Powder for film formation or sintering
A powder for coating or sintering has a peak assigned to cubic Y 3 Al 5 O 12 and a peak assigned to orthorhombic YAlO 3 exhibited in X-ray diffractometry, and the intensity ratio of the peak assigned to the (112) plane of the orthorhombic YAlO 3 to the peak assigned to the (420) plane of the cubic Y 3 Al 5 O 12 is at least 0.01 and less than 1. Alternatively, a powder for coating or sintering includes a composite oxide of yttrium and aluminum, and the volume of pores with a pore size of from 0.1 to 1 μm of the powder is at least 0.16 mL/g. It is preferable that, in X-ray diffractometry using CuKα radiation with a scan range of 2θ=20° to 60°, a peak assigned to the cubic Y 3 Al 5 O 12 is a peak that shows the highest peak intensity.
1. A powder for coating or sintering, exhibiting a peak assigned to cubic Y 3 Al 5 O 12 and a peak assigned to orthorhombic YAlO 3 in X-ray diffractometry,
wherein an intensity ratio of a peak assigned to a (112) plane of the orthorhombic YAlO 3 to a peak assigned to a (420) plane of the cubic Y 3 Al 5 O 12 is at least 0.01 and less than 1,
the powder exhibits a peak within a pore size range from 0.1 to 1 μm and a peak within a pore size range from 5 to 50 μm in a pore volume distribution relative to pore sizes as measured by mercury intrusion porosimetry,
a volume of pores with a pore size of from 0.1 to 1 μm is at least 0.16 mL/g and 1.0 mL/g or less, and
a ratio of a pore volume V1 to a pore volume V2 (V1/V2) is 0.3 to 1.0 where V1 is the volume of the pores with the pore size of from 0.1 to 1 μm and V2 is a volume of the pores with the pore size of from 5 to 50 μm.
2. The powder for coating or sintering according to claim 1 , further exhibiting a peak assigned to cubic Y 2 O 3 in the X-ray diffractometry, wherein an intensity ratio of a peak assigned to a (222) plane of the cubic Y 2 O 3 to the peak assigned to the (420) plane of the cubic Y 3 Al 5 O 12 is at least 0.001 and less than 0.1.
3. The powder for coating or sintering according to claim 1 , wherein an intensity ratio of a peak assigned to a (104) plane of trigonal Al 2 O 3 to the peak assigned to the (420) plane of the cubic Y 3 Al 5 O 12 is less than 0.1.
4. The powder for coating or sintering according to claim 1 , wherein the powder has a crystallite size of at least 50 nm as determined from a full width at half maximum of the peak assigned to the (420) plane of Y 3 Al 5 O 12 in the X-ray diffractometry.
5. The powder for coating or sintering according to claim 1 , wherein the volume of pores with a pore size of from 5 to 50 μm is at least 0.1 mL/g.
6. The powder for coating or sintering according to claim 5 , wherein the volume of pores with the pore size of from 5 to 50 μm is at least 0.1 mL/g and at most 0.5 mL/g.
7. The powder for coating or sintering according to claim 1 , wherein the powder has a BET specific surface area of 1 to 5 m 2 /g.
8. The powder for coating or sintering according to claim 1 , wherein the powder is granular and has an average particle size of at least 15 μm.
9. The powder for coating or sintering according to claim 1 , wherein, in X-ray diffractometry using CuKα radiation in a scan range of 2θ=20° to 60°, a peak assigned to the cubic Y 3 Al 5 O 12 is a peak that has the highest peak intensity.
10. The powder for coating or sintering according to claim 1 , wherein a ratio of an intensity S4 of a peak assigned to a (104) plane of trigonal Al 2 O 3 to the intensity S1 of the peak assigned to the (420) plane of the cubic Y 3 Al 5 O 12 , S4/S1, is at most 0.01.
11. The powder for coating or sintering according to claim 1 , wherein the ratio (V1/V2) is 0.4 to 1.0.
12. The powder for coating or sintering according to claim 1 , wherein the ratio (V1/V2) is 0.5 to 1.0.
13. A method for producing a coating, comprising a step of thermal spraying the powder for coating or sintering according to claim 1 .
14. A method for producing a sintered material, comprising sintering the powder for coating or sintering according to claim 1 .
15. A coating made from the powder for coating or sintering according to claim 1 , formed by thermal spraying or PVD.
16. A sintered material made from the powder for coating or sintering according to claim 1 .
17. A method for producing a coating, comprising a step of forming the coating by PVD using the powder for coating or sintering according to claim 1 .