Polyester polymer compositions
A fiber reinforced polyester polymer composition is disclosed that contains at least one tribological modifier. The tribological modifier may comprise an ultra-high molecular weight silicone alone or in combination with polyytetrafluoroethylene particles. The composition not only has excellent tensile properties but also can produce a low friction surface.
1. A polymer composition that can be compounded or extruded into a polymer article comprising:
a polyester polymer, the polyester polymer comprising a polybutylene terephthalate polymer alone or in combination with a polyethylene terephthalate polymer, the polybutylene terephthalate polymer being present in the polymer composition in an amount greater than 60% by weight;
optionally reinforcing fibers present in the polymer composition in an amount from about 5% to about 35% by weight; and
a masterbatch comprising a first tribological modifier dispersed in a carrier polymer, the first tribological modifier comprising an ultra-high molecular weight silicone having a kinematic viscosity of greater than 100,000 mm 2 s −1 , the ultra-high molecular weight silicone being present in the polymer composition in an amount from about 0.5% by weight to about 6% by weight, the ultra-high molecular weight silicone being present in the masterbatch in an amount from about 35% by weight to about 60% by weight, and wherein the carrier polymer comprises a polyester elastomer.
2. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 1 , wherein the ultra-high molecular weight silicone is a polydimethylsiloxane.
3. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 1 , wherein the composition contains a second tribological modifier.
4. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 3 , wherein the polybutylene terephthalate polymer is present in the composition in an amount from about 70% to about 90% by weight, the reinforcing fibers comprising glass fibers and being present in the polymer composition in an amount from about 5% to about 30% by weight, and the ultra-high molecular weight silicone dispersed within the carrier polymer being present in the composition in an amount from about 0.5% to about 5% by weight.
5. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 1 , wherein the composition is isocyanate free.
6. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 1 , wherein the polymer composition exhibits a dynamic coefficient of friction according to VDA 230-206 of less than 0.08 when tested against polycarbonate containing 15% by weight polytetrafluoroethylene and 20% by weight glass fiber, when tested against polybutylene terephthalate containing 15% by weight polytetrafluoroethylene and 20% by weight glass fiber, or when tested against itself at a speed of 8 mm/s, at a load of 30 N and after 1,000 cycles.
7. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 1 , wherein the polymer composition exhibits a dynamic coefficient of friction according to VDA 230-206 of less than 0.07 when tested against polycarbonate containing 15% by weight polytetrafluoroethylene and 20% by weight glass fiber, when tested against polybutylene terephthalate containing 15% by weight polytetrafluoroethylene and 20% by weight glass fiber, or when tested against itself at a speed of 8 mm/s, at a load of 30 N and after 1,000 cycles.
8. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 1 , wherein the polymer composition exhibits a dynamic coefficient of friction according to VDA 230-206 of less than 0.05 when tested against polycarbonate containing 15% by weight polytetrafluoroethylene and 20% by weight glass fiber, when tested against polybutylene terephthalate containing 15% by weight polytetrafluoroethylene and 20% by weight glass fiber, or when tested against itself at a speed of 8 mm/s, at a load of 30 N and after 1,000 cycles.
9. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 1 , wherein the reinforcing fibers comprise glass fibers, the glass fibers being present in the polymer composition in an amount from about 10% to about 30% by weight.
10. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 1 , wherein the composition exhibits a Charpy notched impact strength of greater than 9 kJ/m 2 at 23° C.
11. An apparatus comprising:
a first sliding member in operative association with a second sliding member, the first sliding member and the second sliding member being configured to remain in contact and move relative to each other,
wherein the first sliding member and the second sliding member are both made from the polymer composition as defined in claim 1 .
12. The apparatus as defined in claim 11 , wherein the apparatus is a medical inhaler or injector.
13. A polymer composition that can be compounded or extruded into a polymer article comprising:
a polyester polymer, the polyester polymer comprising a polybutylene terephthalate, the polybutylene terephthalate polymer being present in the polymer composition in an amount greater than 60% by weight;
a masterbatch comprising a tribological modifier comprising an ultra-high molecular weight silicone having a kinematic viscosity of greater than 100,000 mm 2 s −1 dispersed in a carrier polymer, the ultra-high molecular weight silicone being present in an amount of from about 0.1% to about 6% by weight based upon the weight of the polymer composition, the ultra-high molecular weight silicone being present in an amount of from about 10% to about 60% by weight based upon the weight of the combination of the ultra-high molecular weight silicone and the carrier polymer, and wherein the carrier polymer comprises a polyester elastomer; and
a second tribological modifier comprising a fluoropolymer powder having an average particle size of less than 15 microns and greater than 0.5 microns, the fluoropolymer powder having a melt flow rate of less than 3 g/10 min.
14. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 13 , wherein the second tribological modifier comprises a polytetrafluorethylene.
15. The polymer composition that can be compounded or extruded into a polymer article as defined in claim 13 , wherein the ultra-high molecular weight silicone is a polydimethylsiloxane.