Process for preparing a catalyst for the hydrogenation of aromatics, comprising a step of forming a Ni—Cu alloy in pre-impregnation
A process for preparing a catalyst for the hydrogenation of aromatic or polyaromatic compounds comprising nickel, copper and a support comprising at least one refractory oxide, comprising the following steps: bringing the support into contact with a solution containing at least one copper precursor and one nickel precursor; drying the catalyst precursor at a temperature of less than 250° C.; reducing the catalyst precursor by bringing said precursor into contact with a reducing gas at a temperature of between 150° C. and 250° C.; bringing the catalyst precursor into contact with a solution comprising a nickel precursor; a step of drying the catalyst precursor at a temperature of less than 250° C.; reducing the catalyst precursor by bringing said precursor into contact with a reducing gas at a temperature of between 150° C. and 250° C.
1. A process for preparing a catalyst for the hydrogenation of aromatic or polyaromatic compounds comprising nickel, in a proportion of 20% to 45% by weight of nickel element relative to the total weight of the catalyst, and copper, in a proportion of 0.5% to 15% by weight of copper element relative to the total weight of the catalyst, and a support comprising at least one refractory oxide chosen from silica, alumina and silica-alumina, said process consisting of the following steps:
a) a step of bringing the support into contact with at least one solution consisting of, as metal precursors in said solution, of at least one copper precursor and one nickel precursor at a desired nickel concentration in order to obtain, on the final catalyst, a content of between 0.5% and 15% by weight of nickel element relative to the total weight of the final catalyst;
b) at least one step of drying the catalyst precursor resulting from step a) at a temperature of less than 250° C.;
c) optionally, a heat treatment of the catalyst precursor obtained at the end of step b) at a temperature of between 250 and 1000° C., in the presence or absence of water;
d) the catalyst precursor resulting from step b), or optionally step c), is reduced by bringing said catalyst precursor into contact with a reducing gas at a temperature of between 150 and 250° C.;
e) a step of bringing the catalyst precursor obtained at the end of step d) into contact with a solution consisting of, as a metal precursor in said solution, of at least one nickel precursor;
f) at least one step of drying the catalyst precursor resulting from step e) at a temperature of less than 250° C.;
g) optionally, a heat treatment of the catalyst precursor obtained at the end of step f) at a temperature of between 250 and 1000° C., in the presence or absence of water;
h) the catalyst precursor resulting from step f), or optionally step g), is reduced by bringing said catalyst precursor into contact with a reducing gas at a temperature of between 150 and 250° C.
2. The process as claimed in claim 1 , wherein, in step a), the mole ratio between nickel and copper is between 0.5 and 5.
3. The process as claimed in claim 1 , wherein step d) and/or h) is (are) carried out at a temperature of between 160 and 230° C.
4. The process as claimed in claim 1 , wherein step d) and/or h) is (are) carried out at a temperature of between 170 and 220° C.
5. The process as claimed in claim 1 , wherein steps d) and/or h) is (are) carried out for between 10 minutes and 110 minutes.
6. The process as claimed in claim 1 , also comprising a step of passivation of the catalyst precursor with a sulfur-containing compound after the reduction step d) but before step e), and/or after the reduction step h).
7. The process as claimed in claim 6 , wherein the passivation step(s) is (are) carried out at a temperature of between 20 and 350° C. for 10 to 240 minutes.
8. The process as claimed in claim 6 , wherein said sulfur-containing compound is chosen from thiophene, thiophane, dimethyl sulfide, diethyl sulfide, dipropyl sulfide, propylmethyl sulfide and dithiodiethanol.
9. The process as claimed in claim 1 , wherein the copper precursor is chosen from copper acetate, copper acetylacetonate, copper nitrate, copper sulfate, copper chloride, copper bromide, copper iodide and copper fluoride.
10. The process as claimed in claim 9 , wherein the copper precursor is copper nitrate.
11. The process as claimed in claim 1 , wherein the reducing gas of step d) and/or h) is dihydrogen.
12. The process as claimed in claim 11 , wherein the dihydrogen flow rate, expressed in 1/hour/gram of catalyst precursor, is between 0.01 and 100 l/hour/gram of catalyst precursor.
13. The process as claimed in claim 1 , wherein the nickel precursor supplied during step a) and/or e) is chosen from nickel nitrate, nickel carbonate and nickel hydroxide.
14. The process as claimed in claim 1 , wherein the solution in step a) and/or e) are independently aqueous or organic solutions, or a mixture of water and at least one organic solvent.
15. The process as claimed in claim 1 , wherein the solution in step a) and/or e) are independently aqueous or organic solutions, or a mixture of water and at least one organic solvent, wherein the organic solution contains methanol, ethanol, phenol, acetone, toluene or dimethyl sulfoxide.
16. The process as claimed in claim 1 , wherein the solution in step a) and/or e) are aqueous solutions.
17. A process for the hydrogenation of at least one aromatic or polyaromatic compound present in a hydrocarbon feedstock having a final boiling point of less than or equal to 650° C., said process being carried out in the gas phase or in the liquid phase, at a temperature of between 30 and 350° C., at a pressure of between 0.1 and 20 MPa, at a hydrogen/(aromatic compounds to be hydrogenated) mole ratio between 0.1 and 10 and at an hourly space velocity HSV of between 0.05 and 50 h −1 , in the presence of a catalyst obtained as claimed in claim 1 .