Graphene-based lubricant additives and lubricants
A graphene-based lubricant is provided that includes a graphene-based additive. The graphene-based additive, along with and other optional additives is dispersed in a base liquid. A method of lubrication is also provided that includes the application of the composition to two mating surfaces to form a protective coating between the two mating surfaces.
1. A graphene-based lubricant comprising:
a graphene-based additive having a surface area in the range of 300-800 m 2 /g;
a base liquid in which the graphene-based additive is dispersed; and
other additives dispersed in the base liquid,
wherein the graphene-based additive includes one or more surfactants comprising sulfonates, sulfates, polysaccharides, maleic anhydride grafted polyolefins, polyethylene glycols, or styrene acrylics bonded to the surface of the graphene.
2. The graphene-based lubricant of claim 1 , wherein the graphene-based additive comprises one or more of single-layer graphene, double-layer graphene, few-layer graphene (FLG), graphene nanoplatelets (GNP), graphene oxide (GO), reduced graphene oxide (rGO), functionalized graphene, and doped graphene.
3. The graphene-based lubricant of claim 1 , wherein the graphene-based additive is made by mechanical exfoliation of graphite.
4. The graphene-based lubricant of claim 1 , wherein the graphene-based additive has an average particle size of <5 microns.
5. The graphene-based lubricant of claim 1 , wherein the graphene-based additive has an oxygen content in the range of 2-20 wt %.
6. The graphene-based lubricant of claim 1 , wherein the graphene-based additive is made by chemical exfoliation of graphite.
7. The graphene-based lubricant of claim 1 , wherein the graphene-based additive has a particle size in the range of 0.1-50 microns.
8. The graphene-based lubricant of claim 1 , wherein the base liquid is an oil-based solvent or mixture or an aqueous based solvent.
9. The graphene-based lubricant of claim 1 , wherein the graphene-based additive content is in the range of 0.1-2 wt %.
10. The graphene-based lubricant of claim 8 , wherein the oil-based solvent or mixture has a viscosity index range of 80 to 120 and an operating temperature range of from 32° F. to 150° F.
11. The graphene-based lubricant of claim 8 , wherein the oil-based solvent comprises one or more of synthetic polyalphaolefins (PAOs).
12. The graphene-based lubricant of claim 1 , further comprising a dispersant, wherein the dispersant is selected from the group consisting of sulfonates, sulfates, phosphonates, phosphates, fatty acids, naphthenic acids, fatty amides, organic alcohols, succinimides, succinate esters, polysaccharides, maleic anhydride, maleic anhydride grafted polyolefins, polyols, polyethylene glycols (PEG), PEG based copolymers, polyacrylic acids (PAA), polyvinyl chloride (PVC), phenoxy ethers, styrene acrylics, and a mixture of any of the above,
wherein the amount of dispersant in the final lubricant formulation is in the range of 1 to 20 wt %.
13. The graphene-based lubricant of claim 8 , wherein the oil-based solvent comprises one or more of silicone, phosphate ester, polyalkylene glycol (PAG), polyolester, and biolubes with or without a dispersant.
14. The graphene-based lubricant of claim 13 , further comprising a dispersant, wherein the dispersant is selected from the group consisting of sulfonates, sulfates, phosphonates, phosphates, fatty acids, naphthenic acids, fatty amides, organic alcohols, succinimides, succinate esters, polysaccharides, maleic anhydride, maleic anhydride grafted polyolefins, polyols, polyethylene glycols (PEG), PEG based copolymers, polyacrylic acids (PAA), polyvinyl chloride (PVC), phenoxy ethers, styrene acrylics, and a mixture of any of the above,
wherein the amount of dispersant in the final lubricant formulation is in the range of 1 to 20 wt %.
15. The graphene-based lubricant of claim 1 , wherein the base liquid is an aqueous solvent.
16. A method of lubrication comprising:
applying a composition according to claim 1 to two mating surfaces to form a protective coating between the two mating surfaces.