Silicon-lithium-lead system, conductive paste and preparation method thereof
View Patent ↗The present disclosure discloses a silicon-lithium-lead system, a conductive paste and a preparation method thereof, and belongs to the field of solar cells. A silicon-lead-lithium oxide frit includes the following composition: Si a —Pb b —Li c —(B x —Al y —Bi z )-M e -O f , where, 0<a<0.6, 0<b<0.8, 0<c<0.6, x+y+z=d, the x and the y are not zero at the same time, and the z is greater than zero. In the present disclosure, by adding B 2 O 3 and Bi 2 O 3 , Al 2 O 3 and Bi 2 O 3 , or B 2 O 3 , Al 2 O 3 and Bi 2 O 3 at the same time, the prepared frit has greater water resistance, and therefore, a solar cell prepared by using the conductive paste containing glass has good water resistance. In addition, the photoelectric conversion efficiency of the solar cell prepared by using the conductive paste prepared in the present disclosure can also be maintained, or even be slightly improved.
1. A silicon-lead-lithium oxide frit, comprising the following component:
Si a —Pb b —Li c —(B x —Al y —Bi z )-M e -O f (I)
wherein, 0.05≤a≤0.15, 0.19≤b≤0.25, 0.21≤c≤0.25, 0≤x≤0.02, 0≤y≤0.02, 0.04≤z≤0.08, x+y+z=d, at least one of x, y and z is greater than zero, 0<d<0.12, c:d=(5:95)-(95:5), M is one or a mixture of more of Na, K, Mg, Ca, Sr, Ti, Zr, V, Cr, Mo, W, Mn, Cu, Ag, Zn, Cd, Ga, TI, Ge, P and Te, and a+b+c+d+e=1; wherein f is an amount O that balances the valence of the silicon-lead-lithium oxide frit;
wherein x and y are not zero at the same time.
2. The silicon-lead-lithium oxide frit according to claim 1 , wherein all the x, the y and the z are greater than zero.
3. The silicon-lead-lithium oxide frit according to claim 1 , wherein c:d=(30:70)-(90:10).
4. The silicon-lead-lithium oxide frit according to claim 1 , wherein c:d=(40:60)-(90:10).
5. A conductive paste of a silicon-lead-lithium oxide frit, comprising, by weight percentage, 84%-94% of a conductive metal, 0.1-9% of the silicon-lead-lithium oxide frit according to claim 1 and 5%-15% of an organic material.
6. The conductive paste of a silicon-lead-lithium oxide frit according to claim 5 , wherein the conductive metal is one or more of silver, gold, platinum, rhodium, copper, nickel and aluminum; and the organic material comprises an organic binder, an organic solvent, a thixotropic agent, a surfactant or any combination thereof.
7. The conductive paste of a silicon-lead-lithium oxide frit according to claim 6 , wherein the conductive metal is silver.
8. A method of preparing the conductive paste of a silicon-lead-lithium oxide frit according to claim 5 , the method comprising: weighing the conductive metal, the silicon-lead-lithium system frit and the organic vehicle according to a proportion of a formula, uniformly mixing and stirring the raw materials of the conductive paste by using a mixer, repeatedly milling the conductive paste by using a three-roll mill, and further mixing the conductive paste uniformly by using a shearing force between rollers of the three-roll mill.
9. A solar cell device, wherein the solar cell device comprises the silicon-lead-lithium oxide frit according to claim 1 .
10. A solar cell device, wherein the solar cell device comprises the conductive paste of a silicon-lead-lithium oxide frit according to claim 5 .