NI-BASED CORROSION RESISTANT ALLOY POWDER FOR ADDITIVE MANUFACTURING AND MANUFACTURING METHOD OF ADDITIVE MANUFACTURING PRODUCT USING SAID POWDER
The invention addresses the problem of providing an Ni-based corrosion resistant alloy powder that is suitable for additive manufacturing, and a manufacturing method for an additive manufacturing product using the powder, the product having excellent corrosion-resistance and few defects. The invention consists of an Ni-based alloy powder having a component composition, in percentages by mass, of 14.5-23.9% Cr, 12.0-23.0% Mo, 0.01-7.00% Fe, 0.001-2.500% Co, 0.010% or less Mg, 0.040% or less N, 0.001-0.50% Mn, 0.001-0.200% Si, more than 0-0.50% Al, 0.001-0.500% Ti, 0.250% or less Cu, 0.001-0.300% V, 0.0001-0.0050% B, 0.0001-0.0200% Zr, and 0.0010-0.0300% O, the remainder being Ni, and contained as inevitable impurities, less than 0.05% C, less than 0.01% S, and less than 0.01% P. The angle of repose of the Ni-based alloy powder is 48 degrees or less.
1 . A Ni-based corrosion resistant alloy powder for additive manufacturing, composed of a powder of a Ni-based alloy having a component composition including, in mass %,
Cr: 14.5 to 23.9%,
Mo: 12.0 to 23.0%,
Fe: 0.01 to 7.00%,
Co: 0.001 to 2.500%,
Mg: 0.010% or less,
N: 0.040% or less,
Mn: 0.001 to 0.50%,
Si: 0.001 to 0.200%,
Al: more than 0 and 0.50% or less,
Ti: 0.001 to 0.500%,
Cu: 0.250% or less,
V: 0.001 to 0.300%,
B: 0.0001 to 0.0050%,
Zr: 0.0001 to 0.0200%, and
O: 0.0010 to 0.0300%,
with the remainder being Ni and unavoidable impurities,
wherein C, S and P are contained as the unavoidable impurities (C: less than 0.05%, S: less than 0.01% and P: less than 0.01%), and
wherein a repose angle of the Ni-based alloy powder is 48 degrees or less.
2 . The Ni-based corrosion resistant alloy powder for additive manufacturing according to claim 1 ,
wherein, in the Ni-based alloy powder, in a cumulative distribution curve showing the relationship between a particle size and a cumulative volume from a small particle size side obtained by a laser diffraction method,
a particle size d10 corresponding to a cumulative frequency of 10 volume % of the powder is 7 μm or more and 35 μm or less,
a particle size d50 corresponding to a cumulative frequency of 50 volume % of the powder is 10 μm or more and 60 μm or less, and
a particle size d90 corresponding to a cumulative frequency of 90 volume % of the powder is 20 μm or more and 98 μm or less.
3 . The Ni-based corrosion resistant alloy powder for additive manufacturing according to claim 2 ,
wherein, in the cumulative distribution curve, the uniformity represented by (d90-d10)/d50 is 1.5 or less.
4 . The Ni-based corrosion resistant alloy powder for additive manufacturing according to claim 1 ,
wherein the component composition of the Ni-based alloy further includes Ta: 2.5% or less.
5 . The Ni-based corrosion resistant alloy powder for additive manufacturing according to claim 1 ,
wherein the component composition of the Ni-based alloy further includes W: 5.0% or less.
6 . A method of manufacturing an additive manufacturing product, comprising
performing additive manufacturing using the Ni-based corrosion resistant alloy powder for additive manufacturing according to claim 1 as a raw material powder.
7 . The method of manufacturing an additive manufacturing product according to claim 6 ,
wherein the additive manufacturing product is a member for semiconductor manufacturing device.
8 . The method of manufacturing an additive manufacturing product according to claim 6 ,
wherein the additive manufacturing is a powder bed fusion method.