Process for the hydrophobization of porous silica
A process for the hydrophobization of a porous silica based compound involves the steps of providing a composition (I) containing a porous silica based compound, treating the composition (I) with a composition (II) containing hexamethyldisiloxane or its hydrolyzed form, and removing the treated silica based compound. The porous silica based compound obtained by the process is useful. A porous silica based compound obtained or obtainable by the process can be used for medical and pharmaceutical applications, as adsorbents, for cosmetic applications, as an additive for food, as a catalyst support, for the preparation of sensors, or for thermal insulation.
1. A process for the hydrophobization of a porous silica-based compound, the process comprising:
(i) providing a composition (I) comprising a porous silica-based compound,
(ii) treating the composition (I) in a treatment vessel with a composition (II) comprising hexamethyldisiloxane or its hydrolyzed form, to obtain a treated porous silica-based compound, and
(iii) removing the treated porous silica-based compound from the treatment vessel,
wherein the treatment according to (ii) is carried out at a temperature in the range of from 60 to 90° C. and at a pH value in the range of from 0.5 to 3,
and wherein the porous silica-based compound is a silica-based aerogel.
2. The process according to claim 1 , wherein the porous silica-based compound is selected from the group consisting of a silicate, an alumino-silicate, a calcium silicate, precipitated silica, and fumed silica.
3. The process according to claim 1 , wherein the silica-based compound is obtained from a sodium silicate precursor, a silica hydrogel, a fumed silica, or a precipitated silica.
4. The process according to claim 1 , wherein the composition (II) comprises hexamethyldisiloxane and an alcohol.
5. The process according to claim 1 , wherein the composition (II) comprises hexamethyldisiloxane, ethanol, and optionally, water.
6. The process according to claim 1 , wherein the composition (II) comprises hexamethyldisiloxane, ethanol, and optionally, dilute acid.
7. The process of claim 1 , wherein the porous silica-based compound is an aerogel, and wherein providing the composition (I) comprising the porous silica-based compound comprises providing a gel and drying the gel under supercritical conditions.
8. The process of claim 1 , wherein the porous silica-based compound is an aerogel, and wherein providing the composition (I) comprising the porous silica-based compound comprises providing a gel, acidifying the gel, and drying the gel under supercritical conditions.
9. The process of claim 1 , wherein the treated porous silica-based compound has a contact angle of from 138.8° to 149.5°.
10. The process of claim 1 , wherein, before (ii) treating the composition (I) in a treatment vessel, the porous silica-based compound is a hydrophilic compound having a contact angle of from 0° to 72°.