Provided is a method for producing a decorated cycloolefin resin molded article, the method comprising curing a gel coat composition and polymerizing a cycloolefin polymerizable composition containing a radical generator while the gel coat composition is in contact with the cycloolefin polymerizable composition, thereby containing a decorated cycloolefin resin molded article including a gel coat and a cycloolefin resin layer adhering to each other.
1. A method for producing a decorated cycloolefin resin molded article, comprising:
curing a gel coat composition containing a base resin and a thermal curing agent and polymerizing a cycloolefin polymerizable composition containing a radical generator at the same timing while the gel coat composition is in contact with the cycloolefin polymerizable composition, thereby obtaining the decorated cycloolefin resin molded article including a gel coat obtained by curing the gel coat composition and a cycloolefin resin layer obtained by polymerizing the cycloolefin polymerizable composition adhering to each other,
wherein an amount of the thermal curing agent is 0.2 to 4 parts by mass relative to 100 parts by mass of the base resin, a content of a curing accelerator in the gel coat composition is 1 mass % or less, and the cycloolefin polymerizable composition further comprises an isocyanate compound and/or a polyfunctional acrylate compound,
the isocyanate compound is at least one selected from the group consisting of 4,4′-methylenediphenyl diisocyanate, toluene-2,4-diisocyanate, 4-methoxy-1,3-phenylene diisocyanate, 4-isopropyl-1,3-phenylene diisocyanate, 4-chloro-1,3-phenylene diisocyanate, 4-butoxy-1,3-phenylene diisocyanate, 2,4-diisocyanate diphenyl ether, 1,4-phenylene diisocyanate, tolylene diisocyanate, xylylene diisocyanate, 1,5-naphthalene diisocyanate, benzidine diisocyanate, o-nitrobenzidine diisocyanate, 4,4′-dibenzyl diisocyanate, methylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,10-decamethylene diisocyanate, 4-cyclohexylene diisocyanate, 4,4′-methylene bis(cyclohexyl isocyanate), 1,5-tetrahydronaphthalene diisocyanate, isophorone diisocyanate, hydrogenated 4,4′-methylenediphenyl diisocyanate, hydrogenated xylylene diisocyanate, and a polyurethane prepolymer prepared by reacting these diisocyanate compounds with a low molecular weight polyol or polyamine to be isocyanate terminated, and
the polyfunctional acrylate compound is at least one selected from the group consisting of ethylene glycol dimethacrylate, triethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, and neopentyl glycol dimethacrylate.
2. The method for producing the decorated cycloolefin resin molded article according to claim 1 , wherein the cycloolefin polymerizable composition contains a filler.
3. The method for producing the decorated cycloolefin resin molded article according to claim 2 , wherein the filler includes at least one of a fibrous filler and a particulate filler.