Roofing shingles, tiles and shakes
The present disclosure relates generally to roofing elements and methods for making them. In one embodiment, the disclosure provides a roofing element in the form of a roofing shingle that includes a body of a foamed cured cross-linked polymer, the body having a top surface and a bottom surface, the body extending substantially in a plane and having a thickness in the range of 0.5 mm to 35 mm; and a layer of weather-resistant roofing granules disposed on and adhered at the top surface of roofing element. The roofing element can be made by providing a body of wet foamed curable composition, and allowing the curable composition to cure to provide the body of foamed cured cross-linked polymer.
1 . A roofing element in the form of a roofing shingle, shake or tile extending substantially in a plane, the roofing element having a top surface, the roofing element comprising:
a body of a foamed cured cross-linked polymer, the body having a top surface at the top surface of the roofing element and a bottom surface, the body extending substantially in the plane,
a support sheet disposed within the body of foamed cured cross-linked polymer, the support sheet comprising roofing felt; and
a layer of weather-resistant roofing granules disposed on and adhered at the top surface of the roofing element,
wherein the weather-resistant roofing granules are disposed directly on and partially embedded in a top surface of the body of the foamed cured cross-linked polymer,
wherein the roofing element has an asphalt content of less than about 5 wt %, and
wherein the roofing element passes the ASTM E-84 flame spray test.
2 . The roofing element of claim 1 , having an asphalt content of less than about 2 wt %.
3 . The roofing element of claim 1 , further comprising a mesh sheet disposed within the body of foamed cured cross-linked polymer.
4 . The roofing element of claim 1 , further comprising a backing sheet disposed on the bottom surface of the body of foamed cured cross-linked polymer.
5 . The roofing element of claim 1 , wherein the body of foamed cured cross-linked polymer is in the form of a substantially closed-cell foam.
6 . The roofing element of claim 1 , comprising a support sheet that is a glass mat, and a polymer film disposed on a bottom surface of the body of foamed cured cross-linked polymer.
7 . The roofing element of claim 1 , wherein the body of foamed cured cross-linked polymer has a density in the range of 1 g/mL to 2 g/mL.
8 . The roofing element of claim 1 , wherein the body of foamed cured cross-linked polymer has a void volume, and wherein no more than 10% of the void volume is formed by foam cells having a longest dimension in excess of 100 microns.
9 . The roofing element of claim 1 , wherein the polymer of the body of foamed cured cross-linked polymer is a poly(meth)acrylate-based polymer, a polyurethane/acrylate hybrid polymer, a polyurethane, a polyvinylidine difluoride or a copolymer thereof.
10 . The roofing element of claim 1 , wherein the polymer of the body of foamed cured cross-linked polymer is a poly(meth)acrylate-based polymer or a polyurethane/acrylate hybrid polymer.
11 . The roofing element of claim 1 , wherein the body of foamed cured cross-linked polymer further comprises a filler.
12 . The roofing element of claim 1 , having a headlap portion and an exposure portion, wherein the headlap portion is adapted to have its top surface generally covered in the installed condition of the element on a roof, and the exposure portion being adapted to have its top surface generally uncovered and weather-exposed in the installed condition of the element on a roof.
13 . The roofing element of claim 1 , wherein the body of foamed polymer has a thickness of at least 0.5 mm.
14 . The roofing element of claim 1 , wherein the body of foamed polymer has a thickness of at least 2 mm.
15 . The roofing element of claim 1 , wherein the body of foamed polymer has a thickness in the range of 0.5 mm to 35 mm.
16 . An array of the roofing elements according to claim 1 , disposed on a roof deck.
17 . A process for preparing a roofing element according to claim 1 , comprising:
providing a wet body of a foamed curable composition, the foamed curable composition being adapted to provide the foamed cured cross-linked polymer upon curing, the foamed curable composition having a wet foam density of about 0.1 to about 1.0 g/mL to provide a wet roofing element precursor;
disposing the granules on a top surface of the wet body of foamed curable composition; and then
allowing the wet body of foamed curable composition to cure to provide the body of foamed cured cross-linked polymer having the granules adhered to the top surface thereof.
18 . A roofing element in the form of a roofing shingle, shake or tile extending substantially in a plane, the roofing element having a top surface, the roofing element comprising:
a body of a foamed cured cross-linked polymer, the body having a top surface at the top surface of the roofing element and a bottom surface, the body extending substantially in the plane, and
a layer of weather-resistant roofing granules disposed on and adhered at the top surface of the roofing element,
wherein the weather-resistant roofing granules are disposed directly on and partially embedded in a top surface of the body of the foamed cured cross-linked polymer,
wherein the roofing element has an asphalt content of less than about 5 wt %, and
wherein the roofing element passes the ASTM E-84 flame spray test,
wherein the body of foamed cured cross-linked polymer has a void volume, and wherein no more than 10% of the void volume is formed by foam cells having a longest dimension in excess of 100 microns.
19 . The roofing element of claim 18 , further comprising a support sheet disposed within the body of foamed cured cross-linked polymer.
20 . The roofing element of claim 19 , wherein the support sheet comprises roofing felt.