Diphosphorus pentasulfide composition for sulfide-based inorganic solid electrolyte material
Provided is a diphosphorus pentasulfide composition for a sulfide-based inorganic solid electrolyte material, in which a molar ratio (S/P) of a content of sulfur (S) to a content of phosphorus (P) is 2.40 or higher and 2.49 or lower. In the diphosphorus pentasulfide composition for a sulfide-based inorganic solid electrolyte material, in a DSC curve of the diphosphorus pentasulfide composition obtained by measurement using a differential scanning calorimeter under conditions of a start temperature of 25° C., a measured temperature range of 30° C. to 350° C., a temperature increase rate of 5° C./min, and an argon atmosphere with a flow rate of 100 ml per minute, an endothermic peak is shown in a temperature range of 280° C. or higher and 300° C. or lower, and a half-width of the endothermic peak is 4.1° C. or higher.
1. A diphosphorus pentasulfide composition for a sulfide-based inorganic solid electrolyte material,
wherein a molar ratio (S/P) of a content of sulfur (S) to a content of phosphorus (P) is 2.40 or higher and 2.49 or lower, and
wherein a melting point of the diphosphorus pentasulfide composition measured using a differential scanning calorimeter is 291° C. or higher.
2. The diphosphorus pentasulfide composition according to claim 1 ,
wherein in a DSC curve of the diphosphorus pentasulfide composition obtained by measurement using a differential scanning calorimeter under conditions of a start temperature of 25° C., a measured temperature range of 30° C. to 350° C., a temperature increase rate of 5° C./min, and an argon atmosphere with a flow rate of 100 ml per minute, an endothermic peak is shown in a temperature range of 280° C. or higher and 300° C. or lower, and a half-width of the endothermic peak is 4.1° C. or higher.
3. A diphosphorus pentasulfide composition for a sulfide-based inorganic solid electrolyte material,
wherein in a DSC curve of the diphosphorus pentasulfide composition obtained by measurement using a differential scanning calorimeter under conditions of a start temperature of 25° C., a measured temperature range of 30° C. to 350° C., a temperature increase rate of 5° C./min, and an argon atmosphere with a flow rate of 100 ml per minute, an endothermic peak is shown in a temperature range of 280° C. or higher and 300° C. or lower, and a half-width of the endothermic peak is 4.1° C. or higher, and
wherein a heat of fusion of the endothermic peak is 70 J/g or more.
4. The diphosphorus pentasulfide composition according to claim 3 ,
wherein a melting point of the diphosphorus pentasulfide composition measured using a differential scanning calorimeter is 285° C. or higher.
5. The diphosphorus pentasulfide composition according to claim 3 ,
wherein a heat of fusion of the endothermic peak is 150 J/g or less.
6. The diphosphorus pentasulfide composition according to claim 1 or 3 ,
wherein a content of diphosphorus pentasulfide in the diphosphorus pentasulfide composition is 95 mass % or higher.
7. The diphosphorus pentasulfide composition according to claim 1 or 3 ,
wherein the diphosphorus pentasulfide composition is powdery.
8. A raw material composition of a sulfide-based inorganic solid electrolyte material, the raw material composition comprising:
the diphosphorus pentasulfide composition according to claim 1 or 3 ; and
lithium sulfide.
9. A method of manufacturing a sulfide-based inorganic solid electrolyte material, the method comprising a step of mechanically processing the raw material composition of the sulfide-based inorganic solid electrolyte material according to claim 8 .
10. A sulfide-based inorganic solid electrolyte material that is obtained by using the diphosphorus pentasulfide composition according to claim 1 or 3 as a raw material.
11. A solid electrolyte comprising the sulfide-based inorganic solid electrolyte material according to claim 10 .
12. A solid electrolyte membrane comprising the solid electrolyte according to claim 11 as a main component.
13. A lithium ion battery comprising:
a positive electrode including a positive electrode active material layer;
an electrolyte layer; and
a negative electrode including a negative electrode active material layer,
wherein at least one of the positive electrode active material layer, the electrolyte layer, and the negative electrode active material layer includes the sulfide-based inorganic solid electrolyte material according to claim 10 .
14. The diphosphorus pentasulfide composition according to claim 1 ,
wherein a melting point of the diphosphorus pentasulfide composition measured using a differential scanning calorimeter is 300° C. or lower.