ION CONDUCTIVE CERAMIC AND METHOD FOR PREPARING SAME
The present invention relates to a ceramic solid electrolyte, which is a key component of an all-solid-state lithium secondary battery, for improving safety, and a method for synthesizing the same. The present invention relates to an oxide-based conductive ceramic of a new NASICON structure of the chemical formula Li 1+x Al x X 2−x P 3 O 12 (X is Zr, Si, Sn, or Y, 0<x<2) or Li 1+x Zr 2 X x P 3−x O 12 (X=Si, Sn, Ge, or Y, 1.5≤x≤2.3). The present invention relates to a method for manufacturing an oxide-based conductive ceramic having the above novel NASICON structure.
1 . An oxide-based conductive ceramic having a NASICON structure of the following chemical formula 1,
Li 1+x Al x X 2−x P 3 O 12 [Chemical Formula 1]
(X is Zr, Si, Sn, or Y, and 0<x<2)
2 . An oxide-based conductive ceramic having a NASICON structure of the following chemical formula 2,
Li 1+x Zr 2 X x P 3−x O 12 [Chemical Formula 2]
(X=Si, Sn, Ge, or Y, and 1.5≤x≤2.3)
3 . A process for synthesizing an oxide-based conductive ceramic having a NASICON structure of the following chemical formula 1 or 2, wherein the raw materials of the ceramic solid electrolyte are mixed, ball milled, and subjected to first heat treatment at 300° C. to 500° C., and secondary heat treatment at 800° C. to 1,200° C.
Li 1+x Al x X 2−x P 3 O 12 [Chemical Formula 1]
(X is Zr, Si, Sn, or Y, and 0<x<2)
Li 1+x Zr 2 X x P 3−x O 12 [Chemical Formula 2]
(X=Si, Sn, Ge, or Y, and 1.5≤x≤2.3)
4 . A process for synthesizing an oxide-based conductive ceramic having a NASICON structure of the following chemical formula 1 or 2, wherein the raw materials of the ceramic solid electrolyte are put in water, mixed by ball milling, the ball milled mixture is dried in a dryer, first heat treatment is performed at 300° C. to 500° C., and secondary heat treatment is performed at 800° C. to 1200° C.
Li 1+x Al x X 2−x P 3 O 12 [Chemical Formula 1]
(X is Zr, Si, Sn, or Y, and 0<x<2)
Li 1+x Zr 2 X x P 3−x O 12 [Chemical Formula 2]
(X=Si, Sn, Ge, or Y, and 1.5≤x≤2.3)
5 . A process for synthesizing an oxide-based conductive ceramic having a NASICON structure of the following chemical formula 1 or 2, wherein the raw materials of the ceramic solid electrolyte are put in water, mixed by ball milling, the ball milled mixture is dried first by rotary concentration or spraying, dried second in a dryer, first heat treatment is performed at 300° C. to 500° C., and secondary heat treatment is performed at 800° C. to 1200° C.
Li 1+x Al x X 2−x P 3 O 12 [Chemical Formula 1]
(X is Zr, Si, Sn, or Y, and 0<x<2)
Li 1+x Zr 2 X x P 3−x O 12 [Chemical Formula 2]
(X=Si, Sn, Ge, or Y, and 1.5≤x≤2.3)