Glass-based articles with stress profiles having regions of enhanced stress
Glass-based articles comprise: a lithium-based aluminosilicate composition; a glass-based substrate having opposing first and second surfaces defining a substrate thickness (t), wherein t is less than or equal to 0.74 mm; and a stress profile comprising: a spike region extending from the first surface to a tail region. A stress profile comprises: a maximum compressive stress (CS max ) of greater than or equal to 450 MPa; a spike region extending from the first surface to a tail region; and the tail region extending to a center of the glass-based article; wherein the tail region comprises: a region of enhanced stress having a first average compressive stress (CS avg−1 ) of greater than or equal to 100 MPa; and a FSM depth of layer (DOL FSM ) located at a depth of greater than or equal to 13 micrometers.
1. A glass-based article comprising:
a lithium containing aluminosilicate composition;
a glass-based substrate having opposing first and second surfaces defining a substrate thickness (t), wherein t is less than or equal to 0.74 mm; and
a stress profile comprising:
a maximum compressive stress (CS max ) of greater than or equal to 450 MPa;
a spike region extending from the first surface to a tail region; and
the tail region extending to a center of the glass-based article;
wherein the tail region comprises:
a region of enhanced stress having a first average compressive stress (C avg−1 ), from DOL sp , plus one micron to DOL FSM , of greater than or equal to 100 MPa; and
a FSM depth of layer (DOL FSM ) located at a depth of greater than or equal to 13 micrometers.
2. The glass-based article of the claim 1 , wherein the first average compressive stress (CS avg−1 ) is less than or equal to 220 MPa.
3. The glass-based article of claim 1 , wherein a DOL sp is greater than or equal to 3 micrometers and less than or equal to 20 micrometers.
4. The glass-based article of claim 1 , wherein CS avg−1 is in a range of greater than or equal to 125 to less than or equal to 195.
5. The glass-based article of claim 1 , wherein CS avg-1 is in a range of greater than or equal to 100 to less than or equal to 160.
6. The glass-based article of claim 1 , wherein the DOL FSM is located at a depth of greater than or equal to 20 micrometers.
7. The glass-based article of claim 6 , wherein the DOL FSM is located at a depth of greater than or equal to 22 micrometers.
8. The glass-based article of claim 1 , wherein the t is greater than or equal to 0.2 millimeters.
9. The glass-based article of claim 1 , wherein a molar ratio of Na 2 O to Li 2 O in the lithium containing aluminosilicate composition is greater than or equal to 1.
10. The glass-based article of claim 1 , wherein a maximum central tension (CT max ) is greater than or equal to 40 MPa.
11. The glass-based article of claim 1 comprising potassium oxide (K 2 O) having a non-zero concentration that varies from the first surface to a potassium depth of layer (DOL K ).
12. The glass-based article of claim 1 , wherein all points of the stress profile located in the spike region comprise a tangent having a slope with an absolute value that is 20 MPa/micrometer or greater, and all points of the stress profile located in the tail region deeper than the DOL K comprise a tangent having a slope with an absolute value that is less than 20 MPa/micrometer.
13. The glass-based article of claim 1 , wherein the thickness is less than 0.70 mm.
14. A consumer electronic product comprising:
a housing having a front surface, a back surface, and side surfaces;
electrical components at least partially within the housing, the electrical components comprising at least a controller, a memory, and a display, the display at or adjacent the front surface of the housing; and
a cover disposed over the display;
wherein at least a portion of at least one of the housing and the cover comprises the glass-based article of claim 1 .