GERM-REPELLENT ELASTOMER

1 . A biocide-free, germ-repellent, crosslinked thermoset elastomer comprising:

a thermoset elastomer base selected from natural rubber, synthetic rubber, solid or liquid silicone rubber, or mixtures thereof;

at least one germ-repelling modifier selected from one or more of polyethylene glycol, a polyethylene glycol derivative, alcohol ethoxylate, a polymer including an isocyanate group, a polymer including an allyloxy group, siloxane, polydimethylsiloxane, polyurethane, polyether modified silicone, polysorbates and copolymers or mixtures thereof;

the at least one germ-repelling modifier being permanently bonded to the thermoset elastomer base through a chemical reaction during extrusion, molding, or curing, wherein the chemical reaction also crosslinks the thermoset elastomer base.

2 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 1 , wherein the thermoset base elastomer is liquid silicone rubber.

3 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 1 , wherein the thermoset base elastomer is high consistency rubber (HCR).

4 . The polyurethane, polyether biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 1 , wherein the thermoset base elastomer is natural rubber.

5 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 1 , wherein the thermoset elastomer base is synthetic rubber.

6 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 1 , where the germ-repelling modifier is chemically bond to the thermoset elastomer base through reaction extrusion processing

7 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 1 , wherein the germ-repelling modifier is chemically bond to the thermoset elastomer base through copolymerization between polyethylene glycol or a polyethylene glycol derivative and the thermoset elastomer base.

8 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 1 , wherein the thermoset elastomer base is silicone rubber and the mass ratio of the silicone rubber substrate to the germ-repelling modifier is 100:(2-10).

9 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 8 , wherein the silicone rubber base includes component A and component B, and component A includes polydimethylsiloxane with vinyl groups and component B includes polydimethylsiloxane with functional groups.

10 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 9 , wherein the germ-repelling modifier includes a polyethoxylated non-ionic surfactant, wherein the polyethoxylated non-ionic surfactant is selected from a combination of polyethylene glycol or a polyethylene glycol derivative and silicone oil.

11 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 8 , wherein the mass ratio of the silicone rubber base to the germ-repelling modifier is 100:(2-3).

12 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 9 , wherein the mass ratio of component A to component B is (0.5-1.5):(0.5-1.5).

13 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 10 , wherein the mass ratio between polyethylene glycol or the polyethylene glycol derivative and silicone oil is (60-40):(40-60).

14 . The biocide-free, germ-repellent, crosslinked thermoset elastomer according to claim 1 , wherein the polyethylene glycol or the polyethylene glycol derivative comprises PEG 200, PEG 400, mPEG 600, and poly(ethylene glycol) sorbitol hexaoleate.