Elastomer with tunable properties and method of rapidly forming the elastomer

Inventors: Nancy R. Sottos (Champaign, IL); Jeffrey S. Moore (Savoy, IL); Leon M. Dean (Minneapolis, MN); Qiong Wu (Champaign, IL); Omar Alshangiti (Urbana, IL)
Assignee: The Board of Trustees of the University of Illinois
A61L27/22C08G61/08C08G2261/3321C08G2261/3322
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,533,441
App. No.
17/910,132
Granted
Jan 27, 2026
Kind
B2
Abstract

A method of rapidly forming an elastomer with tunable properties is described herein. The method includes preparing a monomer solution comprising a catalyst and one or more monomers including 1,5-cyclooctadiene (COD). The one or more monomers may further include dicyclopentadiene (DCPD), and each of the COD and the DCPD may be present in the monomer solution at a predetermined volume percentage. A region of the monomer solution is activated to initiate an exothermic polymerization reaction and generate a self-propagating polymerization front, which moves through the monomer solution and polymerizes the one or more monomers. Thus, an elastomer having predetermined properties is rapidly formed.

Claims (40)

1 . A method of rapidly forming an elastomer, the method comprising:

preparing a monomer solution comprising a catalyst and one or more monomers including 1,5-cyclooctadiene (COD);

activating a region of the monomer solution to initiate an exothermic polymerization reaction and generate a self-propagating polymerization front,

wherein the self-propagating polymerization front moves through the monomer solution and polymerizes the one or more monomers, thereby rapidly forming an elastomer.

2 . The method of claim 1 , wherein the one or more monomers further comprises dicyclopentadiene (DCPD), and

wherein the COD and the DCPD have a predetermined volume ratio in the monomer solution.

3 . The method of claim 1 , wherein the elastomer comprises poly (1,4-butadiene) or a copolymer.

4 . The method of claim 1 , wherein the one or more monomers comprises at least 30 vol % COD.

5 . The method of claim 4 , wherein the one or more monomers comprises from 30 vol % COD to 40 vol % COD.

6 . The method of claim 1 , wherein the elastomer has a glass transition temperature below room temperature.

7 . The method of claim 1 , wherein the one or more monomers comprises less than 30 vol % COD.

8 . The method of claim 1 , wherein the elastomer has a glass transition temperature above room temperature.

9 . The method of claim 1 , wherein the monomer solution comprises more than one layer arranged in a vertical stack, each layer comprising the one or more monomers with a different volume percentage of the COD.

10 . The method of claim 1 , wherein the elastomer comprises more than one layer, each layer comprising a different glass transition temperature.

11 . The method of claim 10 , wherein the different glass transition temperature of each layer is above room temperature, and

wherein the elastomer comprises a shape memory polymer configured for sequential actuation.

12 . The method of claim 10 , wherein the different glass transition temperature of each layer is below room temperature, and

wherein the elastomer comprises an elastomeric polymer where each layer comprises different mechanical properties at room temperature.

13 . An elastomer having tunable properties, the elastomer comprising polybutadiene or a copolymer and being formed by:

preparing a monomer solution comprising one or more monomers including 1,5-cyclooctadiene (COD);

activating a region of the monomer solution to initiate an exothermic polymerization reaction and generate a self-propagating polymerization front,

wherein the self-propagating polymerization front moves through the monomer solution and polymerizes the one or more monomers, thereby rapidly forming the elastomer,

wherein the elastomer comprises a gradient in composition, a gradient in glass transition temperature, and/or a gradient in mechanical properties.

14 . The elastomer of claim 13 comprising poly (1,4-butadiene), or

comprising the copolymer, wherein the one or more monomers of the monomer solution further includes dicyclopentadiene (DCPD).

15 . The elastomer of claim 13 comprising a glass transition temperature below room temperature,

wherein the one or more monomers of the monomer solution comprises at least 30 vol % COD.

16 . The elastomer of claim 15 , comprising a tensile strength in a range from about 3 MPa to about 20 MPa and/or an elongation at failure in a range from about 300% to about 520% at room temperature.

17 . The elastomer of claim 13 comprising a glass transition temperature above room temperature,

wherein the one or more monomers of the monomer solution comprises less than 30 vol % COD.

18 . The elastomer of claim 17 , wherein the elastomer is a shape memory polymer.

19 . A method of rapidly forming an elastomer with tunable properties, the method comprising:

preparing a liquid monomer solution comprising a catalyst and monomers including 1,5-cyclooctadiene (COD) and dicyclopentadiene (DCPD), the monomers having a predetermined volume ratio in the liquid monomer solution;

activating a region of the liquid monomer solution to initiate an exothermic polymerization reaction and generate a self-propagating polymerization front,

wherein the self-propagating polymerization front moves through the monomer solution and polymerizes the one or more monomers, thereby rapidly forming an elastomer having predetermined properties.

