Cementitious compositions comprising recycled superabsorbent polymer
A cementitious composition including recycled superabsorbent polymer (RSAP) and a cementitious material. The RSAP has a purity level of at least 85 percent by weight of the RSAP. Also provided is a cementitious composition where the RSAP has substantially low levels of one or more residual drug entities. Also provided is a method for the construction of a self-sealing cement sheath, the method comprising: supplying a self-sealing slurry of a cementitious composition including cementitious material, an aqueous fluid, and RSAP into an underground geological formation, and allowing the self-sealing slurry of the cementitious composition to cure, thereby forming the self-sealing cement sheath. The RSAP is capable of swelling in the presence of fluid to seal any cracks formed in the self-sealing slurry during curing.
1. A cementitious composition comprising:
recycled superabsorbent polymer (RSAP), wherein the RSAP comprises residual material, the residual material comprising fluff pulp, plastic, or combinations thereof; and
a cementitious material;
wherein the RSAP has a purity level of 85% to 99%, wherein the purity level is measured according to the Method to Evaluate the Purity Level of RSAP.
2. The cementitious composition of claim 1 , wherein the RSAP is present in a range of from about 0.025 percent to about 0.5 percent by weight of the cementitious material.
3. The cementitious composition of claim 2 , wherein the cementitious composition comprises a ratio of water to the cementitious material of between about 0.2 to about 0.5 by weight of the cementitious composition.
4. The cementitious composition of claim 1 , wherein the RSAP is present in a range of from about 0.13 kilograms per cubic meter (3.5 ounces per cubic yard) to about 1.48 kilograms per cubic meter (40 ounces per cubic yard) of the cementitious composition.
5. The cementitious composition of claim 1 , wherein the RSAP comprises at least about 25 percent acrylic acid monomer units by weight of the RSAP.
6. The cementitious composition of claim 1 , wherein the RSAP comprises between about 25 percent to about 100 percent acrylic acid monomer units by weight of the RSAP.
7. The cementitious composition of claim 1 , wherein the RSAP comprises between about 25 percent to about 100 percent neutralized acrylic acid monomer units by weight of the RSAP.
8. The cementitious composition of claim 1 , wherein the RSAP comprises one or more crosslinking monomers.
9. The cementitious composition of claim 1 , wherein the RSAP comprises particles with surface crosslinking.
10. The cementitious composition of claim 1 , wherein the RSAP comprises one or more residual drug entities.
11. The cementitious composition of claim 10 , wherein the RSAP is recovered, extracted, or collected from soiled absorbent articles.
12. A cementitious composition comprising:
recycled superabsorbent polymer (RSAP), wherein the RSAP comprises residual material, the residual material comprising fluff pulp, plastic, or combinations thereof; and
a cementitious material;
wherein the RSAP comprises one or more residual drug entities.
13. The cementitious composition of claim 12 , wherein the RSAP is present in a range of between about 0.025 percent to about 0.5 percent by weight of the cementitious composition.
14. The cementitious composition of claim 12 , wherein the RSAP is present in the range of between about 0.13 kilograms per cubic meter (3.5 ounces per cubic yard) to about 1.48 kilograms per cubic meter (40 ounces per cubic yard) of the cementitious composition.
15. The cementitious composition of claim 12 , wherein the RSAP comprises between about 25 percent to about 100 percent acrylic acid monomer units by weight of the RSAP.
16. The cementitious composition of claim 15 , wherein the RSAP comprises one or more crosslinking monomers.
17. The cementitious composition claim 12 , wherein the RSAP is recovered, extracted, or collected from soiled absorbent articles.
18. A cementitious composition comprising:
recycled superabsorbent polymer (RSAP), wherein the RSAP comprises residual material, the residual material comprising fluff pulp, plastic, or combinations thereof; and
a cementitious material;
wherein the RSAP comprises one or more residual drug entities, wherein the one or more residual drug entities have a concentration of less than 1,000 micrograms per kilogram of RSAP.
19. The cementitious composition of claim 18 , wherein the RSAP comprises particles exhibiting a median particle size of about 30 μm to about 1000 μm, as measured according to the Median Particle Size Test Method as mentioned in the description and wherein the RSAP comprises particles exhibiting a Centrifuge Retention Capacity (CRC) of about 10 g/g to about 50 g/g, as measured according to the Centrifuge Retention Capacity Test Method, being measured according to EDANA method WSP 241.2-05.
20. The cementitious composition of claim 18 , wherein the RSAP comprises particles with surface crosslinking, and wherein the RSAP is recovered, extracted, or collected from soiled absorbent articles.