Low-temperature NO
A low-temperature NO x storage catalyst for automobile exhaust purification and a preparation method thereof. Loading a noble metal salt solution on molecular sieve by equal volume impregnation method, wherein the noble metal salt solution comprises palladium nitrate and platinum nitrate, and the molecular sieve comprises SSZ, SAPO and BETA, then drying at 60-120° C. for 2-6 h, roasting at 500-550° C. in air for 2-5 h, and further roasting at 750-850° C. in air for 2-5 h, and then mixing with aluminum sol, ball milling and pulping, and then coating the slurry on a carrier, wherein the loading on the coating is 100-250 g/L and the noble metal content is 10-150 g/ft 3 , drying at 60-120° C. for 2-6 h, then roasting at 500-550° C. in air for 2-5 h, and further continuing roasting at 750-850° C. in air for 2-5 h, to obtain the catalyst. Loading the noble metals Pt and Pd into a pore channel of a molecular sieve improves NO x storage capacity of a catalyst at low temperatures, and selecting a different type of molecular sieve as an NO x storage unit and increasing a roasting temperature of a molecular sieve material on which Pt and Pd are loaded significantly increases NO x storage capacity.
1. A preparation method of low-temperature NO x storage catalyst for automobile exhaust purification, characterized by comprising the following steps:
(1) Loading a noble metal salt solution on molecular sieve by equal volume impregnation method, wherein the noble metal salt solution comprises but not limited to palladium nitrate and platinum nitrate, and the molecular sieve comprises but not limited to SSZ, SAPO and BETA, and the content of noble metals in element accounts for more than 0% and no more than 3% by mass of the coating, then drying at 60-120° C. for 2-6 h, roasting at 500-550° C. in air for 2-5 h, and further roasting at 750-850° C. in air for 2-5 h to obtain M1;
(2) Mixing M1 and aluminum sol, ball milling and pulping to obtain a noble metal slurry N1;
(3) Coating the slurry N1 on a carrier, wherein the loading on the coating is 100-250 g/L and the noble metal content is 10-150 g/ft 3 , drying at 60-120° C. for 2-6 h, then roasting at 500-550° C. in air for 2-5 h, and further continuing roasting at 750-850° C. in air for 2-5 h, to obtain the catalyst.
2. The preparation method of low-temperature NO x storage catalyst for automobile exhaust purification according to claim 1 , characterized in that, in step (1), the noble metal salt solution is a soluble salt solution of platinum and palladium.
3. The preparation method of low-temperature NO x storage catalyst for automobile exhaust purification according to claim 1 , characterized in that, the mass ratio of platinum and palladium in the catalyst is 1:9-9:1.
4. The preparation method of low-temperature NO x storage catalyst for automobile exhaust purification according to claim 1 , characterized in that, the molecular sieve is one of or a mixture of more of SSZ, SAPO or BETA.
5. A low-temperature NO x storage catalyst for automobile exhaust purification, characterized in that, the catalyst is a catalyst prepared by the preparation method of any one of claims 1 to 4 .