Multi-layer film with improved modulus properties
The invention relates to a multi-layer, preferably co-extruded, plastic film with improved modulus properties, which is suitable, in particular, for producing three-dimensionally shaped articles.
1. A multi-layer plastic film, having
a layer A containing at least one polycarbonate or copolycarbonate and/or at least one polyester or copolyester, the layer A having a glass transition temperature T g from 80° C. to 200° C.,
and at least one layer B containing at least one thermoplastic polyurethane, polyester and/or copolyester, the at least one layer B exhibiting a hardness from 45 Shore D to 85 Shore D,
wherein the adhesive force between the layer A and the at least one layer B is greater than 0.5 N/mm, determined in accordance with ASTM D 903 98,
wherein the film has been co-extruded.
2. The multi-layer plastic film according to claim 1 , wherein the layer A containing at least one polyester or copolyester exhibits an inherent viscosity from 0.50 dL/g to 1.20 dL/g and a glass transition temperature T g from 80° C. to 200° C.
3. The multi-layer plastic film according to claim 1 , wherein the at least one layer B contains at least one thermoplastic polyurethane exhibiting a hardness from 45 Shore D to 85 Shore D.
4. The multi-layer plastic film according to claim 1 , wherein
the layer A contains at least one copolyester that exhibits residues from
(a) a dicarboxylic acid component comprising
i) 70 mole % to 100 mole % terephthalic acid residues,
ii) 0 mole % to 30 mole % aromatic dicarboxylic acid residues with up to 20 carbon atoms, and
iii) 0 mole % to 10 mole % aliphatic dicarboxylic acid residues with up to 16 carbon atoms, and
(b) a diol component comprising
i) 5 mole % to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues, and
ii) 50 mole % to 95 mole % 1,4-cyclohexanedimethanol residues,
wherein the sum of the mole % of residues i)-iii) of the dicarboxylic acid component amounts to 100 mole % and the sum of the mole % of residues i) and ii) of the diol component amounts to 100 mole %, and
wherein the inherent viscosity of the copolyester amounts to 0.50 dL/g to 1.20 dL/g and the copolyester exhibits a glass transition temperature T g from 80° C. to 150° C.,
and the layer A is located next to the at least one layer B containing at least one thermoplastic polyurethane, the thermoplastic polyurethane exhibiting a hardness from 45 Shore D to 85 Shore D and being obtainable from
a) one or more linear polyether diols with mean molecular weights from 500 g/mol to 10,000 g/mol, and, on average, in each instance at least 1.8 and at most 3.0 Tserevitinov-active hydrogen atoms
b) one or more organic diisocyanates,
c) one or more diol chain-extenders with molecular weights from 60 g/mol to 500 g/mol and with, on average, 1.8 to 3.0 Tserevitinov-active hydrogen atoms
in the presence of
d) optionally, one or more catalysts
with addition of
e) optionally, auxiliary substances and additives,
wherein the molar ratio of the NCO groups in b) to the groups in a) and c) that are reactive towards isocyanate amounts to 0.85:1 to 1.2:1.
5. The multi-layer plastic film according to claim 4 , wherein the one or more linear polyether diols have mean molecular weights from 500 g/mol to 6000 g/mol.
6. The multi-layer plastic film according to claim 4 , wherein the one or more linear polyether diols have, on average, in each instance 1.8 to 2.2, Tserevitinov-active hydrogen atoms.
7. The multi-layer plastic film according to claim 4 , wherein the molar ratio of the NCO groups in b) to groups in a) and c) that are reactive towards isocyanate amounts to 0.9:1 to 1.1.1.
8. The multi-layer plastic film according to claim 4 , wherein the one or more polyether diols are based on one or more units selected from the group consisting of 1,4-butanediol units and 1,3-propylene glycol units.
9. The multi-layer plastic film according to claim 4 , wherein the one or more organic diisocyanates are one or more selected from the group consisting of 4,4′-diphenylmethane-diisocyanate, isophorone diisocyanate, dicyclohexylmethane-4,4′-diisocyanate, and 1,6-hexamethylene diisocyanate.
10. The multi-layer plastic film according to claim 4 wherein the one or more diol chain-extenders are one or more selected from the group consisting of 1,4-butanediol, 1,3-propanediol, 1,2-propanediol, 1,2-ethylene glycol, 1,6-hexanediol, 1,4-di(β-hydroxyethyl)hydroquinone, and 1,4-di(β-hydroxyethyl)bisphenol A.
11. The multi-layer plastic film according to claim 4 , wherein the thermoplastic polyurethane was produced in a prepolymer process.
12. The multi-layer plastic film according to claim 4 , wherein the diol component of the at least one copolyester comprises 10 mole % to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues and 65 mole % to 90 mole % 1,4-cyclohexanedimethanol residues, the sum of the mole % of these two components of the diol component amounting to 100 mole %.
13. The multi-layer plastic film according to claim 12 , wherein the diol component of the at least one copolyester comprises 15 mole % to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues and 65 mole % to 85 mole % 1,4-cyclohexanedimethanol residues, the sum of the mole % of these two components of the diol component amounting to 100 mole %.
14. The multi-layer plastic film according to claim 12 , wherein the diol component of the at least one copolyester comprises 15 mole % to 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues and 70 mole % to 85 mole % 1,4-cyclohexanedimethanol residues, the sum of the mole % of these two components of the diol component amounting to 100 mole %.
15. The multi-layer plastic film according to claim 4 , wherein the dicarboxylic acid component comprises 95 mole % to 100 mole % terephthalic acid residues.
16. The multi-layer plastic film according to claim 2 , wherein the at least one polyester or copolyester exhibits an inherent viscosity from 0.50 dL/g to 0.80 dL/g.
17. The multi-layer plastic film according to claim 1 , wherein the at least one polyester or copolyester exhibits a glass transition temperature T g from 85° C. to 130° C.
18. The multi-layer plastic film according to claim 17 , wherein the at least one polyester or copolyester exhibits a glass transition temperature T g from 90° C. to 120° C.
19. The multi-layer plastic film according to claim 1 , wherein the at least one thermoplastic polyurethane exhibits a hardness from 50 Shore D to 80 Shore D.
20. The multi-layer plastic film according to claim 1 , wherein the film has a total thickness from 300 μm to 2000 μm.
21. The multi-layer plastic film according to claim 20 , wherein the film has a total thickness from 400 μm to 1500 μm.
22. The multi-layer plastic film according to claim 20 , wherein the film has a total thickness from 500 μm to 1200 μm.
23. The multi-layer plastic film according to claim 1 , wherein the layer A has a layer thickness from 250 μm to 1600 μm.
24. The multi-layer plastic film according to claim 23 , wherein the layer A has a layer thickness from 350 μm to 1400 μm.
25. The multi-layer plastic film according to claim 23 , wherein the layer A has a layer thickness from 400 μm to 1000 μm.
26. The multi-layer plastic film according to claim 1 , wherein the at least one layer B has a layer thickness from 25 μm to 500 μm.
27. The multi-layer plastic film according to claim 26 , wherein the at least one layer B has a layer thickness from 30 μm to 300 μm.
28. The multi-layer plastic film according to claim 26 , wherein the at least one layer B has a layer thickness from 50 μm to 200 μm.
29. A three-dimensionally shaped article obtained by three-dimensionally forming the multi-layer plastic film according to claim 19 .