 20170368644A1 · Handwerker · 2017 [cited by examiner]
CN 102596488B · 2013 [cited by applicant]
CN 102888536B · 2015 [cited by applicant]
JP 2017177156A · 2017 [cited by examiner]
Cooke, Kavian O. et al., “Transient liquid phase diffusion bonding Al-6061 using nano-dispersed Ni coatings”, Materials & Design, Jan. 2012; URL: http://www.sciencedirect.com/science/article/pii/S0261306911003207. [cited by applicant]
“Nickel-Aluminum composite powders”, Phelly Materials (U.S.A.) Inc., published/accessed: Jun. 16, 2017; URL: http://www.phelly.com/2007ThermalSpray/Nickel-Aluminum%20Powder.pdf. [cited by applicant]
Alhazaa, A.N. et al., “Transient liquid phase bonding of Magnesium alloys AZ31 using Nickel coatings and high frequency induction heat sintering”, Journal of King Saud University—Science, Apr. 2016; URL: http://www.scie… [cited by applicant]
“Reference Sheet: Melting Points”, American Elements, https://www.americanelements.com/PDFs/reference/AE-melting-point-reference-sheet.pdf (Year: 2021). [cited by applicant]