20 . An elastomer having tunable properties, the elastomer comprising polybutadiene or a copolymer and being formed by:

preparing a monomer solution comprising one or more monomers including 1,5-cyclooctadiene (COD);

activating a region of the monomer solution to initiate an exothermic polymerization reaction and generate a self-propagating polymerization front,

wherein the self-propagating polymerization front moves through the monomer solution and polymerizes the one or more monomers, thereby rapidly forming the elastomer,

wherein the elastomer is a shape memory polymer.

Assignments (1)
CONFIRMATORY LICENSE Recorded Sep 12, 2024
From: UNIVERSITY OF ILLINOIS
To: U.S. DEPARTMENT OF ENERGY
Reel/Frame 068948/0100 →
Continuity (2)
Provisional Application 62991781 · Mar 19, 2020
Related Publication 20230096431A1 · Mar 30, 2023
References Cited (52)
US 3260708A · Natta et al. · 1966 [cited by applicant]
US 6057406A · Pojman et al. · 2000 [cited by applicant]
US 6489415B2 · Hsu · 2002 [cited by examiner]
US 6776932B1 · Ilyashenko · 2004 [cited by applicant]
US 7151146B1 · Kwag · 2006 [cited by examiner]
US 10487446B2 · Robertson et al. · 2019 [cited by applicant]
US 20100155998A1 · Rule et al. · 2010 [cited by applicant]
US 20120213969A1 · Mather et al. · 2012 [cited by applicant]
US 20140275595A1 · Wampler et al. · 2014 [cited by applicant]
US 20180230642A1 · Robertson et al. · 2018 [cited by applicant]
US 20180327531A1 · Moore et al. · 2018 [cited by applicant]
CN 101553287B · 2012 [cited by applicant]
GB 2005280A · 1979 [cited by examiner]
GB 2005280A1 · 1979 [cited by applicant]
KR 1020180044489A · 2018 [cited by examiner]
KR 10-2018-0044489 A (May 3, 2018); machine translation. (Year: 2018). [cited by examiner]
Second Chinese Office Action from related application CN 202180021814.1, Jul. 31, 2024, 27 pp. [cited by applicant]
Michel et al., “Tuning the properties of α,ω-bis(trialkoxysilyl) telechelic copolyolefins from ruthenium-catalyzed chain-transfer ring-opening metathesis polymerization (ROMP),” [cited by applicant]
Extended European Search Report from related application EP21771591.1, Mar. 20, 2024, 9 pp. [cited by applicant]
Chinese Office Action and English translation from corresponding application CN 202180021814.1, Oct. 24, 2023, pp. 1-31. [cited by applicant]
Allaert et al., “Secondary metathesis with Grubbs catalysts in the 1,4-polybutadiene system,” Catal. Commun. 9 (2008), pp. 1054-1059. [cited by applicant]
Alazari et al., “Effect of Limonene on the Frontal Ring Opening Metathesis Polymerization of Dicyclopentadiene,” J. Polym. Sci. Part A: Polym. Chem. 45 (2016), pp. 63-68. [cited by applicant]
Chekanov et al., “Fronatl Curing of Epoxy Resins: Comparison of Mechanical and Thermal Properties to Batch-Cured Materials,” J. Appl. Polym. Sci. 66 (1997)), pp. 1209-1216. [cited by applicant]
Chen et al., “Polyurethane-Nanosilica Hybrid Nanocomposites Synthesized by Frontal Polymerization,” Polym. Sci. Part A: Polym. Chem. 43 (2005), pp. 1670-1680. [cited by applicant]
Goli et al., “Frontal Polymerization of Dicyclopentadiene: A Numerical Study,” J. Phys. Chem. B, 122 (2018), pp. 4583-4591. [cited by applicant]
Hillmyer et al., “Utilityof a Ruthenium Metathesis Catalyst for the Preparation of End-Functionalized Polybutadiene,” Macromolecules, 30 (1997), pp. 718-721. [cited by applicant]
Holt et al., “Cure-on-demand Wood Adhesive Based on the Frontal Polymerization of Acrylates,” J. Appl. Polym. Sci. 133 (2016), pp. 1-5. [cited by applicant]
Ilker et al., “Alternating Copolymerizations of Polar and Nonpolar Cyclic Olefins by Ring-Opening Metathesis Polymerization,” Macromolecules, 35 (2002), pp. 54-58. [cited by applicant]
Khan et al., “Readily Accessible and Easily Modifiable Ru-Based Catalysts for Efficient and Z-Selective Ring-Opening Metathesis Polymerization and Ring-Opening/Cross-Metathesis,” J. Am. Chem. Soc. 135 (2013), pp. 10258-… [cited by applicant]
