Gas-solid reduction process for preparation of platinum-containing catalysts for fuel cells
A method for manufacturing a catalyst for a fuel cell can include provision of a platinum precursor and a carbon material. The platinum precursor and the carbon material can be mixed to form a platinum carbon mixture. The platinum carbon mixture can be heated to form a porous solid. The porous solid can be milled to form a powder. The powder can be reacted with a reducing agent to form the catalyst.
1. A method for manufacturing a catalyst for a fuel cell, comprising:
mixing a platinum precursor and a carbon material to form a mixture;
heating the mixture to form a porous solid;
milling the porous solid to form a powder; and
reacting the powder with a reducing agent, thereby forming the catalyst, the catalyst including platinum particles disposed on carbon particles.
2. The method of claim 1 , wherein the platinum precursor is hexachloroplatinic acid hexahydrate.
3. The method of claim 1 , wherein the carbon material is carbon black.
4. The method of claim 1 , wherein the mixing step is performed at a temperature from about 60° C. to about 80° C.
5. The method of claim 1 , wherein the mixing step is performed in absence of a solvent.
6. The method of claim 1 , wherein the heating step includes heating the mixture of the platinum precursor and the carbon material to about 110° C.
7. The method of claim 1 , wherein the reducing agent includes hydrogen gas.
8. The method of claim 7 , wherein the reacting step includes placing the powder into a reactor having an inert gas flow.
9. The method of claim 8 , wherein the reactor is heated to a temperature from about 140° C. to about 180° C.
10. The method of claim 8 , wherein the hydrogen gas is added to the inert gas flow to form the catalyst and hydrochloric gas.
11. The method of claim 10 , wherein the reacting step includes increasing a pressure of hydrogen within the reactor over a predetermined period of time.
12. The method of claim 11 , wherein increasing the pressure of hydrogen includes increasing the pressure of hydrogen from about 1 kPa partial pressure to about 150 kPa partial pressure.
13. The method of claim 10 , wherein the inert gas flow includes nitrogen.
14. The method of claim 1 , further comprising repeating the mixing step, the heating step, and the reacting step to provide the catalyst with additional platinum particles disposed on the carbon particles.
15. The method of claim 1 , wherein the catalyst has a platinum loading of about 50 wt. %.
16. The method of claim 1 , wherein the mixing step includes mixing the platinum precursor and the carbon material with an ionomer.
17. The method of claim 1 , wherein the platinum precursor is hexachloroplatinic acid hexahydrate, the carbon material is carbon black, the mixing step is performed at a temperature from about 60° C. to about 80° C. in absence of a solvent, the heating step includes heating the mixture of the platinum precursor and the carbon material to about 110° C., and the reducing agent in the reacting step includes hydrogen gas.
18. The method of claim 17 , wherein the reacting step includes placing the powder into a reactor having an inert gas flow, the reactor is heated to a temperature from about 140° C. to about 180° C., and the hydrogen gas is added to the inert gas flow to form the catalyst and hydrochloric gas.
19. A catalyst manufactured according to the method of claim 1 .
20. A fuel cell comprising a membrane electrode assembly having a catalyst manufactured according to claim 1 .