Phosphor composition
A method is disclosed for forming a blended phosphor composition. The method includes the steps of firing precursor compositions that include europium and nitrides of at least calcium, strontium and aluminum, in a refractory metal crucible and in the presence of a gas that precludes the formation of nitride compositions between the nitride starting materials and the refractory metal that forms the crucible. The resulting compositions can include phosphors that convert frequencies in the blue portion of the visible spectrum into frequencies in the red portion of the visible spectrum.
1. A method of making a phosphor composition comprising:
forming a mixture comprising nitrides of calcium, nitrides of strontium, nitrides of aluminum and nitrides of silicon with a europium source composition; and
forming a phosphor composition with a nominal composition of Ca 1-x-y Sr x Eu y AlSiN 3 , wherein 0<x<1 and 0<y<1, mixed with an amount of silicon aluminum oxynitride of at least 1%.
2. The method of claim 1 , wherein forming the phosphor composition comprises:
heating the mixture in a refractory crucible that is substantially inert in the presence of the forming gas mixture;
at a temperature sufficient to produce the phosphor composition but less than a temperature at which the nitrides or the phosphor composition would decompose or react with the crucible; and
for a time sufficient to form the phosphor composition.
3. The method of claim 1 , wherein the phosphor composition absorbs wavelengths of between about 430 and 480 nanometers and emits peak wavelengths of between about 530 and 750 nanometers.
4. The method of claim 1 wherein the silicon aluminum oxynitride comprises Si 2 Al 4 O 4 N 4 .
5. The method of claim 1 wherein forming the mixture comprises mixing Ca 3 N 2 , Sr 2 N, AlN and Si 3 N 4 .
6. The method of claim 2 wherein the refractory crucible comprises a refractory metal selected from the group consisting of tungsten and molybdenum.
7. The method of claim 1 , wherein forming the phosphor composition comprises heating the mixture to a temperature of between about 1500 and 1800° C.
8. The method of claim 1 , wherein forming the phosphor composition comprises at least three heating steps at increasingly higher temperatures.
9. The method of claim 8 , wherein the at least three heating steps comprise a one hour heating step at 800° C., a one hour heating step at 1200° C., and a two hour heating step at 1675° C. with ramping steps of 350° C. per hour between heating steps.
10. The method of claim 1 , wherein forming the mixture comprises mixing the nitrides and the europium source composition in a proportion that produces a mole fraction of europium in the phosphor composition of between about 0.013 and 0.017.
11. The method according to claim 1 , wherein forming the mixture comprises mixing the nitrides and the europium source composition in a proportion that produces a mole fraction of strontium in the phosphor composition of between about 0.50 and 0.70.