Superconducting wire, method for manufacturing superconducting wire, and MRI device

1 . A superconducting wire, comprising:

a filament formed of MgB 2 ;

a base material covering a periphery of the filament;

a high-thermal expansion metal covering a periphery of the base material, the high-thermal expansion metal being stainless steel; and

a stabilizing material covering a periphery of the high-thermal expansion metal and stabilizing superconductivity, the stabilizing material being copper,

wherein the high-thermal expansion metal has a higher thermal expansion coefficient at room temperature than the MgB 2 and the base material.

2 . The superconducting wire according to claim 1 , further comprising:

a multi-filament wire structure including a plurality of the filaments each having a periphery covered with the base material.

3 . The superconducting wire according to claim 2 , further comprising:

a pipe material formed of iron or niobium to bundle the multi-filament base materials between the base materials and the high-thermal expansion metal.

4 . The superconducting wire according to claim 1 ,

wherein the stabilizing material or both the high-thermal expansion metal and the stabilizing material is/are removed from at least one end portion of the superconducting wire, and

wherein the filament on the end portion is integrated with a sintered body formed of MgB 2 , and the superconducting wire is superconductively joined to another superconductor via the sintered body.

5 . The superconducting wire according to claim 4 ,

wherein a stabilizing member stabilizing superconductivity is added to the end portion from which the stabilizing material is removed so as to be in contact with the superconducting wire.

6 . The superconducting wire according to claim 1 ,

wherein the base material is iron or niobium.

7 . The superconducting wire according to claim 1 ,

wherein the high-thermal expansion metal has a thermal expansion coefficient of 14.0×10−6° C.−1 or more from temperature of heat treatment to generate MgB 2 to room temperature.

8 . The superconducting wire according to claim 1 , further comprising:

a stabilizing member stabilizing superconductivity on an outer side of the stabilizing material, the stabilizing member covering part of the periphery of the stabilizing material and provided in a gantry shape in a cross-sectional view.

9 . A method for manufacturing a superconducting wire, the method comprising the steps of:

packing a mixed powder being a mixture of magnesium powder and boron powder into a first metal pipe;

performing wire-drawing on the first metal pipe filled with the mixed powder;

producing a composite wire by accommodating the first metal pipe subjected to the wire-drawing in a second metal pipe;

performing wire-drawing on the composite wire; and

generating MgB 2 by performing heat treatment on the composite wire subjected to the wire-drawing,

wherein the first metal pipe is formed of a metal to be a base material of the superconducting wire,

the second metal pipe is a composite pipe including a high-thermal expansion metal layer formed of a high-thermal expansion metal being stainless steel and a stabilizing material layer formed of a stabilizing material being copper covering a periphery of the high-thermal expansion metal layer and stabilizing superconductivity, or a multiple pipe including a high-thermal expansion metal pipe formed of the high-thermal expansion metal accommodated in a stabilizing material pipe formed of the stabilizing material stabilizing superconductivity, and

the high-thermal expansion metal has a higher thermal expansion coefficient at room temperature than the MgB 2 and the metal to be the base material.

10 . The method according to claim 9 ,

wherein the metal to be the base material is iron or niobium.

11 . The method according to claim 9 ,

wherein temperature of the heat treatment is 580 to 620° C.

12 . The method according to claim 9 ,

wherein the composite wire is produced by accommodating a plurality of the first metal pipes subjected to the wire-drawing in the second metal pipe.

13 . The method according to claim 9 ,

wherein the second metal pipe includes an inner layer formed of iron or niobium on an inner side of the composite pipe or the multiple pipe, or includes an inner pipe formed of iron or niobium accommodated in the composite pipe or the multiple pipe.

14 . An MRI device, comprising the superconducting wire according to claim 1 .