Fatigue resistant and fracture resistant hydrogels
View Patent ↗The present disclosure relates to triblock and pentablock copolymers and methods of making thereof. Aspects of the disclosure further relate to block copolymer hydrogels that exhibit both fatigue resistance and fracture resistance with superior rates of recovery.
1. A polymeric material comprising a blend, wherein the blend comprises at least one triblock copolymer and at least one pentablock copolymer, wherein the at least one triblock copolymer comprises a triblock copolymer according to formula (I):
A-B-C (I)
wherein,
A is a polystyrene block;
B is a polydiene block; and
C is a polyalkylene oxide block, and
wherein the at least one pentablock copolymer comprises a pentablock copolymer according to formula (II):
A-B-C-B-A (II)
wherein,
A is a polystyrene block;
B is a polydiene block; and
C is a polyalkylene oxide block.
2. The polymeric material of claim 1 , wherein the polydiene block of formula (I) or formula (II) or both comprises a polybutadiene block or a polyisoprene block.
3. The polymeric material of claim 1 , wherein the polyalkylene oxide block of formula (I) or formula (II) or both comprises a polyethylene oxide block.
4. The polymeric material of claim 1 , wherein the ratio of A to B in the polymeric material is 1:3 to 3:1.
5. The polymeric material of claim 1 , wherein a volume fraction for C in the polymeric material is at least about 0.8 to 0.9.
6. The polymeric material of claim 1 , wherein a volume fraction for A and B combined in the polymeric material is 0.15 or less.
7. The polymeric material of claim 1 , wherein the blend comprises at least one triblock copolymer and at least one pentablock copolymer in a molar ratio from between 95:5 and 1:99 triblock copolymer to pentablock copolymer.
8. A composition comprising a polymeric material of claim 1 , the composition selected from the group consisting of hydrated adhesives, coating materials, elastic separation membranes, medical devices, mechanical energy absorbers, battery cell separators, and fuel cell separators.
9. A block copolymer hydrogel, comprising:
a glass formed from a dry blend comprising at least one triblock copolymer and at least one pentablock copolymer; and
a liquid medium at a concentration between about 32:1 and about 2:1 liquid medium/dry blend by weight, wherein the at least one triblock copolymer comprises a triblock copolymer according to formula (I):
A-B-C (I)
wherein,
A is a polystyrene block;
B is a polydiene block; and
C is a polyalkylene oxide block, and wherein the at least one pentablock copolymer comprises a pentablock copolymer according to formula (II):
A-B-C-B-A (II)
wherein,
A is a polystyrene block;
B is a polydiene block; and
C is a polyalkylene oxide block.
10. The block copolymer hydrogel of claim 9 , wherein the polydiene block of formula (I), or formula (II), or both comprises a polybutadiene block or a polyisoprene block.
11. The block copolymer hydrogel of claim 10 , having a tensile modulus ranging between about 0.01 MPa and about 140 MPa.
12. The block copolymer hydrogel of claim 9 , wherein the polyalkylene oxide block of formula (I), or formula (II), or both comprises a polyethylene oxide block.
13. The block copolymer hydrogel of claim 9 , wherein the dry blend comprises at least one triblock copolymer and at least one pentablock copolymer in a molar ratio from between 95:5 and 1:99 triblock copolymer to copolymer.
14. The block copolymer hydrogel of claim 9 , wherein the at least one triblock copolymer and the at least one pentablock copolymer form a core-shell sphere morphology.
15. The block copolymer hydrogel of claim 9 , wherein the at least one triblock copolymer and the at least one pentablock copolymer form a core-shell sphere comprising:
a spherical core comprising A;
a shell comprising B; and
a matrix comprising C.
16. The block copolymer hydrogel of claim 9 , having a fatigue resistance to at least 500,000 compression cycles.
17. The block copolymer hydrogel of claim 9 , further comprising an active pharmaceutical ingredient.
18. A method for preparing a block copolymer hydrogel, comprising:
contacting at least one triblock copolymer and at least one pentablock copolymer in a molar ratio from between 95:5 and 1:99 triblock copolymer to pentablock copolymer to form a triblock-pentablock copolymer dry blend;
heating the dry blend to form a triblock-pentablock copolymer melt;
allowing the triblock-pentablock copolymer melt to attain ambient temperature to form a triblock-pentablock copolymer glass; and
contacting the triblock-pentablock copolymer glass with a liquid medium to form a block copolymer hydrogel
wherein the at least one triblock copolymer comprises a triblock copolymer according to formula (I):
A-B-C (I)
wherein,
A is a polystyrene block;
B is a polydiene block; and
C is a polyalkylene oxide block, and
wherein the at least one pentablock copolymer comprises a pentablock copolymer according to formula (II):
A-B-C-B-A (II)
wherein,
A is a polystyrene block;
B is a polydiene block; and
C is a polyalkylene oxide block.
19. The method of claim 18 , wherein the triblock-pentablock copolymer dry blend is formed by dissolving the triblock copolymer and pentablock copolymer in an organic solvent and removing the organic solvent.
20. The method of claim 18 , wherein the liquid medium concentration is between about 32:1 and about 4:1 liquid medium/ triblock-pentablock copolymer by weight.