NATURAL COMPOSITE MATERIALS DERIVED FROM SEAWEED AND METHODS OF MAKING THE SAME
Provided are natural seaweed composite materials comprising one or more insoluble fibers and agar associated with the insoluble fiber. The natural seaweed composite materials are produced by methods comprising high pressure homogenization which maintains the natural complex structure of the insoluble fiber and the agar as in natural unprocessed seaweeds.
1 . A natural seaweed composite material comprising one or more insoluble fibers and agar, wherein the agar is associated with the insoluble fiber.
2 . The natural seaweed composite material of claim 1 , wherein the insoluble fiber comprises cellulose and insoluble hemicellulose.
3 . The natural seaweed composite material of claim 1 , wherein the agar is bound to the surface of the insoluble fiber.
4 . The natural seaweed composite material of claim 1 , wherein the insoluble fiber is partially or entirely encapsulated by the agar.
5 . The natural seaweed composite material of claim 1 , wherein the insoluble fiber is partially or entirely embedded within the agar.
6 . The natural seaweed composite material of claim 1 , wherein the natural seaweed composite material is obtained from red algae.
7 . The natural seaweed composite material of claim 1 , wherein the natural seaweed composite material has a particle size of less than or about 100 μm, less than or about 90 μm, less than or about 80 μm, less than or about 70 μm, less than or about 60 μm, less than or about 50 μm, less than or about 40 μm, less than or about 30 μm, less than or about 20 μm, less than or about 10 μm, less than or about 5 μm, less than or about 4 μm, less than or about 3 μm, less than or about 2 μm, or less than or about 1 μm.
8 . The natural seaweed composite material of claim 1 , wherein the natural seaweed composite material has a particle size of between 0.1 μm and 100 μm, between 1 μm and 100 μm, between 10 μm and 90 μm, between 20 μm and 80 μm between 30 μm and 70 μm, between 40 μm and 60 μm, between 0.5 μm and 20 μm, between 1 μm and 15 μm, between 2 μm and 10 μm, between 3 μm and 8 μm, between 4 μm and 7 μm, or between 5 μm and 6 μm.
9 . A method of making a natural seaweed composite material from red algae, comprising the steps of:
treating the fresh or dried seaweed with one or more acids,
grinding the acid-treated seaweed by wet milling or dry grinding,
subjecting the ground seaweed to high pressure homogenization (HPH), and
drying and grinding the homogenized seaweed powder to a desired particle size to obtain the natural seaweed composite material.
10 . The method of claim 9 , wherein the HPH is carried out at a temperature of between 0° C. and 85° C.
11 . The method of claim 9 , the HPH is carried out at room temperature.
12 . The method of claim 9 , the seaweed is washed and/or cleaned to remove debris before the acid treatment.
13 . The method of claim 9 , the seaweed is bleached by one or more bleaching agents before HPH.
14 . The method of claim 9 , further comprises treating the fresh or dried seaweed with one or more alkalis before the acid treatment to obtain a natural seaweed composite material having a high gelling strength.
15 . The method of claim 14 , further comprises a step of a second acid treatment after HPH treatment to obtain a natural seaweed composite material having a low gelling strength.
16 . A natural seaweed composite material produced by the method of claim 9 .
17 . The natural seaweed composite material of claim 16 , comprises one or more insoluble fibers and agar, wherein the agar is associated with the insoluble fiber.
18 . The natural seaweed composite material of claim 17 , wherein the insoluble fiber comprises cellulose and insoluble hemicelluloses.
19 . The natural seaweed composite material of claim 17 , wherein the insoluble fiber is associated with agar in a manner similar to the association in the natural state in seaweed before processing.
20 . The natural seaweed composite material of claim 17 , wherein the agar is bound to the surface of the insoluble fiber such as cellulose of the natural seaweed composite material.
21 . The natural seaweed composite material of claim 17 , wherein the insoluble fiber is entirely or partially embedded within agar.
22 . The natural seaweed composite material of claim 17 , wherein the insoluble fiber is partially or entirely encapsulated by agar.
23 . The natural seaweed composite material of claim 17 , wherein the natural seaweed composite material has a particle size of less than or about 100 μm, less than or about 90 μm, less than or about 80 μm, less than or about 70 μm, less than or about 60 μm, less than or about 50 μm, less than or about 40 μm, less than or about 30 μm, less than or about 20 μm, less than or about 10 μm, less than or about 5 μm, less than or about 4 μm, less than or about 3 μm, less than or about 2 μm, or less than or about 1 μm.
24 . The natural seaweed composite material of claim 17 , wherein the natural seaweed composite material has a particle size of between 0.1 μm and 100 μm, between 1 μm and 100 μm, between 10 μm and 90 μm, between 20 μm and 80 μm between 30 μm and 70 μm, between 40 μm and 60 μm, between 0.5 μm and 20 μm, between 1 μm and 15 μm, between 2 μm and 10 μm, between 3 μm and 8 μm, between 4 μm and 7 μm, or between 5 μm and 6 μm.