Methods of surface modification of metal casings and cement sheath bonding
A method of treating the surface of a metal casing used in a wellbore by conditioning the metal casing in a conditioning fluid to form a conditioned metal casing, contacting the conditioned metal casing with a treatment fluid to form a treated metal casing, and drying the treated metal casing. A method of increasing the bond strength between cement and a metal casing surface treated with a reactive organic compound by curing the treated metal casing with a cement slurry.
1. A method for treating the surface of a metal casing, the method comprising:
conditioning the metal casing in a conditioning fluid comprising an aqueous alkali metal hydroxide solution, wherein the conditioning results in the formation of hydroxyl groups on the surface of the metal casing, resulting in a conditioned metal casing;
contacting the conditioned metal casing with a treatment fluid comprising cyanuric chloride, resulting in a treated metal casing; and
drying the treated metal casing, wherein the surface of the treated metal casing comprises cyanuric chloride covalently bound to the surface hydroxyl groups of the metal casing.
2. The method of claim 1 , wherein the conditioning fluid comprises de-ionized water, tap water, or sea water.
3. The method of claim 1 , wherein the concentration of the alkali metal hydroxide in the conditioning fluid is about 0.1 M to about 5 M.
4. The method of claim 1 , wherein the alkali metal hydroxide is selected from the group consisting of lithium hydroxide (LiOH), sodium hydroxide (NaOH), potassium hydroxide (KOH), rubidium hydroxide (RbOH), and cesium hydroxide (CsOH).
5. The method of claim 1 , wherein the conditioning comprises soaking the metal casing in the conditioning fluid or continuously flowing the conditioning fluid through or out of the casing.
6. The method of claim 1 , wherein the conditioning comprises contacting the metal casing with the conditioning fluid for about 1 hour to about 12 hours.
7. The method of claim 1 , wherein the conditioning occurs at about 4° C. to about 25° C.
8. The method of claim 1 , wherein the treatment fluid comprises an organic solvent selected from the group consisting of tetrahydrofuran (THF), dioxane, and mixtures thereof.
9. The method of claim 1 , wherein the treatment fluid comprises about 0.5% w/v to about 5% w/v cyanuric chloride.
10. The method of claim 1 , wherein the contacting of the conditioned metal casing with the treatment fluid occurs at about 2° C. to about 10° C.
11. The method of claim 1 , wherein the contacting the metal casing with the treatment fluid occurs for about 1 hour to about 48 hours.
12. The method of claim 1 , wherein the conditioning and contacting occurs for a total time of about 1 hour to about 48 hours.
13. The method of claim 1 , wherein the drying occurs at about 20° C. to about 30° C.
14. The method of claim 1 , further comprising curing the treated metal casing with a cement slurry.
15. The method of claim 14 , wherein the cement is a Portland cement selected from the group consisting of Class A cement, Class B cement, Class C cement, Class G cement, Class H cement, and mixtures thereof.
16. The method of claim 14 , wherein the cement slurry comprises cement to water in a ratio of about 2:1.
17. The method of claim 14 , wherein the cement slurry further comprises a retarder, a dispersant, a fluid loss additive, silica flour, defoamer, and combinations thereof.
18. The method of claim 14 , wherein the treated metal casing and cement slurry are cured at about 80° C. to about 100° C.
19. The method of claim 14 , wherein the treated metal casing and cement slurry are cured at about 10 MPa to about 25 MPa.