Heat-treated PVC-plastic panel
A method of treating PVC plates as well as plates and panels manufactured by this method. The plates and panels, in particular wall, ceiling or floor panels, comprise a heat-treated carrier plate based on polyvinyl chloride with a density of, for example, 900 to 2,500 kg/m 3 and a film applied thereon. The film is a thin PVC-film and comprises a decorative pattern directly printed thereon.
1. A panel, in particular a wall, ceiling or floor panel, comprising
a polyvinyl chloride plate and
a film attached to the polyvinyl chloride plate,
wherein the film is a PVC film having a thickness of 0.04 to 0.2 mm and having a decorative pattern directly printed thereon,
wherein a cured polymer layer is provided over the PVC film, and
wherein the printing ink used for printing the decorative pattern is solvent based and a UV printing ink, and contains a polymerizable acrylate and/or N-vinylcaprolactam.
2. The panel according to claim 1 , wherein the polymer layer has a hardness gradient, so that the hardness of the polymer layer decreases essentially continuously with increasing depth as seen from the surface of the polymer layer.
3. The panel according to claim 1 , wherein the printing ink for printing the decorative pattern contains a polymerizable acrylate and N-vinylcaprolactam in a weight proportion in the ink of 2 to 50.
4. The panel according to claim 1 , wherein the printing ink and the polymer layer were cured together.
5. The panel according to claim 1 , wherein the decorative pattern was applied by means of digital printing.
6. The panel according to claim 1 , wherein the PVC film has a thickness from 0.05 to 0.15 mm.
7. The panel according to claim 1 , wherein the PVC plate has a thickness between 3 and 20 mm.
8. The panel according to claim 1 , wherein a layer comprising a UV primer is provided on the PVC film.
9. The panel according to claim 8 , wherein the layer comprising a UV primer has a surface mass of 1 to 15 g/m 2 .
10. The panel according to claim 1 , wherein the PVC plate is an extruded PVC plate.
11. The panel according claim 1 , wherein the PVC film is glued or thermally welded to the plate.
12. The panel according to claim 1 , wherein abrasion-resistant particles are provided in the polymer layer.
13. The panel according to claim 1 , wherein the polymer layer is based on one or more of the following acrylates: 1 , 6 -hexane dioldiacrylate, polyester acrylate, polyurethane acrylic acid ester and dipropylene glycol diacrylate.
14. The panel according to claim 1 , wherein, besides the decorative pattern on the PVC film, no further decor layers in particular no decor papers or decor films are provided.
15. The panel according to claim 1 , wherein the directly printed decorative pattern imitates a wood, stone or the surface.
16. The panel according to claim 1 , wherein the polyvinyl chloride plate contains no plasticizers.
17. The panel according to claim 1 , wherein the polyvinyl chloride plate consists of hard PVC (PVC-U).
18. The panel according to claim 4 , wherein the printing ink and the polymer layer were cured together by radiation.
19. The panel according to claim 12 , wherein the abrasion-resistant particles have an average diameter of 10 to 150 μm.
20. The panel according to claim 12 , wherein the abrasion-resistant particles consist of corundum.