Transparent polymer aerogels
View Patent ↗A product includes a polymer aerogel. The aerogel is physically characterized by having a transparency greater than or equal to 90% transmission of visible light through a 3 mm thickness of the aerogel. The aerogel includes at least one oligomer selected from the group consisting of: a polyamide, a polyimide, a polyacrylate, a polyvinyl, and a polythioether. A method includes dissolving at least one monomer in at least one solvent to form a mixture and causing polymerization of the at least one monomer to form at least one oligomer. The method also includes causing crosslinking of the at least one oligomer, initiating gelation of a product of the crosslinking and the at least one solvent to form an aerogel precursor; and forming an aerogel from the aerogel precursor.
1. A product, comprising:
a polymer aerogel, the aerogel being physically characterized by having a transparency greater than or equal to 90% transmission of visible light through a 3 mm thickness of the aerogel, wherein the aerogel comprises at least one oligomer selected from the group consisting of: a polyamide, a polyimide, a polyacrylate, a polyvinyl, and a polythioether, wherein the aerogel includes fibers, wherein an average diameter of the fibers in the aerogel is less than or equal to 10 nm.
2. The product of claim 1 , wherein the aerogel includes pores, wherein an average diameter of the pores in the aerogel is less than or equal to 20 nm.
3. The product of claim 1 , wherein the aerogel is characterized as having a surface area greater than 500 m 2 /g, wherein the aerogel is characterized as having a density between about 50 mg/cm 3 and about 200 mg/cm 3 .
4. A product comprising:
a polymer aerogel, the aerogel being physically characterized by having a transparency greater than or equal to 90% transmission of visible light through a 3 mm thickness of the aerogel, wherein the aerogel comprises at least one oligomer selected from the group consisting of: a polyamide, a polyimide, a polyacrylate, a polyvinyl, and a polythioether, wherein the aerogel is characterized as having a transparency gradient along at least a portion thereof.
5. The product of claim 1 , wherein the aerogel comprises at least two regions, wherein a first region of the aerogel has a first transparency, wherein a second region of the aerogel has a second transparency which is different than the first transparency.
6. A product, comprising:
a polymer aerogel, the aerogel being physically characterized by having a transparency greater than or equal to 90% transmission of visible light through a 3 mm thickness of the aerogel, wherein the aerogel comprises at least one oligomer selected from the group consisting of: a polyamide, a polyimide, a polyacrylate, a polyvinyl, and a polythioether, wherein the aerogel is elastic and exhibits shape memory.
7. The product of claim 1 , comprising a material selected from the group consisting of polystyrene, polyvinyl alcohol, and polyacrylonitrile.
8. The product of claim 1 , comprising a material selected from the group consisting of polyurea and polybenzoxazine.
9. The product of claim 1 , wherein the fibers are unimolecular.
10. The product of claim 1 , wherein the aerogel has a modulus greater than or equal to 1 MPa.
11. The product of claim 1 , wherein the aerogel has a thermal conductivity less than 38 mW/mK.
12. The product of claim 1 , wherein the aerogel has a thermal conductivity in a range between about 38 mW/mK and about 46 mW/mK.
13. The product of claim 1 , wherein the aerogel has a fully conjugated polyimide backbone.
14. The product of claim 1 , wherein the aerogel has a graded composition along at least a portion thereof.
15. The product of claim 4 , wherein the transparency gradient includes a transition from a relatively more transparent region to a relatively more translucent region.
16. The product of claim 4 , wherein the transparency gradient is a product of different phases of the same chemical composition.
17. The product of claim 4 , wherein the transparency gradient is a product of layers having a same chemical composition and different relative transparencies.
18. A method for forming the aerogel of claim 1 , the method comprising:
dissolving at least one monomer in at least one solvent to form a mixture;
causing polymerization of the at least one monomer to form at least one oligomer;
causing crosslinking of the at least one oligomer;
initiating gelation of a product of the crosslinking and the at least one solvent to form an aerogel precursor; and
forming the aerogel from the aerogel precursor.