Filter for glass container
A light filtering glass container including a glass container coated with a light filtering coating obtained by curing a polymerizable composition including semi-conductive nanoparticles. The absorbance through a 5-micrometer thick light filtering coating is greater than 0.5 for each light wavelength ranging from 350 nm to λ cut , λ cut being in the range from 420 nm to 480 nm, and the difference of lightness between the uncoated glass container and the glass container with the light filtering coating is lower than 5.
1 . A light filtering glass container comprising:
(i) a glass container having a colour (L*ug, C*ug, h*ug);
(ii) a light filtering coating obtained by curing a polymerizable composition comprising semi-conductive nanoparticles, said light filtering coating being on at least a part of the glass container;
wherein the glass container with the light filtering coating has a colour (L*cg, C*cg, h*cg);
wherein the absorbance through a 5-micrometer thick light filtering coating is greater than 0.5 for each light wavelength ranging from 350 nm to λ cut , λ cut being in the range from 420 nm to 480 nm; and
wherein the difference of lightness between the uncoated glass container and the glass container with the light filtering coating is lower than 5.
2 . The light filtering glass container according to claim 1 , wherein the luminous transmission of the glass container with the light filtering coating is greater than 90% of the luminous transmission of the uncoated glass container.
3 . The light filtering glass container according to claim 2 , wherein the luminous transmission of the glass container with the light filtering coating is greater than 95% of the luminous transmission of the uncoated glass container.
4 . The light filtering glass container according to claim 1 , having a chroma C*cg lower than 60.
5 . The light filtering glass container according to claim 1 , having a chroma C*cg lower than 50.
6 . The light filtering glass container according to claim 1 , wherein the polymerizable composition is a Sol-Gel polymerizable composition.
7 . The light filtering glass container according to claim 6 , wherein Sol-Gel polymerizable composition comprises monomers or oligomers selected from metal alkoxides, alkoxysilanes, alkylalkoxysilanes, epoxysilanes, epoxyalkoxysilanes, and mixtures thereof.
8 . The light filtering glass container according to claim 6 , wherein the thickness of light filtering coating is in a range from 1 μm to 15 μm.
9 . The light filtering glass container according to claim 6 , wherein the thickness of light filtering coating is in a range from 1 μm to 10 μm.
10 . The light filtering glass container according to claim 1 , wherein polymerizable composition comprises (meth) acrylics monomers or oligomers, epoxy monomers or oligomers, or mixture thereof.
11 . The light filtering glass container according to claim 10 , wherein the thickness of the light filtering coating is in a range from 2 μm to 100 μm.
12 . The light filtering glass container according to claim 10 , wherein the thickness of the light filtering coating is in a range from 3 μm to 50 μm.
13 . The light filtering glass container according to claim 1 , wherein the semi-conductive nanoparticles comprise a material of formula M x Q y E z A w (I), wherein:
M is selected from the group consisting of Zn, Cd, Hg, Cu, Ag, Au, Ni, Pd, Pt, Co, Fe, Ru, Os, Mn, Tc, Re, Cr, Mo, W, V, Nd, Ta, Ti, Zr, Hf, Be, Mg, Ca, Sr, Ba, Al, Ga, In, Tl, Si, Ge, Sn, Pb, As, Sb, Bi, Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Cs or a mixture thereof;
Q is selected from the group consisting of Zn, Cd, Hg, Cu, Ag, Au, Ni, Pd, Pt, Co, Fe, Ru, Os, Mn, Tc, Re, Cr, Mo, W, V, Nd, Ta, Ti, Zr, Hf, Be, Mg, Ca, Sr, Ba, Al, Ga, In, TI, Si, Ge, Sn, Pb, As, Sb, Bi, Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Cs or a mixture thereof;
E is selected from the group consisting of O, S, Se, Te, C, N, P, As, Sb, F, Cl, Br, I, or a mixture thereof;
A is selected from the group consisting of O, S, Se, Te, C, N, P, As, Sb, F, Cl, Br, I, or a mixture thereof; and
x, y, z and w are independently a decimal number from 0 to 5; x, y, z and w are not simultaneously equal to 0; x and y are not simultaneously equal to 0; z and w may not be simultaneously equal to 0.
14 . A light filter for a glass container obtained by curing a polymerizable composition comprising semi-conductive nanoparticles
wherein the absorbance through a 5-micrometer thick light filter is higher than 0.5 for each light wavelength ranging from 350 nm to λ cut , λ cut being in the range from 420 nm to 480 nm; and
wherein the lightness of the light filter is greater than 95.
15 . The light filter according to claim 14 , having a chroma C* lower than 60.
16 . The light filter according to claim 14 , having a chroma C* lower than 50.
17 . The light filter according to claim 14 , wherein the polymerizable composition is a Sol-Gel polymerizable composition.
18 . The light filter according to claim 17 , wherein the Sol-Gel polymerizable composition comprises monomers or oligomers selected from metal alkoxides, alkoxysilanes, alkylalkoxysilanes, epoxysilanes, epoxyalkoxysilanes, and mixtures thereof.
19 . The light filter according to claim 14 , wherein the polymerizable composition comprises (meth) acrylics monomers or oligomers, epoxy monomers or oligomers, or mixture thereof.