ONE-COMPONENT HEAT-ACTIVATABLE POLYURETHANE WATER-BASED ADHESIVE COMPOSITION
One-component heat-activatable polyurethane water-based adhesive composition, which comprises, with respect to the total weight of the adhesive composition: —from 12% to 50%, by weight of dry matter, of an aqueous dispersion of a polyurethane (A) comprising alkoxysilyl pending and/or terminal groups, and —from 0.5% to 5% by weight of a glycidoxy substituted alkoxysilane compound (B) with a glycidoxy functionality of at least 2.
1 - 12 . (canceled)
13 . One-component heat-activatable polyurethane water-based adhesive composition, which comprises, with respect to the total weight of the adhesive composition:
from 12% to 50%, by weight of dry matter of an aqueous dispersion of a polyurethane (A) comprising alkoxysilyl pending and/or terminal groups, and
from 0.5% to 5% by weight of a glycidoxy substituted alkoxysilane compound (B) with a glycidoxy functionality of at least 2.
14 . One-component adhesive composition according to claim 13 , wherein the water-based dispersion of polyurethane (A) is an aqueous anionic aliphatic polyurethane aqueous dispersion.
15 . One-component adhesive composition according to claim 13 , wherein the alkoxy radical comprised in the alkoxysilyl pending and/or terminal groups of polyurethane (A) is selected from the group consisting of methoxy and ethoxy radicals.
16 . One-component adhesive composition according to claim 13 , wherein the silane compound (B) has a glycidoxy functionality of at least 3.
17 . One-component adhesive composition according to claim 13 , wherein it also comprises, with respect to the total weight of said adhesive composition, from 8 to 30%, by weight of dry matter, of an aqueous emulsion of a copolymer (C) of vinyl acetate and ethylene (VAE).
18 . One-component adhesive composition according to claim 17 , wherein the VAE (C) is such that:
the Brookfield viscosity of a 55% weight/weight in dry matter aqueous dispersion of (C) is greater than 4000 mPa·s at 25° C.; and/or
its glass transition temperature (Tg) is greater than 0° C.
19 . One-component adhesive composition according to claim 13 , wherein the composition comprises up to 15% by weight of dry matter of an aqueous dispersion of a non silylated polyurethane (D).
20 . One-component adhesive composition according to claim 13 , wherein water represents from 20% to 60% by weight of the total weight of the adhesive composition.
21 . One-component adhesive composition according to claim 17 , wherein it comprises:
from 12% to 40%, by weight of dry matter of the aqueous dispersion of polyurethane (A);
from 0.5% to 2% by weight of compound (B);
from 9 to 28%, by weight of dry matter of the aqueous emulsion of VAE copolymer (C); and
between 3 and 13% by weight of dry matter of the aqueous dispersion of non silylated polyurethane (D).
22 . Process of manufacturing the heat-activatable polyurethane water-based adhesive composition of claim 13 , said process comprising the steps of:
i. introducing an aqueous emulsion of the VAE copolymer (C), when present, in a mixing vessel under stirring; then
ii. introducing the aqueous dispersion of the polyurethane (A), in said vessel under constant stirring; then
iii. introducing silane compound (B) in said vessel, still under stirring.
23 . Method of joining a substrate and a decorative expandable thermoplastic cover material, by thermoforming lamination, said method comprising the steps of:
a) applying the heat-activatable polyurethane water-based adhesive composition of claim 13 , on the surface of said substrate;
b) drying the applied composition to remove water; then
c) applying the expandable thermoplastic cover material on the substrate surface coated with the dried adhesive composition, by a thermoforming lamination process.
24 . Method according to claim 23 , wherein the expandable thermoplastic cover material is a PVC foil.