Emmission control catalyst article with enriched PGM zone
The present disclosure generally relates to emission control catalyst articles comprising a platinum group metal (PGM) enriched zone, methods of making such emission control catalyst articles, and methods of using such emission control catalyst articles.
1. An emission control catalyst article comprising:
a substrate having an inlet axial end and an outlet axial end,
a bottom washcoat layer coated on about 60% to about 100% of the axial length of the substrate from the inlet axial end to the outlet axial end, and
a top washcoat layer coated on about 60% to about 100% of the axial length of the substrate from either the inlet or the outlet end of the substrate such that the top washcoat layer covers at least about 60% of the length of the bottom washcoat layer,
wherein the top washcoat layer and/or the bottom washcoat layer comprises a first portion comprising one or more platinum group metals and a second portion comprising one or more platinum group metals,
wherein the first portion begins at the inlet axial end of the substrate,
wherein the platinum group metal concentration in the first portion is about 2 to about 100 times higher than the platinum group metal concentration in the second portion,
wherein the first portion has a length of about 0.25 inches to about 2 inches, and
wherein the platinum group metal loading in the first portion is about 10 g/ft 3 to about 1000 g/ft 3 , as determined axially from a first end of the first portion to a second end of the first portion.
2. The emission control catalyst article according to claim 1 , wherein the first portion is a PGM enriched zone formed by coating a portion of the top washcoat layer and/or the bottom washcoat layer, which layer is already pre-loaded with platinum group metal, with an additional platinum group metal solution.
3. The emission control catalyst article according to claim 1 , wherein the one or more platinum group metals is chosen from a group consisting of platinum, palladium, rhodium, and combinations thereof.
4. The emission control catalyst article according claim 1 , wherein the platinum group metal is supported on a support chosen from a group consisting of an oxygen storage component, an alumina component, a ceria component, a zirconia component, and combinations thereof.
5. The emission control catalyst article according to claim 4 , wherein:
the alumina component comprises one or more components chosen from a group consisting of alumina, lanthana-alumina, ceria-alumina, ceria-zirconia-alumina, zirconia-alumina, lanthana-zirconia-alumina, baria-alumina, baria-lanthana-alumina, baria-lanthana-neodymia-alumina, and combinations thereof;
the oxygen storage component comprises one or more components chosen from a group consisting of ceria-zirconia, ceria-zirconia-lanthana, ceria-zirconia-yttria, ceria-zirconia-lanthana-yttria, ceria-zirconia-neodymia, ceria-zirconia-praseodymia, ceria-zirconia-lanthana-neodymia, ceria-zirconia-lanthana-praseodymia, ceria-zirconia-lanthana-neodymia-praseodymia, and combinations thereof; and
the zirconia component comprises one or more components chosen from a group consisting of lanthana-zirconia, barium-zirconia, and combinations thereof.
6. The emission control catalyst article according to claim 1 , wherein the first portion has a length ranging from about 0.5 inches to about 1 inch.
7. The emission control catalyst article according to claim 1 , wherein 50% or more of the platinum group metal in the first portion exists in an uppermost third (%) of the first portion, as determined by an electron-probe microanalysis (EPMA) line scan from an uppermost surface of the first portion to the substrate.
8. The emission control catalyst article according to claim 1 , wherein the one or more platinum group metals in the first portion is chosen from a group consisting of palladium, platinum, rhodium, and combinations thereof.
9. The emission control catalyst article according to claim 1 , wherein:
the bottom washcoat layer comprises a first portion comprising palladium or platinum optionally supported on a support chosen from a group consisting of an oxygen storage component, an alumina component, and combinations thereof and a second portion comprising palladium or platinum, wherein the concentration of palladium or platinum in the first portion is about 2 to about 100 times higher than the concentration of palladium or platinum in the second portion; and
the top washcoat layer comprises one or more platinum group metals chosen from a group consisting of rhodium, platinum, and combinations thereof impregnated on a support chosen from a group consisting of an oxygen storage component, an alumina component, and combinations thereof.
10. The emission control catalyst article according to claim 9 , wherein the first portion comprises palladium, wherein the amount of palladium in the first portion is about 30 wt. % to about 100 wt. % of the total palladium present in the catalyst article.
11. The emission control catalyst article according to claim 9 , wherein the first portion comprises platinum, wherein the amount of platinum in the first portion is about 30 wt. % to about 100 wt. % of the total platinum present in the catalyst article.
12. The emission control catalyst article according to claim 9 , wherein the first portion comprises a palladium or platinum concentration gradient, wherein the palladium or platinum concentration exponentially decreases from the top surface of the washcoat layer comprising the first portion to the bottom surface of the washcoat layer comprising the first portion.
13. The emission control catalyst article according to claim 1 , wherein the weight ratio of the platinum group metal of the first portion to the platinum group metal of the second portion ranges from about 4.0 to about 50.
14. The emission control catalyst article according to claim 1 , wherein:
the bottom washcoat layer comprises palladium impregnated on a support chosen from a group consisting of an oxygen storage component, an alumina component, and combinations thereof,
the top washcoat layer is coated on about 60% to about 100% of the axial length of the substrate from the inlet axial end,
the top washcoat layer comprises a first portion comprising palladium or platinum optionally supported on a support chosen from a group consisting of an oxygen storage component, an alumina component, and combinations thereof and a second portion comprising palladium or platinum, wherein the concentration of palladium or platinum in the first portion is about 2 to about 100 times higher than the concentration of palladium or platinum in the second portion.
15. The emission control catalyst article according to claim 1 , wherein the bottom washcoat layer comprises one or more alkaline-earth metal oxides chosen from a group consisting of barium oxide, strontium oxide, and combinations thereof, in an amount of about 1.0 wt. % to about 20 wt. %, based on the total weight of the bottom washcoat layer.
16. The emission control catalyst article according to claim 1 , wherein the substrate is a ceramic substrate, a metal substrate, a ceramic foam substrate, a polymer foam substrate, or a woven fibre substrate.
17. An exhaust system for internal combustion engines, said system comprising the emission control catalyst article according to claim 1 .
18. A method of treating a gaseous exhaust stream comprising hydrocarbons, carbon monoxide, and nitrogen oxides, the method comprising contacting the exhaust stream with the emission control catalyst article according to claim 1 .
19. A method of reducing hydrocarbon, carbon monoxide, and nitrogen oxide levels in a gaseous exhaust stream, the method comprising contacting the gaseous exhaust stream with the emission control catalyst article according to claim 1 to reduce the levels of hydrocarbons, carbon monoxide, and nitrogen oxides in the exhaust gas.