Lithium oxyhalide battery separator material
Methods for producing ceramic films Yttria Stabilized Zirconia (3YSZ) and aluminum titanate (Al 2 TiO 5 ), and the physical properties of these films are described. The films produced have thicknesses and integrity suitable for handling and corrosion resistance to electrolytes, porosity, ion permeability and electrical resistivity suitable for use as separators between positive and negative layers for forming electrical batteries, particularly lithium batteries.
1. A method of forming a flexible ceramic battery separator comprising:
a. Combining ceramic particles with a fugitive organic binder to form a solution and casting the solution to form a film of ceramic particles,
b. drying the film in ambient air with a relative humidity (RH) ranging from about 30% to about 60% to form a dry tape,
c. pressing the dry tape with a pressure of about 0-3 Klb at about 25-52° C.,
d. placing the pressed dry tape on an inert substrate and heating the dry tape in air at a temperature of at least about 1500° C. for at least 8 hours to form a fired tape, and
e. cooling the fired tape to room temperature over a period of 2-12 hours.
2. The method of claim 1 further including heating the dry tape while applying pressure to said dry tape while heating.
3. The method of claim 1 wherein the ceramic particles comprise Al 2 TiO 5 or yttria stabilized zirconia (YSZ).
4. The method of claim 3 wherein Al 2 TiO 5 ceramic particles have a size of about 15-30 μm.
5. The method of claim 3 wherein the Al 2 TiO 5 ceramic particles have a of about 5-20 μm.
6. The method of claim 3 wherein the YSZ comprises agglomerates of 1-10 μm of YSZ particles which are about 40 nm. in size.