Khoury et al., “Ring Strain Energies: Substituted Rings, Norbornanes, Norbornenes and Norbornadienes,” Tetrahedron, 60 (2004), pp. 8103-8112. [cited by applicant]
Liu et al., “Review of progress in shape-memory polymers,” Mater. Chem. 17, (2007), pp. 1543-1558. [cited by applicant]
Makhiyanov, “Glass Transition Temperature and Microstructure of Polybutadienes,” Polym. Sci., Ser. A, 52, 12 (2010), pp. 1292-1300. [cited by applicant]
Mariani et al., “UV-Ignited Frontal Polymerization of an Epoxy Resin,” Polym. Sci. Part A: Polym. Chem. 42 (2004), pp. 2066-2072. [cited by applicant]
Martinez et al., “Ring-Opening Metathesis Polymerization of 8-Membered Cyclic Olefins,” Polym. Chem. 5, (2014), pp. 3507-3532. [cited by applicant]
Michel et al., “Tuning the Properties of α,ωvus(trialkoxysilyl) Telechelic Copolyolefins from Ruthenium-Catalyzed Chain-Transfer Ring-Opening Metathesis Polymerization (ROMP),” Polym. Chem. 8 (2017), pp. 1177-1187. [cited by applicant]
Morita et al., “A Ring-Opening Metathesis Polymerization (ROMP) Approach to Carboxyl- and Amino-Terminated Telechelic Poly(butadiene)s,” Macromolecules 33 (2000), pp. 6621-6623. [cited by applicant]
Nuvoli, et al., “Synthesis and Characterization of Functionally Gradient Materials Obtained by Frontal Polymerization,” ACS Appl. Mater. Interfaces, 7 (2015), pp. 3600-3606. [cited by applicant]
Pojman et al., “Traveling Fronts of Methacrylic Acid Polymerization,” J. Am. Chem. Soc. 113 (1991), pp. 6284-6286. [cited by applicant]
Robertson et al., “Rapid Stiffening of a Microfluidic Endoskeleton via Frontal Polymerization,” ACS Appl. Mater. Interfaces, 6 (2014), pp. 18469-18474. [cited by applicant]
Ruiu et al., “Advances in the Frontal Ring Opening Metathesis Polymerization of Dicyclopentadiene,” J. Polym. Sci. Part A: Polym. Chem. 52 (2014), pp. 2776-2780. [cited by applicant]
Vitale et al., “A Unified Approach for Patterning via Frontal Photopolymerization,” Adv. Mater. 27, (2015), pp. 6118-6124. [cited by applicant]
Washington et al., “Frontal Polymerization Synthesis of Temperature-Sensitive Hydrogels,” J. Am. Chem. Soc. 123 (2001), pp. 7933-7934. [cited by applicant]
Yan et al., “Frontal Polymerization Synthesis of Monolithic Macroporous Polymers,” Adv. Funct. Mater. 17 (2007), pp. 3355-3362. [cited by applicant]
International Search Report and Written Opinion from corresponding international application No. PCT/US21/21656, May 19, 2021, 11 pp. [cited by applicant]
Luo, Y. et al., “A General Approach Towards Thremoplastic Multishape-Memory Polymers via Sequence Structure Design”, Advanced Materials, 25, 5 (2013) pp. 743-748. [cited by applicant]
Dean, L. M. et al., “Rapid Synthesis of Elastomers and Thermosets with Tunable Thermomechanical Properties”, ACS Macro Letters, 9, 6 (2020) pp. 819-824. [cited by applicant]
Robertson, I. D. et al., “Frontal Ring-Opening Metathesis Polymerization of Exo-Dicyclopentadiene for Low Catalyst Loadings”, ACS Macro Letters, 5, 5 (2016) pp. 593-596. [cited by applicant]
Robertson, I. D. et al., “Rapid Energy-Efficient Manufacturing of Polymers and Composites via Frontal Polymerization”, Nature, 557 (2018) pp. 223-227. [cited by applicant]
Robertson, I. D. et al., “Alkyl Phosphate Inhibitors for Frontal Ring-Opening Metathesis Polymerization Greatly Increase Pot Life”, ACS Macro Letters, 6 (2017) pp. 609-612. [cited by applicant]
Mariani, A. et al., “Frontal Ring-Opening Metathesis Polymerization of Dicyclopentadiene”, Macromolecules, 34, 19 (2001) pp. 6539-6541. [cited by applicant]
Rejection Decision from Chinese Office Action from related application CN 202180021814.1 dated Dec. 21, 2024, 24 pp. [cited by applicant]
European Search Report from related application EP 21771591.1, dated Jun. 25, 2025, 5 pp. [cited by applicant]
Cited By (1)
US 12,655,250