Superabsorbent polymer and preparation method for the same
A method of preparing a superabsorbent polymer includes preparing a base resin in which an acrylic acid-based monomer having acidic groups which are at least partially neutralized and an internal crosslinking agent are crosslinked in the presence of a sodium polycarboxylate surfactant; and heating the base resin in the presence of a surface crosslinking agent to carry out surface modification of the base resin, wherein the internal crosslinking agent includes a first epoxy crosslinking agent having an epoxy equivalent weight of 100 g/eq or more to less than 130 g/eq, and a second epoxy crosslinking agent having an epoxy equivalent weight of 130 g/eq or more. The superabsorbent polymer provides improved rewetting property and liquid permeability.
1. A method of preparing a superabsorbent polymer, comprising:
preparing a base resin in which an acrylic acid-based monomer having acidic groups which are at least partially neutralized and an internal crosslinking agent are crosslinked in the presence of a sodium polycarboxylate surfactant; and
heating the base resin in the presence of a surface crosslinking agent to carry out surface modification of the base resin,
wherein the internal crosslinking agent includes a first epoxy crosslinking agent having an epoxy equivalent weight of 100 g/eq or more to less than 130 g/eq, and a second epoxy crosslinking agent having an epoxy equivalent weight of 130 g/eq or more.
2. The method of claim 1 , wherein the sodium polycarboxylate surfactant is included in an amount of 0.01 part by weight to 1 part by weight with respect to 100 parts by weight of the acrylic acid-based monomer.
3. The method of claim 1 , wherein the sodium polycarboxylate surfactant has a density of 1.07 g/ml to 1.13 g/ml, and a weight average molecular weight of 500 g/mol to 1,000,000 g/mol.
4. The method of claim 1 , wherein the second epoxy crosslinking agent has an epoxy equivalent weight of 150 g/eq to 400 g/eq.
5. The method of claim 1 , wherein the first epoxy crosslinking agent and the second epoxy crosslinking agent are included in an amount of 0.01 part by weight to 0.5 parts by weight, respectively, with respect to 100 parts by weight of the acrylic acid-based monomer.
6. The method of claim 1 , wherein a weight ratio of first epoxy crosslinking agent:second epoxy crosslinking agent is 1:1 to 30:1.
7. The method of claim 1 , wherein the first epoxy crosslinking agent is ethylene glycol diglycidyl ether, diethylene glycol diglycidyl ether, or a combination thereof.
8. The method of claim 1 , wherein the second epoxy crosslinking agent is one or more selected from the group consisting of poly(ethylene glycol) diglycidyl ethers having 3 to 15 ethylene glycol repeating units.
9. The method of claim 1 , wherein the surface crosslinking agent is one or more selected from the group consisting of ethylene glycol diglycidyl ether, diethylene glycol diglycidyl ether, triethyleneglycol diglycidyl ether, tetraethyleneglycol diglycidyl ether, glycerin polyglycidyl ether, and sorbitol polyglycidyl ether.
10. The method of claim 1 , wherein the preparing the base resin includes:
forming a water-containing gel polymer by polymerizing a monomer composition including the acrylic acid-based monomer having acidic groups which are at least partially neutralized, the internal crosslinking agent including the first epoxy crosslinking agent and the second epoxy crosslinking agent, the sodium polycarboxylate surfactant, and a polymerization initiator;
drying the water-containing gel polymer;
pulverizing the dried polymer; and
size-sorting the pulverized polymer.
11. A superabsorbent polymer comprising:
a base resin including a crosslinked polymer in which an acrylic acid-based monomer having acidic groups which are at least partially neutralized is crosslinked in the presence of a sodium polycarboxylate surfactant and an internal crosslinking agent including a first epoxy crosslinking agent having an epoxy equivalent weight of 100 g/eq or more to less than 130 g/eq, and a second epoxy crosslinking agent having an epoxy equivalent weight of 130 g/eq or more; and
a surface crosslinked layer which is formed on the particle surface of the base resin and is prepared by further crosslinking the crosslinked polymer via a surface crosslinking agent.
12. The superabsorbent polymer of claim 11 , wherein the superabsorbent polymer has a centrifuge retention capacity (CRC) of 29.5 g/g or more.
13. The superabsorbent polymer of claim 11 , wherein the superabsorbent polymer has 1-min tap water absorbency of 113 g/g or more, the 1-min tap water absorbency defined by the weight of tap water absorbed by the superabsorbent polymer, when 1 g of the superabsorbent polymer is put in 1000 mL of tap water and left for 1 minute.
14. The superabsorbent polymer of claim 11 , wherein the superabsorbent polymer has a long-term brine rewetting under pressure of 1.4 g or less, the long-term brine rewetting defined by the weight of brine that soaks out from the superabsorbent polymer to a filter paper, when 4 g of the superabsorbent polymer is immersed in 100 g of brine and allowed to swell for 2 hours, and then the swollen superabsorbent polymer is left on the filter paper under a pressure of 0.75 psi for 5 minutes.
15. The method of claim 11 , wherein the second epoxy crosslinking agent has the epoxy equivalent weight of 130 g/eq or more to 400 g/eq or less.
16. The superabsorbent polymer of claim 12 , wherein the CRC of the superabsorbent polymer is 29.5 g/g or more to 40 g/g or less.
17. The superabsorbent polymer of claim 13 , wherein the superabsorbent polymer has a long-term brine rewetting under pressure of 1.4 g or less, the long-term brine rewetting defined by the weight of brine that soaks out from the superabsorbent polymer to a filter paper, when 4 g of the superabsorbent polymer is immersed in 100 g of brine and allowed to swell for 2 hours, and then the swollen superabsorbent polymer is left on the filter paper under a pressure of 0.75 psi for 5 minutes.