Glass compositions, glass articles, and methods of making the same
Disclosed herein are glass compositions, articles made from the disclosed glass compositions, and methods of making the same. More specifically, disclosed herein is a glass composition comprising from about 10 to about 14 mol % of K 2 O; from 0 to about 4 mol % of CaO; from about 14 to about 18 mol % of Al 2 O 3 ; and from about 66 to about 74 mol % SiO 2 .
1 . A glass fiber composition comprising:
a) from equal to or greater than 11.2 to 14 mol % of K 2 O;
b) from 0 to 4 mol % of CaO;
c) from 14 to 18 mol % of Al 2 O 3 ; and
d) from 66 to 74 mol % SiO 2 ;
wherein the glass composition exhibits a coefficient of thermal expansion from 5.5 ppm/° C. to 9 ppm/° C. averaged over a temperature range from 20° C. to 300° C., and a glass transition temperature T g from 720° C. to 1,000° C.
2 . A glass fiber article comprising the glass fiber composition of claim 1 .
3 . An article comprising:
a) a core layer having a predetermined thickness; and
b) a cladding layer having a predetermined thickness and wherein the cladding layer surrounds the core layer and wherein the cladding layer comprises a glass composition comprising:
i) from equal to or greater than 11.2 to 14 mol % of K 2 O;
ii) from 0 to 4 mol % of CaO;
iii) from 14 to 18 mol % of Al 2 O 3 ; and
iv) from 66 to 74 mol % SiO 2 ;
wherein the glass composition exhibits a coefficient of thermal expansion from 5.5 ppm/° C. to 9 ppm/° C. averaged over a temperature range from 20° C. to 300° C. and a glass transition temperature T g from 720° C. to 1,000° C.; and
wherein the cladding layer exhibits a coefficient of thermal expansion that is substantially similar to a coefficient of thermal expansion of the core layer.
4 . The article of claim 3 , wherein the core layer comprises a transition metal doped chalcogenide comprising ZnSe, ZnS, ZnTe, CdSe, CdS, CdTe, HgSe, HgS, or HgTe, and wherein the core layer exhibits an optical loss of less than about 1 dB/cm.
5 . The article of claim of claim 3 , wherein the glass composition further comprises from greater than 0 mol % to 1 mol % of a fining agent.
6 . The article of claim 5 , wherein the fining agent comprises a sulfate salt, chloride salt, iodide salt, bromide salt, a metallic oxide, or a combination thereof.
7 . The article of claim 6 , wherein the metallic oxide comprises CeO 2 , SnO 2 , Fe 2 O 3 , As 2 O 3 , Sb 2 O 3 , MnO 2 , or a combination thereof.
8 . The article of claim 3 , wherein the glass composition further comprises one or more of Na 2 O, B 2 O 3 , SrO, BaO, MgO, or ZnO present in an amount of less than 10 mol %.
9 . The article of claim 3 , wherein the cladding layer is substantially defect-free.
10 . The article of claim 3 , wherein the cladding layer exhibits a substantially uniform thickness.
11 . The article of claim 3 , wherein the cladding layer is substantially color free.
12 . The article of claim 3 , wherein the core layer is substantially defect-free.
13 . The article of claim 3 , wherein the core layer is a high-pressure vapor deposited core layer.
14 . A laser comprising the article of claim 3 .
15 . An article comprising:
a) a core layer having a predetermined thickness; and
b) a cladding layer having a predetermined thickness and wherein the cladding layer surrounds the core layer and wherein the cladding layer comprises a glass composition comprising:
i) from equal to or greater than 11.2 to 14 mol % of K 2 O;
ii) from 0 to 4 mol % of CaO;
iii) from 14 to 18 mol % of Al 2 O 3 ; and
iv) from 66 to 74 mol % SiO 2 ;
v) greater than 0 mol % to 1 mol % of a fining agent, wherein the fining agent comprises a sulfate salt, chloride salt, iodide salt, bromide salt, a metallic oxide, or a combination thereof, wherein the metallic oxide comprises CeO 2 , SnO 2 , Fe 2 O 3 , As 2 O 3 , Sb 2 O 3 , MnO 2 , or a combination thereof; and
wherein the glass composition exhibits a coefficient of thermal expansion from 5.5 ppm/° C. to 9 ppm/° C. averaged over a temperature range from 20° C. to 300° C. and a glass transition temperature T g from 720° C. to 1,000° C.
16 . The article of claim 15 , wherein the article is a glass fiber.