Blue-emitting nanocrystals with cubic shape and fluoride passivation
This disclosure pertains to the field of nanotechnology. The disclosure provides methods of preparing nanostructures with fluoride passivation. The disclosure also provides methods of preparing nanostructures with fluoride and amine passivation. The nanostructures have high quantum yield, narrow emission peak width, tunable emission wavelength, and colloidal stability. Also provided are nanostructures prepared using the methods. And, nanostructure films and molded articles comprising the nanostructures are also provided.
1. A nanostructure comprising:
a nanocrystal core; and
at least one shell disposed on the core, wherein at least one shell comprises ZnS or ZnSe;
at least one fluoride bound to the surface of the nanostructure; and
at least one amine bound to the surface of the nanostructure.
2. The nanostructure of claim 1 , wherein the core comprises InP.
3. The nanostructure of claim 1 , wherein at least one shell comprises ZnSe.
4. The nanostructure of claim 1 , wherein at least one shell comprises a first shell comprising ZnSe and a second shell comprising ZnS.
5. The nanostructure of claim 1 , wherein the fluoride is in the form of a metal fluoride, ammonium fluoride, or tetraalkylammonium fluoride.
6. The nanostructure of claim 1 , wherein the fluoride is in the form of a tetraalkylammonium fluoride.
7. The nanostructure of claim 1 , wherein the molar ratio of fluoride bound to the nanostructure to zinc in the nanostructure is between about 0.05 and about 0.35.
8. The nanostructure of claim 1 , wherein the nanostructure comprises a nanostructure comprising a core comprising InP, at least one shell comprising ZnS, at least one shell comprising ZnSe, tetraalkylammonium fluoride bound to the surface of the nanostructure, and octylamine bound to the surface of the nanostructure.
9. The nanostructure of claim 1 , wherein the nanostructure exhibits a peak emission wavelength of between 450 nm and 550 nm.
10. The nanostructure of claim 1 , wherein the nanostructure exhibits a peak emission wavelength of between 550 nm and 650 nm.
11. The nanostructure of claim 1 , wherein the nanostructure exhibits a photoluminescence quantum yield of between about 60% and about 99%.
12. The nanostructure of claim 1 , wherein the nanostructure exhibits a photoluminescence quantum yield of between about 60% and about 90%.
13. The nanostructure of claim 1 , wherein the nanostructure is a quantum dot.
14. A device comprising the nanostructure of claim 1 .
15. A film comprising the nanostructure of claim 1 and at least one organic resin.
16. A molded article comprising the film of claim 15 .
17. A method of preparing the nanostructure of claim 1 , comprising admixing:
(a) a nanostructure comprising a nanocrystal core and at least one shell disposed on the core, wherein at least one shell comprises ZnS or ZnSe;
(b) at least one fluoride source; and
(c) at least one amine source;
to provide a nanostructure.