Bird-friendly, thermally-insulating glass and method for making the same
A method for manufacturing a glazing. A low-emissivity protected glass piece has a low-emissivity coating applied to a second face thereof and a protective film covering the low-emissivity coating. The glass piece is placed on a surface of a screen printing table, the protective layer being in contact with said surface. Acid etching is performed with an acid paste which attacks the first face of the low-e protected glass piece to print visual markers thereon using a screen printing canvas on the first face. After waiting, the first face of the low-e protected glass piece is washed to remove the acid paste to obtain a permanent frosted finish pattern forming the bird-friendly visual markers on the first face. The protective film is removed to obtain a low-e marked glass having visual markers on one side and a low-e coating on another side, and then the marked glass is tempered.
1. A method for manufacturing a glazing comprising the steps of:
providing a low-emissivity protected glass piece having a glass piece with a first face and a second face, the first face opposing the second face, the low-emissivity protected glass piece having
a low-emissivity coating applied to the second face of the glass piece and
a protective film covering the low-emissivity coating;
placing the low-emissivity protected glass piece on a surface of a screen printing table, the protective layer being in contact with the surface of the screen printing table;
using a screen printing canvas on the first face, performing an acid etching with an acid paste which attacks the first face of the low-emissivity protected glass piece to print visual markers thereon;
after having waited for a period of time, washing the first face of the low-emissivity protected glass piece to remove the acid paste to obtain a permanent frosted finish pattern forming the visual markers on the first face;
removing the protective film to obtain a low-e marked glass having the visual markers on one side and the low-emissivity coating on another side; and
following the removing of the protective film, tempering the low-e marked glass.
2. The method of claim 1 , further comprising, prior to placing the low-emissivity protected glass piece on the surface of the screen printing table,
providing the glass piece having the low-emissivity coating applied to the second face of the glass piece; and
applying the protective film onto the low-emissivity coating to obtain the low-emissivity protected glass piece.
3. The method of claim 1 , wherein the period of time is ranging between 2 and 6 minutes.
4. The method of claim 1 , wherein the period of time is about 5 minutes.
5. The method of claim 1 , wherein the low-emissivity coating is transparent in a visible spectrum.
6. The method of claim 1 , wherein the tempering of the low-emissivity marked glass is performed when the visual markers are in contact with rollers of a conveyor of a tempering furnace.
7. A method for manufacturing a glazing comprising the steps of:
providing a low-emissivity protected glass piece having a glass piece with a first face and a second face, the first face opposing the second face, the low-emissivity protected glass piece having
a low-emissivity coating applied to the second face of the glass piece and
a consumable protective layer covering the low-emissivity coating;
placing the low-emissivity protected glass piece on a screen printing table, the consumable protective layer of the low-emissivity protected glass piece being in contact with the surface of the table;
using a screen printing canvas on the second face, performing an acid etching with an acid paste which attacks the second face to print visual markers thereon;
after having waited for a period of time, washing the glass to remove the acid paste to obtain a permanent frosted finish pattern forming the visual markers; and
tempering the low-emissivity marked glass while leaving the protective layer in a tempering furnace for burning during tempering.
8. The method of claim 7 , further comprising, prior to placing the low-emissivity protected glass piece on the surface of the screen printing table,
providing the glass piece having the low-emissivity coating applied to the second face of the glass piece; and
applying the consumable protective layer onto the low-emissivity coating to obtain the low-emissivity protected glass piece.
9. The method of claim 7 , wherein the period of time is ranging between 2 and 6 minutes.
10. The method of claim 7 , wherein the period of time is about 5 minutes.
11. The method of claim 7 , wherein the low-emissivity coating is transparent.
12. The method of claim 7 , wherein the tempering of the low-emissivity marked glass is performed when the visual markers are in contact with rollers of a conveyor of the tempering furnace.