Aluminum alloy and aluminum alloy die casting material
Provided are a non-heat-treated aluminum alloy which has excellent casting properties and is high in both strength and toughness, and an aluminum alloy die casting material which is high in both strength and toughness, and which, in addition to having minimal difference in characteristics between regions thereof, is not prone to be affected by aging. An aluminum alloy comprises Si: 5.0 to 12.0% by mass, Mn: 0.3 to 1.9% by mass, Cr: 0.01 to 1.00% by mass, Ca: 0.001 to 0.050% by mass, with the balance being Al and unavoidable impurities, and the content of Mg in the unavoidable impurities being less than 0.3% by mass.
1. An aluminum alloy consisting of
Si: 7.0 to 12.0% by mass,
Mn: 0.3 to 1.9% by mass,
Cr: 0.01 to 1.00% by mass,
Ca: 0.001 to 0.050% by mass, and
optionally one or more selected from a group consisting of Ti: 0.05 to 0.20% by mass, B: 0.005 to 0.100% by mass and Zr: 0.05 to 0.20% by mass,
with the balance being Al and unavoidable impurities, and
the content of Mg in the unavoidable impurities being less than 0.3% by mass.
2. The aluminum alloy according to claim 1 , wherein a Cr content is 0.10 to 0.50% by mass.
3. The aluminum alloy according to claim 1 , wherein Fe is 0.4% by mass or less in the unavoidable impurities.
4. The aluminum alloy according to claim 3 , wherein Fe is 0.2% by mass or less.
5. An aluminum alloy die casting material comprising the aluminum alloy according to claim 1 , which has a tensile property of 0.2% proof stress of 110 MPa or more and elongation of 10% or more.
6. The aluminum alloy die casting material according to claim 5 , wherein, in a cross-sectional structure observation,
an average value of an equivalent circle diameter of an eutectic Si structure is 3 μm or less, and
a cross-sectional area ratio of a Cr-based crystallized product to the whole is 10% or less.
7. The aluminum alloy according to claim 1 , wherein the content of Mg in the unavoidable impurities is less than 0.1% by mass.
8. The aluminum alloy according to claim 1 , wherein the content of Mg in the unavoidable impurities is less than 0.08% by mass.
9. An aluminum alloy die casting material consisting of
Si: 7.0 to 12.0% by mass,
Mn: 0.3 to 1.9% by mass,
Cr: 0.01 to 1.00% by mass,
Ca: 0.001 to 0.050% by mass, and
optionally one or more selected from a group consisting of Ti: 0.05 to 0.20% by mass, B: 0.005 to 0.100% by mass and Zr: 0.05 to 0.20% by mass,
with the balance being Al and unavoidable impurities, and
the content of Mg in the unavoidable impurities being less than 0.3% by mass.
10. The aluminum alloy die casting material according to claim 9 , wherein the content of Mg in the unavoidable impurities is less than 0.1% by mass.
11. The aluminum alloy die casting material according to claim 9 , wherein the content of Mg in the unavoidable impurities is less than 0.08% by mass.