High solids, sprayable setting type joint compound
A high solids, sprayable, fast drying, ready-mixed setting-type joint compound comprising a blend of a joint compound mixture comprising: joint compound mixture ingredients comprising: calcium sulfate hemihydrate (e.g. US Gypsum's HYDROCAL C-Base), a chelating agent, and water; and an activator mixture, wherein the activator mixture comprises: activator mixture ingredients comprising: inert filler, set accelerator, and water, wherein a weight ratio of joint compound mixture:activator mixture is 1:1 to 100:1, wherein the activator mixture viscosity is the same as the joint compound mixture viscosity plus or minus 50 percent, and wherein the joint compound has about 55 to about 80 wt. % solids and a viscosity of 2,500-28,000 cps.
1 . A sprayable ready-mixed setting-type joint compound comprising a blend of
(A) a joint compound mixture comprising:
(a) joint compound mixture ingredients comprising in weight percent on a dry basis:
about 75 to about 99 wt. % calcium sulfate hemihydrate in an alpha morphological form having blocky cubic crystal microstructure with a D50 average particle size of about 15 to 50 microns, and
said calcium sulfate hemihydrate having a consistency of 31-36 cc water per 100 g said calcium sulfate hemihydrate,
about 0-4 wt. % thickening agent,
about 0-2 wt. % set retarder,
about 0.05-5 wt. % chelating agent, wherein the chelating agent is selected from tetra sodium pyrophosphate or tetra potassium pyrophosphate,
about 0-2 wt. % preservative,
optionally about 0-5 wt. % second chelating agent,
optionally about 0-80 wt. % filler, and
optionally about 0-5 wt. % binder, and
(b) joint compound mixture water, wherein weight ratio of the joint compound mixture ingredients to the joint compound mixture water is within a range of 3:1 to 1.5, and
(B) an activator mixture, wherein the activator mixture comprises:
(a) activator mixture ingredients comprising in weight percent on a dry basis:
inert filler, wherein the inert filler comprises calcium carbonate at about 50 to 95 wt. % of the activator mixture ingredients,
set accelerator at 5-50 wt. % of the activator mixture ingredients,
thickening agent at about 0-4 wt. % of the activator mixture ingredients,
preservative at about 0-2 wt. % of the activator mixture ingredients, and
(b) activator mixture water, wherein weight ratio of the activator mixture ingredients to the activator mixture water is within a range of 3:1 to 1.5:1,
wherein the composition has an absence of Portland cement,
wherein a weight ratio of joint compound mixture:activator mixture is 1:1 to 10:1,
wherein the activator mixture viscosity is the same as the joint compound mixture viscosity plus or minus 20%,
wherein the joint compound mixture viscosity is 2,500-5600 cps,
wherein the activator mixture viscosity is 2,500-5600 cps,
wherein the joint compound viscosity is between 2,500-5600 cps, and
wherein the joint compound mixture has about 60 to about 88 wt. % solids,
wherein the activator mixture has about 60 to about 88 wt. % solids, and
wherein the sprayable ready-mixed setting-type joint compound has a spray viscosity which is substantially the same as the joint compound mixture viscosity.
2 . The joint compound of claim 1 , wherein the set accelerator comprises zinc sulfate and the accelerator is 26.8-50 wt. % of the activator mixture ingredients.
3 . The joint compound of claim 1 , wherein the joint compound has about 69 to about 78 wt. % solids, having an absence of hydraulic cements.
4 . The joint compound of claim 1 , wherein the joint compound has about 72 to about 78 wt. % solids.
5 . The joint compound of claim 1 ,
wherein the joint compound mixture has a viscosity of 2,500-4005 cps.
6 . The joint compound of claim 1 , wherein the joint compound has a Vicat set-time of 23-39 minutes.
7 . A method of dispersing the sprayable ready-mixed setting-type joint compound of claim 1 comprising
mixing a joint compound mixture and an activator mixture to obtain the sprayable ready-mixed setting-type joint compound and
spraying the sprayable ready-mixed setting-type joint compound through a nozzle on a spray gun,
(A) wherein the joint compound mixture comprises
(a) joint compound mixture ingredients comprising in weight percent on a dry basis:
about 75 to about 99 wt. % calcium sulfate hemihydrate in an alpha morphological form having blocky cubic crystal microstructure with a D50 average particle size of about 15 to 50 microns, and
said calcium sulfate hemihydrate having a consistency of 31-36 cc water per 100 g said calcium sulfate hemihydrate,
about 0-4 wt. % thickening agent,
about 0-2 wt. % set retarder,
about 0.05-5 wt. % chelating agent, wherein the chelating agent is selected from tetra sodium pyrophosphate or tetra potassium pyrophosphate,
about 0-2 wt. % preservative,
optionally about 0-5 wt. % second chelating agent,
optionally about 0-80 wt. % filler, and
optionally about 0-5 wt. % binder, and
(b) joint compound mixture water, wherein weight ratio of the joint compound mixture ingredients to the joint compound mixture water is within a range of 3:1 to 1.5, and
(B) wherein the activator mixture comprises:
(a) activator mixture ingredients comprising in weight percent on a dry basis:
inert filler wherein the inert filler comprises calcium carbonate at about 50 to 95 wt. % of the activator mixture ingredients,
set accelerator at about 50 wt. % of the activator mixture ingredients,
thickening agent at about 0-4 wt. % of the activator mixture ingredients, preservative at about 0-2 wt. % of the activator mixture ingredients, and
(b) activator mixture water, wherein weight ratio of the activator mixture ingredients to the activator mixture water is within a range of 3:1 to 1.5:1,
wherein the composition has an absence of Portland cement,
wherein a weight ratio of joint compound mixture:activator mixture is 1:1 to 10:1
wherein the activator mixture viscosity is the same as the joint compound mixture viscosity plus or minus 20%,
wherein the joint compound mixture viscosity is 2,500-5600 cps,
wherein the activator mixture viscosity is 2,500-5600 cps,
wherein the joint compound viscosity is 2,500-5600 cps, and
wherein the joint compound has about 60 to about 88 wt. % solids,
wherein the joint compound mixture has about 60 to about 88 wt. % solids,
wherein the activator mixture has about 60 to about 88 wt. % solids, and
wherein the sprayable ready-mixed setting-type joint compound has a spray viscosity which is substantially the same as the joint compound mixture viscosity.
8 . The method of claim 7 , wherein the joint compound mixture has a viscosity of about 4,000-5,600 cps, a ratio of joint compound mixture:activator mixture is 1:1 to 10:1 and the activator mixture has a viscosity of about 4,000-5,600 cps.
9 . The joint compound of claim 1 , further comprising a custom colorant.
10 . The joint compound of claim 1 , wherein the joint compound mixture further comprises a colorant, wherein the colorant is a different color from the color of the activator mixture.
11 . The joint compound of claim 1 , wherein the activator mixture further comprises a colorant, wherein the colorant is a different color from the color of the joint compound mixture.
12 . The joint compound of claim 1 , wherein the calcium sulfate hemihydrate D50 average particle size is 15 to 20 microns.
13 . The joint compound of claim 1 , wherein the calcium sulfate hemihydrate D50 average particle size is 20 to 50 microns.
14 . The joint compound of claim 1 , wherein the joint compound mixture viscosity is 2,500-4000 cps,
wherein the activator mixture viscosity is 2,500-4000 cps, and
wherein the joint compound viscosity is between 2,500-4000 cps.