Method and device for directly preparing foamed polylactic acid (PLA) product from PLA melt
A method for directly preparing a foamed polylactic acid (PLA) product from a PLA melt includes PLA melt preparation, feeding, and two-stage extrusion. In the two-stage extrusion, a pressure at an outlet of a first-stage twin-screw extruder is 15 MPa to 17 MPa, a PLA melt is fed at a rate of 250 kg/h, a foaming additive is fed at a rate of 7.5 kg/h to 10 kg/h, and a foaming gas is fed at a rate of 2.8 L/h to 7.5 L/h. The method can ensure both foamability and quality of a material and reduce more than ⅓ of energy consumption; and an obtained product has an adjustable foaming rate of 3 to 25, a crystallinity of 40.3% to 48.5%, a tensile strength of 8.7 MPa to 19.6 MPa, and an apparent density of 0.05 g/cm 3 to 0.4 g/cm 3 .
1. A method for directly preparing a foamed polylactic acid (PLA) product from a PLA melt, comprising: PLA melt preparation, feeding, and two-stage extrusion, wherein
the PLA melt obtained from the PLA melt preparation has a weight-average molecular weight of 200,000 to 221,000 and a molecular weight distribution of 1.21 to 1.24; and
the two-stage extrusion comprises first-stage extrusion and a second-stage extrusion, wherein
in the first-stage extrusion, a first-stage twin-screw extruder has a length-to-diameter ratio of 40:1, and a temperature distribution of 245° C. to 195° C. in a gradual decrease trend from a main feeding port of the first-stage twin-screw extruder to a die head, and
in the second-stage extrusion, a second-stage single-screw extruder has a length-to-diameter ratio of ≥30:1, and a temperature range of 180° C. to 128° C.
2. The method for directly preparing the foamed PLA product from the PLA melt according to claim 1 , wherein in the feeding, a feeding rate ratio of the PLA melt to a foaming additive is 25-35:1.
3. The method for directly preparing the foamed PLA product from the PLA melt according to claim 1 , wherein in the first-stage extrusion, a feeding port for a foaming additive is located at a position of ⅔ a length of a screw barrel from the main feeding port and ⅓ the length of the screw barrel from the die head.
4. The method for directly preparing the foamed PLA product from the PLA melt according to claim 1 , wherein a foaming gas used for the first-stage extrusion is one selected from the group consisting of alkane, halogenated alkene, carbon dioxide, nitrogen, argon, and Freon.
5. The method for directly preparing the foamed PLA product from the PLA melt according to claim 1 , wherein in the PLA melt preparation, a mass ratio of lactide, stannous octoate, isooctyl alcohol, and 2-ethyloctanoic acid is 7,500:1:10-15:0.1.
6. The method for directly preparing the foamed PLA product from the PLA melt according to claim 1 , wherein in the feeding, a weight of a foaming additive is 0.5% to 10% of a weight of the PLA melt;
the foaming additive comprises a chain extender, a nucleating agent, and a lubricant, wherein
the chain extender accounts for 8 wt % to 17 wt % of the foaming additive,
the nucleating agent accounts for 50 wt % to 83 wt % of the foaming additive, and
the lubricant accounts for 8 wt % to 17 wt % of the foaming additive.
7. The method for directly preparing the foamed PLA product from the PLA melt according to claim 1 , wherein a foaming gas used for the first-stage extrusion is one selected from the group consisting of alkane, halogenated alkene, carbon dioxide, nitrogen, argon, and Freon.