Rapid mercury-free photochemical microencapsulation/nanoencapsulation at ambient conditions
View Patent ↗A method of mercury-free photochemical micro-/nano-encapsulation of an active material is a process for obtaining Micro-/nano-capsules by means of curing by UV LED radiation at ambient or even cold temperatures. A stirrer photo-reactor made from glass or transparent plastics can be used but mixed flow reactor could be also employed. Appropriate mixing is sufficient to expose all droplets, which contain an active material surrounded by curable-shell materials in the emulsion to the LED radiation. Using the optimum light intensities and reactions' times is critical for encapsulating the active material with a high efficiency and producing a high quality micro-/nano-capsules, Solar monochromator device can also be used as long as it generate the same radiation with a narrow/single wavelengths as the LED device. Light emitted diode (LED) is a mercury-free UV radiation source with a long operating life time and an instant ON-Off, it has a high efficiency, a very low cooling requirements and cost-efficient in photochemical encapsulation. It reduces the time of microencapsulation from 6 hours to a less than 5 minutes. It has a significant decrease in manufacturing cost, waste-water, unconverted monomers, and leftover active phase change material (PCM) compared to other methods. Conversion of more than 90% of monomers can be achieved, and encapsulation efficiency can reach 100% at optimum conditions. This is in addition to the ability of this invented technology for encapsulate volatile and heat sensitive active materials at ambient as well as low temperatures. Normal glass or transparent plastics can be used as a reactor material. Only the matched useful wavelength radiation is emitted by LED without having other wavelengths which might have a bad impact on the encapsulation process.
1. A method for photochemical micro- or nano-encapsulation of a phase change active material with a curable material wherein the curable material comprises a mono-functional monomer and the method comprises the steps of:
(a) preparing a discontinuous droplets phase wherein the discontinuous droplets phase contains (i) at least one phase change active material; (ii) at least one curable mono-functional monomer; and (iii) at least one photo-initiator;
(b) preparing a continuous liquid phase that is immiscible with the discontinuous droplets phase and contains water and at least one stabilizer/emulsifying agent without surfactant;
(c) preparing a micro- or nano-emulsion by emulsifying the discontinuous droplets phase in the continuous phase by a high shear emulsifier; and
(d) introducing the emulsion to a photoreactor wherein the emulsion is irradiated at an ambient or cold temperature for five minutes or less with at least one UV-LED lamp and continuously mixed with a helix stirrer to encapsulate the phase change active material with the curable mono-functional monomer to afford microcapsules or nanocapsules.
2. The method of claim 1 , further comprising a step after step (c) wherein the emulsion is subjected to sonication to reduce the droplets' size.
3. The method of claim 2 , wherein the step after step (c) reduces the size of the droplets to 100 nm.
4. The method of claim 1 , wherein the curable material further comprises a second mono-functional monomer or a di-, tri-, or poly-functional monomer.
5. The method of claim 1 , wherein the irradiation of step (d) is for five minutes.
6. The method of claim 1 , wherein the irradiation of step (d) is for less than five minutes.
7. The method of claim 1 , wherein the UV-LED radiation is a wavelength of 365 nm and the radiation intensity is 0.6 W/cm 2 .
8. The method of claim 1 , wherein the UV-LED radiation is a wavelength of 365 nm, and the radiation intensity is 1.2 W/cm 2 , and the irradiation of step (d) is for five minutes.
9. The method of claim 1 , further comprising step (e) wherein the microcapsules or nanocapsules are filtered, washed, and dried.
10. The method of claim 1 , wherein the photoreactor is a rounded or square glass or UV transparent plastic tube.
11. The method of claim 10 , wherein the photoreactor is rounded and is 3.5 cm in diameter.
12. The method of claim 1 , wherein more than one UV-LED lamp each having a different or similar light wavelength and different light intensity is used.
13. The method of claim 1 , wherein more than 90% of the mono-functional monomer is polymerized.
14. The method of claim 1 , wherein the encapsulation efficiency is 100%.
15. The method of claim 1 , wherein the UV-LED radiation is a wavelength of 365 nm and the radiation intensity is 1.2 W/cm 2 .