Long-term fire retardant with corrosion inhibitors and methods for making and using same
A forest fire retardant composition contains a retardant compound that includes a phosphate salt. The phosphate salt may include diammonium phosphate, diammonium orthophosphate, monoammonium phosphate, monoammonium orthophosphate, monosodium phosphate, disodium phosphate, disodium phosphate hydrate, sodium ammonium phosphate, sodium ammonium phosphate hydrate, sodium tripolyphosphate, trisodium phosphate, or dipotassium phosphate, and combinations thereof. The forest fire retardant composition may include an ammonium source. The composition may be in the form of a dry concentrate, a liquid concentrate, or a final diluted product. The final diluted product is effective in suppressing, retarding, and controlling forest fires while exhibiting corrosion resistance and low toxicity.
1. A forest fire retardant concentrate, comprising:
a retardant compound comprising:
diammonium phosphate; and
at least one of disodium phosphate, monosodium phosphate, or dipotassium phosphate;
a corrosion inhibitor for at least one of iron, brass, aluminum, or magnesium present in the concentrate in an amount having a weight percent of about 0.1% to about 3.0% relative to the total weight of the concentrate; and
a thickening agent, present in the concentrate in an amount having a weight percent of about 0.75% to about 5.0% relative to the total weight of the concentrate;
wherein:
the concentrate has a molar ratio of ammoniacal nitrogen to phosphorus (N/P molar ratio) of less than about 1.1; and
the corrosion inhibitor comprises an alkyl amine, one or more azoles, and disodium molybdate dihydrate.
2. The concentrate of claim 1 , wherein the thickening agent comprises at least one of a polyurethane, a polyvinyl alcohol, an acrylic polymer, a gum, a cellulosic, a sulfonate, a saccharide, a clay, an organosilicone, or a protein.
3. The concentrate of claim 1 , further comprising a colorant, present in the concentrate in an amount having a weight percent of about 0.04% to about 6.0% relative to the total weight of the concentrate, wherein the colorant comprises at least one of an inorganic pigment and an organic pigment.
4. The concentrate of claim 1 , further comprising monoammonium phosphate.
5. The concentrate of claim 1 , further comprising a buffering agent present in the concentrate in an amount having a weight percent of about 3% to about 56% relative to the total weight of the concentrate.
6. The concentrate of claim 1 , wherein the concentrate is a dry concentrate having no more than about 3% by weight of water relative to the total weight of the dry concentrate.
7. The concentrate of claim 6 , wherein the retardant compound is present in the dry concentrate in an amount having a weight percent of about 62% to about 99% relative to the total weight of the dry concentrate.
8. The concentrate of claim 1 , further comprising water;
wherein:
the concentrate is a final diluted product intended for use to suppress, retard, or contain forest fires;
the retardant compound is present in the final diluted product in an amount having a weight percent of about 6% to about 28% relative to the total weight of the final diluted product; and
the pH of the final diluted product is about 6.1 to about 7.9.
9. A forest fire retardant concentrate, comprising:
a retardant compound comprising:
diammonium phosphate; and
at least one of disodium phosphate, monosodium phosphate, or dipotassium phosphate;
a corrosion inhibitor for at least one of iron, brass, aluminum, or magnesium present in the concentrate in an amount having a weight percent of about 0.1% to about 3.0% relative to the total weight of the concentrate;
a thickening agent, present in the concentrate in an amount having a weight percent of about 0.75% to about 5.0% relative to the total weight of the concentrate; and
a surfactant present in the concentrate in an amount having a weight percent of about 0.04% to about 2.5% relative to the total weight of the concentrate;
wherein:
the concentrate has a molar ratio of ammoniacal nitrogen to phosphorus (N/P molar ratio) of less than about 1.1; and
the surfactant comprises a 10% active silicone emulsion.
10. The concentrate of claim 9 , wherein the thickening agent comprises at least one of a polyurethane, a polyvinyl alcohol, an acrylic polymer, a gum, a cellulosic, a sulfonate, a saccharide, a clay, an organosilicone, or a protein.
11. The concentrate of claim 9 , further comprising a colorant, present in the concentrate in an amount having a weight percent of about 0.04% to about 6.0% relative to the total weight of the concentrate, wherein the colorant comprises at least one of an inorganic pigment and an organic pigment.
12. The concentrate of claim 9 , further comprising monoammonium phosphate.
13. The concentrate of claim 9 , further comprising a buffering agent present in the concentrate in an amount having a weight percent of about 3% to about 56% relative to the total weight of the concentrate.
14. The concentrate of claim 9 , wherein the concentrate is a dry concentrate having no more than about 3% by weight of water relative to the total weight of the dry concentrate.
15. The concentrate of claim 14 , wherein the retardant compound is present in the dry concentrate in an amount having a weight percent of about 62% to about 99% relative to the total weight of the dry concentrate.
16. The concentrate of claim 9 , further comprising water;
wherein:
the concentrate is a final diluted product intended for use to suppress, retard, or contain forest fires;
the retardant compound is present in the final diluted product in an amount having a weight percent of about 6% to about 28% relative to the total weight of the final diluted product; and
the pH of the final diluted product is about 6.1 to about 7.9.
17. A forest fire retardant concentrate, comprising:
a retardant compound comprising:
monoammonium phosphate;
disodium phosphate; and
an ammonium source;
a corrosion inhibitor for at least one of iron, brass, aluminum, or magnesium present in the concentrate in an amount having a weight percent of about 0.1% to about 3.0% relative to the total weight of the concentrate; and
a thickening agent, present in the concentrate in an amount having a weight percent of about 0.75% to about 5.0% relative to the total weight of the concentrate;
wherein:
the concentrate has a molar ratio of ammoniacal nitrogen to phosphorus (N/P molar ratio) of less than about 1.1; and
the corrosion inhibitor comprises an alkyl amine, one or more azoles, and disodium molybdate dihydrate.
18. The concentrate of claim 17 , wherein the ammonium source comprises at least one of diammonium phosphate, sodium ammonium phosphate, sodium ammonium phosphate hydrate, ammonium chloride, ammonium acetate, ammonium citrate, ammonium sulfate, or diammonium phosphate.
19. The concentrate of claim 18 , wherein the N/P ratio is about 0.5 to about 0.9.
20. The concentrate of claim 17 , wherein the thickening agent comprises at least one of a polyurethane, a polyvinyl alcohol, an acrylic polymer, a gum, a cellulosic, a sulfonate, a saccharide, a clay, an organosilicone, or a protein.
21. The concentrate of claim 17 , further comprising a colorant, present in the concentrate in an amount having a weight percent of about 0.04% to about 6.0% relative to the total weight of the concentrate, wherein the colorant comprises at least one of an inorganic pigment and an organic pigment.
22. The concentrate of claim 17 , further comprising a buffering agent present in the concentrate in an amount having a weight percent of about 3% to about 56% relative to the total weight of the concentrate.
23. The concentrate of claim 17 , wherein the concentrate is a dry concentrate having no more than about 3% by weight of water relative to the total weight of the dry concentrate.
24. The concentrate of claim 23 , wherein the retardant compound is present in the dry concentrate in an amount having a weight percent of about 62% to about 99% relative to the total weight of the dry concentrate.
25. The concentrate of claim 17 , further comprising water;
wherein:
the concentrate is a final diluted product intended for use to suppress, retard, or contain forest fires;
the retardant compound is present in the final diluted product in an amount having a weight percent of about 6% to about 28% relative to the total weight of the final diluted product; and
the pH of the final diluted product is about 5.2 to about 6.8.
26. A forest fire retardant concentrate, comprising:
a retardant compound comprising:
monoammonium phosphate;
disodium phosphate; and
an ammonium source;
a corrosion inhibitor for at least one of iron, brass, aluminum, or magnesium present in the concentrate in an amount having a weight percent of about 0.1% to about 3.0% relative to the total weight of the concentrate;
a thickening agent, present in the concentrate in an amount having a weight percent of about 0.75% to about 5.0% relative to the total weight of the concentrate; and
a surfactant present in the concentrate in an amount having a weight percent of about 0.04% to about 2.5% relative to the total weight of the concentrate;
wherein:
the concentrate has a molar ratio of ammoniacal nitrogen to phosphorus (N/P molar ratio) of less than about 1.1; and
the surfactant comprises a 10% active silicone emulsion.
27. The concentrate of claim 26 , wherein the ammonium source comprises at least one of diammonium phosphate, sodium ammonium phosphate, sodium ammonium phosphate hydrate, ammonium chloride, ammonium acetate, ammonium citrate, ammonium sulfate, or diammonium phosphate.
28. The concentrate of claim 27 , wherein the N/P ratio is about 0.5 to about 0.9.
29. The concentrate of claim 26 , wherein the thickening agent comprises at least one of a polyurethane, a polyvinyl alcohol, an acrylic polymer, a gum, a cellulosic, a sulfonate, a saccharide, a clay, an organosilicone, or a protein.
30. The concentrate of claim 26 , further comprising a colorant, present in the concentrate in an amount having a weight percent of about 0.04% to about 6.0% relative to the total weight of the concentrate, wherein the colorant comprises at least one of an inorganic pigment and an organic pigment.
31. The concentrate of claim 26 , further comprising a buffering agent present in the concentrate in an amount having a weight percent of about 3% to about 56% relative to the total weight of the concentrate.
32. The concentrate of claim 26 , wherein the concentrate is a dry concentrate having no more than about 3% by weight of water relative to the total weight of the dry concentrate.
33. The concentrate of claim 32 , wherein the retardant compound is present in the dry concentrate in an amount having a weight percent of about 62% to about 99% relative to the total weight of the dry concentrate.
34. The concentrate of claim 26 , further comprising water;
wherein:
the concentrate is a final diluted product intended for use to suppress, retard, or contain forest fires;
the retardant compound is present in the final diluted product in an amount having a weight percent of about 6% to about 28% relative to the total weight of the final diluted product; and
the pH of the final diluted product is about 5.2 to about 6.8.